Search Results

Hole expansion of a dual phase steel, DP600, was numerically investigated using a damage-based constitutive law to predict failure. The parameters governing void nucleation and coalescence were identified from an extensive review of the x-ray micro-tomography data available in the literature to ensure physically-sound predictions of damage evolution. A recently proposed technique to experimentally quantify work-hardening and damage in the shear-affected zone is incorporated into the damage model to enable fracture predictions of holes with sheared edges. Finite-element simulations of a hole expansion test with a conical punch were performed for both a punched and milled hole edge condition and the predicted hole expansion ratios are in very good agreement with the experiment values reported by several researchers.

Two different shear sample geometries were employed to investigate the elastoplastic and failure behaviour of three automotive alloy rolled sheets; a highly anisotropic magnesium alloy (ZEK100) and two relatively isotropic dual phase steels (DP600 and DP780). The performance of the so-called butterfly type specimen (Mohr and Henn 2007, Dunand and Mohr 2011) was evaluated at quasi-static conditions along with the shear geometry of Peirs et al. (2012) using in situ 3-D digital image correlation (DIC) strain measurement techniques. It was shown that both test geometries resulted in similar trends of the load-displacement response; however, the fracture strains obtained using the butterfly specimen were lower for the ZEK100 and DP780. It was demonstrated that the ZEK100 exhibits strong anisotropy in terms of the shear work hardening rate and failure strain.

A so-called damage percolation model is coupled with Gurson-based finite element (FE) approach in order to accommodate the high strain gradients and localized ductile damage. In doing so, void coalescence and final failure are suppressed in Gurson-based FE modeling while a measured second phase particle field is mapped onto the most damaged mesh area so that percolation modeling can be performed to capture ductile fracture in real sheet forming operations. It is revealed that void nucleation within particle clusters dominates ductile fracture in aluminum alloy sheet forming. Coalescence among several particle clusters triggered final failure of materials. A stretch flange forming is simulated with the coupled modeling.

Stretch flange features are commonly found in the corner regions of commercial parts, such as window cutouts, where large strains can induce localization and necking. In this study, laboratory-scale stretch flange forming experiments on AA5182 and AA5754 were conducted to address the formability of these aluminum alloys under undergoing this specific deformation process. Two distinct cracking modes were found in the stretch flange samples. One is radial cracking at the inner edge of flange (cutout edge) while the other is circumferential cracking away from the inner edge at the punch profile radius. Numerical simulation of the stretch flange forming operations was conducted with an explicit finite element code-LS-DYNA. A coalescence-suppressed Gurson-based material model is used in the finite element model. Void coalescence and final failure in stretch flange is simulated through measured second-phase particle fields with a so-called damage percolation model.

This work presents comparisons of finite element model predictions of static and dynamic denting with experimental results. Panels were stamped from 0.81, 0.93 and 1.00mm AA6111-T4 and then paint-baked to produce representative automotive outer body panels. Each type of panel was statically and dynamically dented at three locations using a 25.4mm steel ball. Static denting was accomplished with incremental loading of 22.24N loads up to a maximum of 244.48N. Dynamic denting was accomplished by dropping the steel ball from heights ranging from 200mm to 1200mm. Multi-stage finite element analysis was performed using LS-DYNA1 and ABAQUS2 to predict the entire process of forming, spring-back, denting and final spring-back of the dented panels. The predicted results show good correlation with the experiments, but also highlight the sensitivity of the predictions to formulation of the finite element problem.

New innovations in the field of advanced high strength steels (AHSS) have led to the development of steels with improved stretch-flangeability known as hot-rolled multi-phase (HR) steels. To understand the performance of HR steels, hole expansion tests were conducted on five prototype HR steels and compared with their commercial dual-phase (DP) steel equivalent. A variety of hole edge conditions were considered to study the influence of the shear-affected-zone (SAZ), the surface roughness at the sheared edge and the shear burr orientation. The microstructure of each material was characterized and discussed in relation to its formability for the different edge conditions. It was observed that the bainitic-ferrite microstructure of the HR steels showed superior formability during sheared edge stretching compared to commercial dual-phase steels.

The effect of stress triaxiality on failure strain in as-cast magnesium alloy AM60B is examined. Experiments using one uniaxial and two notched tensile geometries were used to study the effect of stress triaxiality on the quasi-static constitutive response of super vacuum die cast AM60B castings. For all tests, local strains, failure location and specimen elongation were tracked using two-dimensional digital image correlation (DIC) analysis. The uniaxial specimens were tested in two orthogonal directions to determine the anisotropy of the casting. Finite element models were developed to estimate effective plastic strain histories and stress state (triaxiality) as a function of notch severity. It was found that there is minimal, if any, anisotropy present in AM60B castings. Higher stress triaxiality levels caused increases in maximum stress and decreases in elongation and local effective plastic strain at failure.