With the introduction of a stringent particulate number (PN) limit and real driving emission (RDE) requirements, gasoline particulate filters (GPF) are widely adopted for gasoline engines in Europe and China. The filter collects soot and ash. Like in diesel applications, the collected soot will continuously burn under favorable exhaust conditions. However, at extreme conditions, there could be large amounts of soot build-up, which may induce a highly exothermal event, potentially damaging the filter. Thus, it is important to understand what drives the over-heating in application, and develop counter measures. In this study, an on-vehicle fuel cut (FC) testing procedure was developed. The testing was conducted on two vehicles, one gasoline direct injection (GDI) vehicle and one multiple port injection (MPI) vehicle, with different exhaust systems designs (a close coupled GPF and an under floor GPF) and catalyst coating levels (bare and heavily coated GPFs).

In the auto industry, lightweight window designs are drawing more attention for improved gas mileage and reduced exhaust emission. Corning’s Gorilla® Glass used in laminate design enables more than 30% weight reduction compared to conventional soda-lime glass laminates. In addition, Gorilla® Glass hybrid laminates (which are a laminate construction of a thick soda-lime glass outer play, a middle polyvinyl butyral interlayer, and a thin Gorilla Glass inner ply) also show significantly improved toughness due to advanced ion-exchange technology that provides high-surface compression. However, the reduced mass also allows increased transmission of sound waves through the windshield into the vehicle cabin. A system-level measurement approach has always been employed to assess overall vehicle acoustic performance by measuring sound pressure levels (SPL) at the driver’s ears. The measured sound signals are usually a superimposition of a variety of noise sources and transmission paths.

In order to effectively use CAE to meet wind noise NVH targets, it is important to understand the main wind noise transfer paths. Testing confirmation of these paths by means of acoustic wind tunnel test is expensive and not always available. An on-road test procedure including a “windowing” method (using barriers) was developed to measure wind noise contribution at important higher frequencies through the main transfer paths, which were shown by test to be the glasses at a typical operating condition in which wind noise was dominant. The test data was used to correlate a full-vehicle SEA (Statistical Energy Analysis) model that placed emphasis on the glass properties, main noise transfer paths, and interior acoustic spaces while simplifying all other transmission paths. A method for generating wind noise loads was developed using measured glass vibration data, exterior pressure data, and interior acoustic data.

Diesel particulate filters are expected to be used on most passenger car applications designed to meet coming European emission standards, EU5 and EU6. Similar expectations hold for systems designed to meet US Tier 2 Bin 5 standards. Among the various products oxide filter materials, such as cordierite and aluminum titanate, are gaining growing interest due to their unique properties. Besides the intrinsic robustness of the filter products a well designed operating strategy is required for the successful use of filters. The operating strategy is comprised of two elements: the soot estimation and the regeneration strategy. In this paper the second element is discussed in detail by means of theoretical considerations as well as dedicated engine bench experiments. The impact the key operating variables, soot load, exhaust mass flow, oxygen content and temperature, have on the conditions inside the filter are discussed.

The effect of web thickness on emission performance, pressure drop, and mechanical properties was investigated for a series of catalyzed ceramic monolith substrates having cell densities of 900, 600 and 400 cpsi. As expected, thinner webs provide better catalyst light off performance and lower pressure drop, but mechanical strength generally decreases as web thickness is reduced. Good correlations were found between emission performance and geometric parameters based on bare and coated parts. An improved method for estimating the effects of cell density and web thickness on bare substrate strength is described, and the effect of porosity on material strength is also examined. New mechanical strength correlations for ceramic honeycombs are presented. The availability of a range of ceramic product geometries provides options for gasoline exhaust emission design and optimization, especially where increased levels of performance are desired.

This paper employs a systematic approach to packaging design and testing of a system and its components in order to determine the long term durability of light duty diesel filters. This effort has utilized a relatively new aluminum titanate filter technology as well as an advanced support mat technology engineered to provide superior holding force at lower temperatures while maintaining its high temperature performance. Together, these two new technologies form a system that addresses the unique operating conditions of diesel engines. Key physical properties of both the filter and the mat are demonstrated through laboratory testing. The system behavior is characterized by various laboratory techniques and validation procedures.

Over the past decade, regulations for mobile source emissions have become more stringent thus, requiring advances in emissions systems to comply with the new standards. For the popular diesel powered passenger cars particularly in Europe, diesel particulate filters (DPFs) have been integrated to control particulate matter (PM) emissions. Corning Incorporated has developed a new proprietary aluminum titanate-based material for filter use in passenger car diesel applications. Aluminum titanate (hereafter referred to as AT) filters were launched commercially in the fall of 2005 and have been equipped on more than several hundred thousand European passenger vehicles. Due to their outstanding durability, filtration efficiency and pressure drop attributes, AT filters are an excellent fit for demanding applications in passenger cars. Extensive testing was conducted on engine to evaluate the survivability and long-term thermo-mechanical durability of AT filters.

Continuous improvement in vehicle emissions is necessary to meet ever tightening regulations. These regulations are advancing in both passenger and light truck vehicle markets, currently at different rates. Divergent design requirements and target markets for these platforms create unique conditions for aftertreatment needs. To understand the performance of various products in these categories and the potential for optimization, we examine various ultrathin-wall products in the context of a close-coupled configuration in a SULEV vehicle. In addition, these comparisons are carried over to a larger platform to show the performance trends in the context of the sport utility vehicle category. This study considers converter performance in FTP tests, examining bag data, light-off behavior, pressure drop comparisons and front and rear converter contributions. Conclusions are drawn regarding the optimization of converter substrate selection for various target design criteria

Current trends in automotive emissions control have tended towards reduced mass substrates for improved light-off performance coupled with a reduction in PGM levels. This trend has led to increasingly thinner walls in the substrates and increased open frontal areas, with a potential of reducing the overall mechanical strength of the substrate relative to the thicker walled lower cell density supports. This change in demand driven technology has also led to developments, at times costly, in the processing of the catalytic converter system. Changes in mat materials, handling technology and coating variables are only a few sources of overall increased system costs. Corning has introduced the Celcor® XS™ product to the market which significantly increases the strength of thin and ultra thin walled substrates.

Compositions in the mixed strontium/calcium feldspar ([Sr/Ca]O·Al2O3·2SiO2) - aluminum titanate (Al2O3·TiO2) system have been investigated as alternative materials for the diesel particulate filter (DPF) application. A key attribute of these compositions is their low coefficient of thermal expansion (CTE). Samples have been prepared with porosities of >50% having average pore sizes of between 12 and 16μm. The superior thermal shock resistance, increased resistance to ash attack, and high volumetric heat capacity of these materials, coupled with monolithic fabrication, provide certain advantages over currently available silicon carbide products. In addition, based on testing done so far aluminum titanate-based filters have demonstrated chemical durability and comparable pressure drop (both bare and catalyzed) to current, commercially available, silicon carbide products.

This paper provides elastic analysis of compressive stresses in the matrix and skin regions of automotive substrates during 3D- and 2D-isostatic strength testing. The matrix region is treated as transversely isotropic material and the skin region as isotropic material, each with their independent elastic properties. Such a solution helps quantify load sharing by the matrix and skin regions which, in turn, affect compressive stresses in each region. The analysis shows that the tangential compressive stresses in the skin and matrix differ significantly at the interface due to high stiffness ratio of skin versus matrix. The resulting strain in the skin is more severe for thin and ultrathin wall substrates and may lead to localized bending of interfacial cells thereby inducing premature failure. Methods to reduce compressive strain in both the matrix and skin without affecting performance-related advantages are discussed.

Diesel Oxidation Catalyst in conjunction with large frontal area substrates is a key element in HDV Diesel emission control systems. This paper describes and reviews tests on a set of various Diesel Oxidation Catalyst configurations (for example cell densities), all with the same catalyst coating. The Diesel Oxidation Catalyst specimens were subjected to the European Stationary Cycle (ESC), the European Transient Cycle (ETC), and the US heavy duty Federal Test Procedure (US FTP). The focus was to study relative emissions, pressure drop, and light-off performance. All tests were conducted using the same Detroit Diesel Series 60 engine operating on ultra low sulfur diesel fuel. In addition to this, the exhaust was regulated so that the backpressure on the engine, upstream of the catalyst was also the same for all catalysts.

This paper describes a study of ternary V2O5/WO3/TiO2 SCR catalysts coated on standard Celcor® and new highly porous cordierite substrates. At temperatures below 275°C, where NOx conversion is kinetically limited, high catalyst loadings are required to achieve high conversion efficiencies. In principle there are two ways to achieve high catalyst loadings: 1. On standard Celcor® substrates the washcoat thickness can be increased. 2. With new highly porous substrates a high amount of washcoat can be deposited in the walls. Various catalyst loadings varying from 120g/l to 540 g/l were washcoated on both standard Celcor® and new high porosity cordierite substrates with standard coating techniques. Simulated laboratory testing of these samples showed that high catalyst loadings improved both low temperature conversion efficiency and high temperature ammonia storage capacity and consequently increased the overall conversion efficiency.

The oven shock test is an accelerated test which is often used to quantify the thermal durability of both coated and uncoated ceramic substrates. The test calls for heating the substrate for 30 minutes in an oven, which is preheated to specified temperature, and then cooling it in ambient environment for 30 minutes. Such a cycle induces axial and tangential stresses, during cooling, in the skin region whose magnitude depends on physical properties, oven temperature, radial temperature gradient and the aspect ratio of substrate. In addition, these stresses vary with time; their maximum values occur as soon as the substrate is taken out of the oven. This paper evaluates the severity of thermal stresses as function of above factors and estimates the probability and mode of failure during cooling using thermocouple data. Methods to reduce these stresses are discussed.

The present work intends to examine the selective NOx reduction efficiency of a current commercial Titanium-Vanadium washcoated catalyst and to develop a transient numerical model capable of describing the SCR process while using a wide range of inlet conditions such as space velocity, oxygen concentrations, water concentration and NO2/NO ratio. The concentrations of different components (NO, NO2, N2O, NH3, H2O and HNO3) were analyzed continuously by a FT-IR spectrometer. A temperature range from 150°C up to 650°C was examined and tests were carried out using a model exhaust gas comparable to the real diesel exhaust gas composition. There is a very good correlation between experimental and calculated results with the given chemical kinetics.

Driven by the worldwide automotive emission regulations, ceramic substrates were developed to serve as catalyst support. Since the introduction of Standard wall substrates in 1974, substrates with thinner walls and higher cell densities have been developed to meet the tighter emission requirements; Worldwide, the amount of Thinwall and Ultrathinwall substrates in series applications is increasing continuously. The properties of the substrates determine their performance regarding pressure drop, heat-up and conversion efficiency. These properties are analyzed, as well as the packaging process for Thinwall and Ultrathinwall substrates; A new packaging technique with lower pressure load is described.

The diesel oxidation catalyst is required to remove hydrocarbons and carbon monoxide from the diesel engine exhaust stream while minimizing the impact of all other features such as cost, space, pressure drop, weight, fuel consumption, etc. The challenge of designing a catalytic converter for a particular application then becomes to: first, understand the emissions and other performance targets and requirements for the engine; second, understand the influence each of the converter parameters has on the overall system performance and; third, optimize the system using these relationships. This paper will explore some of the considerations with respect to the second of the above challenges.

Recently, SiC has been investigated and pursued as an alternative material for diesel particulate filter (DPF) applications. SiC has acceptable physical properties such as good thermal conductivity, refractoriness, and chemical durability. Materials for DPF applications require a particular mean pore size, porosity, and permeability. In addition, these material attributes must be coupled to an appropriate thermal design so that the filter can survive the extreme temperature gradients generated during the regeneration process. In this report several approaches to making porous SiC will be discussed and performance data based on material properties and thermal design will be presented.

This paper examines the relative thermal shock requirements for ceramic catalysts in underbody vs. close-coupled positions. The higher operating temperature in the latter position may imply higher coefficient of thermal expansion and higher thermal stresses, depending on substrate/washcoat interaction, than those for underbody position. An analysis of thermal stresses, using relevant physical properties and temperature gradients, is presented for both close-coupled and underbody catalysts. Three different high temperature close-coupled catalysts, employing advanced ceramic substrates with 600/3, 600/4 and 900/2 cell structure, and an underbody catalyst with 400/6.5 standard ceramic substrate are examined. Such an analysis is valuable for designing the optimum aspect ratio (length/diameter) and packaging system, which will minimize thermal and mechanical stresses over the desired lifetime of 120K vehicle miles.

A concern has been expressed regarding the durability of the ceramic thin wall and ultra-thin wall substrates under severe thermal and mechanical conditions. Damage that might result from these conditions would most likely lead to a reduction in catalyst performance. One of the potential damage mechanisms for automotive catalysts is erosion resulting from the impingement of particles onto the front face of the catalyst system. A basic study of the particulate erosion phenomenon of cellular ceramic substrates was undertaken in order to determine, in a controlled setting, the substrate, particulate, and flow conditions that might bring this damage about. This report will discuss a room temperature study of the effects of particle size, particle density, gas flow rate, cellular part orientation, and cellular design parameters on the erosion of ceramic substrates.