Search Results

The efforts of the ISO “Test Variability Task Force” have been aimed at improving the understanding and at reducing brake dynamometer test variability during performance testing. In addition, dynamometer test results have been compared and correlated to vehicle testing. Even though there is already a vast amount of anecdotal evidence confirming the fact that different procedures generate different friction coefficients on the same brake corner, the availability of supporting data to the industry has been elusive up to this point. To overcome this issue, this paper focuses on assessing friction levels, friction coefficient sensitivity, and repeatability under ECE, GB, ISO, JASO, and SAE laboratory friction evaluation tests.

Development of reliable magnesium (Mg) to steel joining methods is one of the critical issues in broader applications of Mg in automotive body construction. Ultrasonic spot welding (USW) has been demonstrated successfully to join Mg to steel and to achieve strong joints. In this study, corrosion test of ultrasonic spot welds between 1.6 mm thick Mg AZ31B-H24 and 0.8 mm thick galvanized mild steel, without and with adhesive, was conducted. Adhesive used was a one-component, heat-cured epoxy material, and was applied between overlapped sheets before USW. Corrosion test was conducted with an automotive cyclic corrosion test, which includes cyclic exposures of dipping in the 0.5% sodium chloride (NaCl) bath, a constant humidity environment, and a drying period. Lap shear strength of the joints decreased with the cycles of corrosion exposure. Good joint strengths were retained at the end of 30-cycle test.

Gear rattle, clunk, and other such noises, commonly referred to as impulsive or unusual noise, are often classified as unique problems without common origins. This paper examines the underlying structure that promotes them and traces physical system behaviors that predispose them to such noises. Though the audible noise itself is not modeled directly, a good deal of the disposable energy that sustains it can be inferred from the impulsive dynamics that underlies the whole process. Further effort quantifies the energies involved and appraises the distinctiveness of the perceived noise. Whether one hears gear rattle or clunk depends on the initiating site within the system and the impulsivity index of the prevailing dynamics. Observable indicators suggest that periodic noise is supported by periodic dynamics and, similarly, impulsive noise, by impulsive dynamics and that the latter is non-deterministic, discontinuous and even chaotic.

A review of many years of published work has shown that hydrogen embrittlement can occur under rolling contact conditions. Breakdown of lubrication and contamination with water have been cited as the probable sources of atomic hydrogen. In this paper, a unique fracture morphology is identified and the mechanism of the fracture progression from initiation to final catastrophic failure is proposed. Development of beneficial residual compressive stress near the contacting surfaces is one approach used to avoid this type of failure. Several alternative methods capable of developing a more desirable stress distribution will be discussed.

Modern approaches to durability assurance in ground vehicle design are reviewed in the context of recent developments in computer-based analytical and experimental tools for use by designers and development engineers. Examples, using an automotive wheel assembly, are presented to illustrate the application of fatigue analysis in product development. Major challenges associated with the linking of various design tools into integrated networks appropriately configured for industrial problem solving are discussed along with an assessment of the potential benefits to be gained from such integration.

Hydraulic fluids of the HFC category are aqueous polymer solutions with a fire resistance enhancing water content of 35 to approx. 50 %. The use of HFC fluids, above all in mobile and stationary drives in mining and in casting is subject to restrictions resulting from a number of features of a fluid. Field practice has shown that while axial-piston pumps may be successfully operated using HFC fluids, rolling bearing failures reduce their operational lifetimes. The bearing failures essentially result from material fatigue. This can be remedied by new quality steel for roller bearings. The combination of high fatigue life and corrosion resistance assures a wide application range for nitrogen-treated steel qualities.

This paper provides a review of the fatigue properties reported in the open literature for die cast magnesium-based alloys. Recently developed fatigue data, in the form of stress versus number of cycles to failure for bending fatigue (R=-1), are presented for die cast AM60B and AZ91D alloy specimens with thicknesses between 1 and 10 mm. The effects of specimen thickness and macrostructural features, such as porosity distributions and surface features (parting line and ejection pin marks), on the fatigue data are discussed.

Reported tensile and fatigue properties of die cast AZ91D and AM60B magnesium alloys indicate that those values depend on the size and shape of the test samples and their global porosities. This paper reviews the mechanical properties reported in the open literature for these die cast alloys and indicates that section thickness and global porosity are inadequate for predicting the tensile and fatigue properties of die cast AZ91D and AM60B magnesium alloys.

Die cast AZ91D and AM60 magnesium alloy components are finding increasing usage in automotive applications. Both hot and cold chamber die cast components of these alloys generally exhibit several common microstructural features, including “skin”, porosity banding, and porosity distributed about the component centerline. Methods for quantitatively characterizing these microstructural features are described and representative values for skin thicknesses, porosity band dimensions and porosity band locations from selected die castings will be presented. The expected influence of these common microstrucutral features on mechanical properties and acceptability of die cast magnesium components for given applications are discussed.

There have been plastics in automobiles almost as long as there have been plastics. This paper deals with plastic molded parts from the 1930’s through 1970. These parts include steering wheels, tail light lenses, knobs, electrical connectors, fasteners, speedometer wheels, distributor caps, water pump impellers, dials, and various decorative ornaments.