Improvements in component/system design is a daily challenge these days, always looking for high performance, reduced mass and low costs. The source for the best fit between these factors, coupled with adequate durability performance, is crucial to the success of a given product and this is what motivates engineering teams around the world. The demand for efficient projects with short deadlines for validation and certification is huge and simulation tools focused on accelerated durability and virtual validation are increasingly being used. When developing a new spring for commercial vehicles, lessons learned from the actual loads applied to the suspension are the “key” to a successful project. The loads/stresses from the ground (vertical loads, lateral loads, longitudinal and braking loads) are quite high and, consequently, relevant to the proper definition of the design of the suspension components.

Fatigue testing of components is used to validate new product designs as well as changes made to existing designs. On new designs it is common to initially test parts at the design stage (design verification or DV) and then again at the production stage (production verification or PV) to make sure the performance has not changed. On changes to existing designs typically the life of the new part (B) is compared to that of the old part (A). When comparing the fatigue life Weibull analysis is normally used to evaluate the data. The expectation is that the B10 or B50 life of the new part or PV parts should be equal to or better than that of the old parts or the DV parts. However, fatigue testing has a great deal of inherent variability in the resulting life. In this paper the variability of numerous carburized and induction hardened components is examined.

A series of bending fatigue tests were conducted and S-N data were obtained for two groups of 4320 steel samples: (1) carburized, quenched and tempered, (2) carburized, quenched, tempered and shot peened. Shot peening improved the fatigue life and endurance limit. The S-N data exhibited large scatter, especially for carburized samples and at the high cycle life regime. Sample characterization work was performed and scatter bands were established for residual stress distributions, in addition to fracture and fatigue properties for 4320 steel. Moreover, a fatigue life analysis was performed using fracture mechanics and strain life fatigue theories. Scatter in S-N curves was established computationally by using the lower bound and upper bound in materials properties, residual stress and IGO depth in the input data. The results for fatigue life analysis, using either computational fracture mechanics or strain life theory, agreed reasonably well with the test data.

Hydroformed components are replacing stamped parts in automotive frames and front end and roof structures to improve the crash performance of vehicles. Due to the increasing application of hydroformed components, a better understanding of the crash behavior of these parts is necessary to improve the correlation between full-vehicle crash tests and FEM analysis. Accurately predicting the performance of hydroformed components will reduce the amount of physical crash testing necessary to develop the new components and new vehicles as well as reduce cycle time. Virgin material properties are commonly used in FEM analysis of hydroformed components, which leads to erroneous prediction of the full-vehicle crash response. Changes in gauge and material properties during the hydroforming process are intuitive and can be reasonably predicted by using forming simulations. The effects of the forming process have been investigated in the FEA models that are created for crash analyses.

This paper discusses the virtual development process used to support design of a high-tonnage hydroform press. It also discusses the optimized design for structural integrity while achieving low target cost. Other considerations included optimization of setup issues such as press fabrication and assembly. Due to tightly constrained development time, a diverse range of CAE methodologies were used to refine and validate the design. Detailed linear and nonlinear finite element models were developed to provide the required accuracy in the critical regions of the press structure. From these detailed models simplified analytical tools were developed to calculate the key press parameters such as alternating stress and predicted fatigue life. Finite element models were validated with physical strain gage measurements from an array of strain gages installed on the production presses.

A new proprietary Atmospheric Pressure Microwave Plasma Technology, developed for various materials processing applications, has been applied to P/M sintering of cam lobes. The aims were a) to compare the new processing route with conventional process for the same alloy composition and b) to check the possibility of successful sintering at higher temperatures so that different higher temperature P/M alloys may be used. P/M green cam lobes were used, and sintering runs were carried out initially at temperatures comparable to that currently used in the conventional processes; this was followed by runs at higher temperatures that are not very practical in the conventional processing route due to equipment component constraints. Properties such as density and hardness were measured for the sintered samples, together with corresponding microstructural analysis.

The main objective of this paper is to investigate contact fatigue life models and to evaluate the effect of surface finish on contact fatigue life. The effect of surface finish on contact fatigue life was investigated experimentally using two roller contact fatigue tests. The test samples, i.e. rollers, were carburized, quenched and then tempered. Two different roller surface finishes were evaluated: machined and as heat-treated surface (baseline rough surface) vs. super finished surface (smooth). Because many factors are involved in sliding/rolling contact fatigue, contact fatigue modeling is still in the early development stage. In this work, we will analyze our contact fatigue test results and correlate contact fatigue life with several empirical contact fatigue models, such as the lambda ratio, a new surface texture parameter, and a normalized pitting model which includes Hertzian Stress, sliding, surface roughness and oil film thickness.

The effect of multiple braze furnace exposures has been questioned by many because the rework of brazed parts is a common practice in manufacturing. However, there are process controls that limit the number of exposures for an assembly due to known issues with multiple exposures. A common concern deals with the effect of multiple braze furnace exposures on the structural integrity of the base material of the components. Another concern regards the effect of multiple exposures on the structural integrity of the braze joint itself. This paper details experimental results of a physical study to investigate these questions. The material forms used are seam-welded tube and a thin-wall stamped component, both made from 304L stainless steel. The copper paste used in the study has an industry designation of ANSI/AWS A5.8 - BCu-1a.

Locati method is suitable in preliminary fatigue tests and production quality control. It is efficient since it uses just one test sample. The method requires that the slope of the S-N curve be known a priori, however. In this paper, a modified Locati method is presented that virtually eliminated this requirement. The method produces a point on the S-N plane that is independent of the slope of the S-N curve. The test design strategy to control the fatigue life of such a point is provided. The presented method has been successfully applied to preliminary fatigue tests of several welded components of ground vehicles.

Axle primary gearing is normally carburized for high and balanced resistance to contact fatigue, wear, bending fatigue, and impact loading. The focus of this work is on bending fatigue which is a key design consideration of automotive and commercial vehicle axle gearing. Since a carburized component is basically a composite material with steep gradients in carbon content, hardness, tensile strength and microstructure from surface to the middle of the cross section combined with non-linear residual stress, its bending fatigue life prediction is a complex and challenging task. Many factors affect the bending fatigue performance of axle gearing, such as gear design, gear manufacturing, loading history during service, residual stress distribution, steel grade, and heat treatment. In this paper, the general methodology for bending fatigue life prediction of a carburized component is investigated. Carburized steel composites are treated as two homogeneous materials: case and core.

This paper will describe the development of an accelerated testing methodology for an off-highway vehicle rotary oil seal system. There are two typical field failure mechanisms associated with off-highway input pinion shaft oil seals: 1) excessive abrasive wear of soft seal lip and hard shaft surface due to abrasive environment; 2) excessive heat and degradation of the seal lip due to lack of lubricity and wear of the shaft surface run against this seal. The accelerated testing of the rotary oil seal consisted of a combination of the following factors; shaft run-out, eccentricity, testing temperature, rotation and reciprocal motion of the seal lip relative to the shaft surface. The combination of these factors especially reciprocal motion reproduces the same failure mechanism, i.e. shaft wear grooves and oil seal lip wear observed on the field usage samples with 6,300 hours service in only 350 hours of accelerated testing.

Higher demands from automotive customers for quieter vehicles and the reduction of noise and vibration levels from major sources like the engine necessitate better performance of other sources of noise and vibrations in a vehicle. One of these sources that Original Equipment Manufacturers (OEM) demand making quieter is the power steering system. The pressure ripple generated by the power steering pump transfers to the fluid lines where it can generate objectionable noise and vibrations. This can become an excitation force to the structure of a vehicle or the steering gear and can become a source of discomfort to the vehicle occupants. Attenuation of the pressure ripple within the hose assembly can result in significant reduction in noise inside the vehicle. The NVH research team at the Fluid System Products of Dana Corporation has developed “Dana's Virtual Test Rig (DVTR™),” - a hydraulic system simulation software.

Vehicular suspension ball joints can be categorized in the family of tribological systems which can reduce useful service or working capacity through malfunction or breakdown. Detailed metallurgical analysis of the friction and wear mechanisms on typical ball joint bearing surfaces point to a Teflon-based woven fabric, self-lubricating liner as the best bearing material for the joint. Laboratory functional testing was conducted on modern, 4-axis test equipment simulating the applicable loading and motion conditions typically encountered in use. The self-lubricated bearing liner woven with Teflon thread demonstrated higher sustained load capacity, less rotating friction, excellent torque retention qualities and extended life in comparison to existing components utilizing greased metal-on-metal and/or “plastic” bearing materials.