Search Results

The application of tailored blanks to autobody parts has progressed because of its numerous advantages. The forming of tailored blanks has, however, a lot of technical problems. Among the problems, weld-line movement and formability deterioration are the most significant ones in case of deep drawing. The weld-line movement and formability change were examined experimentally as a function of weld-line location in square cup deep drawing. The weld-line movement of tailored blank consists of two sources. One is the geometrical reason, and the other is due to the hardening of weld bead. The formability of tailored blank is inferior to that of an original blank by the existence of hardened weld region. The mode of fracture changes from wall breakage to a fracture adjacent to punch radius when the weld-line was close to the punch corner.

A method of fatigue life prediction of spot welded joint under multi-axial loads has been developed by fatigue life estimation working groups in the committee on fatigue strength and structural reliability of JSAE. This method is based on the concept of nominal structural stress ( σ ns) proposed by Radaj and Rupp, and improved so that D value is not involved in stress calculation. The result of fatigue life estimation of actual vehicle with nominal structural stress which was calculated through newly developed method had very good correlation with the result of multi-axial loads fatigue test carried out with test piece including high strength steel.

In this paper the fatigue life of welded steel sheet structures is predicted by using FE-Fatigue, which is one of fatigue analysis software tools on the market, and these predicted results are evaluated by reference to corresponding experimental results. Also, we try to predict these structures by using two fatigue life prediction theories established by the JSAE fatigue and reliability committee to compare prediction results. It was confirmed that spot welds fatigue life predictions agree qualitatively with corresponding experimental results and arc welds fatigue life predictions are in good agreement with corresponding experimental results in cases where the SN curve database is modified appropriately.

The main operations for the manufacturing of auto parts are the cutting of the flange and the stamping. In order to perform accurate fatigue calculation it is necessary to have the material properties for each point of the structure. Usually, only the fatigue curve obtained on the flat sheet with polished edges is used because it represents the basic metal behaviour. The real edge quality decreases the fatigue limit while the hardening induced by the stamping increases it. To take these effects into account allows a better fatigue calculation of the structural part.

The influence of tensile strength on fatigue strength and the effect of strengthening mechanism on fatigue notch factor were investigated into conventional mild steels, HSLA steels, DP steels and TRIP steels. The grade of studied steels was altered from 440MPa to 780MPa. Not only smooth fatigue specimens with side surface ground and smooth fatigue specimens with laser-cut side surface but also fatigue specimens with a pierced hole were prepared for each of steel sheets. Fatigue tests were conducted in an axial load method. These experiments made it clear that the fatigue limits of smooth specimen increase along the tensile strength approximately independent of strengthening mechanism but those of notched specimen do not necessarily increase along the tensile strength. Namely, fatigue limits of DP steels and TRIP steels with notch increase in proportion to tensile strength although those of HSLA steels with notch do not increase.

Aluminum alloy sheets are used for automotive body-panels, but their small Young's modulus results in inferior shape-fixability than conventionally-applied steel sheets with similar strengths. Smaller radius of curvature, indicating better shape-fixability, is found at the center of a panel press-formed with higher blank holder force (BHF). Higher force can be applied for press-forming of alloy sheets with larger strain-hardening exponent (n value) induced by an increased addition of Mg. Recently-developed 5000 series alloy sheets containing 5.5 pct Mg and 0.3 pct Cu have an elongation over 33 pct at an ultimate tensile strength of 270 MPa and can be press-formed with better shape-fixability.

To give the wear-resistance to titanium intake valves by simple oxidation treatment, oxidation condition and microstructure of Ti-6Al-4V bars were studied. The wear test using a valve simulator shows that the wear of the face oxidized at 820°C for 1 and 4h in air is superior to that of ferrous valves. The best micro-structure of Ti-6Al-4V bar is an acicular structure with the prior β grain size of 30 to 60 μ m in average, which prevents distortion during the oxidation treatment and has excellent mechanical properties.

Carburizing heat treatment is one of the automobile component manufacturing steps, which consumes a large amount of energy. Raising the carburizing temperature can shorten the carburizing time and save the energy, but involves the risks of grain coarsening and attendant property deterioration. The authors have clarified the precipitation behavior of aluminum nitride (A1N) in the automobile gear manufacturing process and the optimum precipitation of A1N in as-rolled steel bars to prevent the grain coarsening. Through the application of the controlled rolling technique to ensure the optimum precipitation of A1N in continuously cast steel of uniform chemical composition, the authors have substantially saved energy while maintaining high quality, and developed a high-temperature carburizing steel expected to minimize and stabilize quenching strains.

Eight kinds of the spot-welded test specimens were studied to obtain the basic fatigue data on steel sheets for car bodies. Analytical methods such as the strain amplitude at outside and inside plates close to the nugget, the maximum nominal stress and Kθmax criteria of fracture mechanics were used. The authors propose that the ratio of strains at two points around the nugget can provide evaluation of the bending load and estimation of the fatigue strength.

The application of high-strength steel sheets to car bodies is expanding to improve the crashworthiness and achieve weight reduction [1, 2]. Conversely, in recent years, the occurrence of liquid metal embrittlement (LME) cracks has been discussed in resistance spot welding using a Zn-based coated high-strength steel [3-5]. This study examined the factors causing LME cracks and identified the locations of LME cracks found in resistance spot welds using a Zn-coated high-strength steel sheet. Furthermore, through an analytical approach using a scanning electron microscopy (SEM) and transmission electron microscopy (TEM), for a joint with an LME crack, it was found that (1) grain boundary fracture occurred at LME crack portion and its fracture surface was covered with Zn, (2) Zn penetrated into prior-austenite grain boundaries near the LME crack, and (3) Zn concentration decreased toward the tip of the Zn-penetrated site.