An inhibitor package which is silicate-, nitrate-, borate- and phosphate-free has been developed as the basis for a world-wide automotive coolant formulation. The formulation contains aliphatic mono- and dicarboxylic acids and tolyltriazole as the sole inhibitors. Formulations containing carboxylic acid inhibitors have been studied in ASTM bench tests and found to sufficiently protect all prevalent cooling system metals. In addition, fleet tests have shown that carboxylic acid inhibitors deplete much more slowly than conventional inhibitors, making possible a much longer life coolant. Results from laboratory tests which simulate extended usage indicated that carboxylic acid-containing coolants have a significantly longer life span for the protection of all cooling system metals. Finally, the carboxylic acid/tolyltriazole inhibitor package is completely adaptable to a propylene glycol base.

High lead solder coupons are frequently tested in ASTM D 1384-87 and D 2570-91 tests to determine the corrosion protection provided by engine coolants. In contrast to 70/30 solder, high lead solder is often observed to show relatively high corrosion rates in D 1384-87 testing. Surprisingly, the high lead solder corrosion rates tend to be lower in the D 2570-91 test, despite the longer duration of this test. The basis of this effect has been investigated in different coolant formulations and in both ethylene glycol and propylene glycol. The corrosion of high lead solder was found to be directly related to the presence of oxygen in the D 1384-87 test. Replacement of the air purge with a nitrogen purge significantly reduced the corrosion rate of high lead solder in inhibited coolants. These results are interpreted in terms of the solder composition.

Field-test samples cut from radiator tubes in two 1990 Chevy Luminas (3.1L engine) after 100,000 miles were analyzed to determine corrosion layer differences. One car used a carboxylic acid-based inhibitor technology (C1). The other car used a conventional coolant (C2). X-ray photoelectron spectroscopy (XPS) analysis of the two samples was performed. Results indicate a significant difference between the two samples. The C1 sample had a thin (<60Å) organic coating bound to the aluminum alloy surface, while the C2 sample had a much thicker (>1000 Å) silicate-rich layer. This resulted in the C2 sample exhibiting “surface charging” behavior. These results relate directly to the metal/insulator (conductor/insulator) characteristics of the two samples, and imply that the heat transfer of the protective coating provided by the carboxylate technology (C1) is significantly better than that of traditional inhibitor technology (C2).