Search Results

Recent engine design trends towards increasing power, reducing weight, advancing of injection timing and increasing of injection rate and pressure could result in increased incidence of liner pitting. Liner pitting due to coolant cavitation is a complex function of many engine design parameters and operating conditions as described in reference [1]*. Traditionally, liner cavitation problems were not detected early in the development cycle. Traditional liner vibration and coolant pressure measurements in conjunction with a numerous amount of expensive engine endurance tests were then needed to resolve cavitation problems. A method newly developed by the author and described in reference [2] for cavitation intensity measurements was successfully utilized to map out engine operating condition and develop limit curves. This method could also be applied in a non intrusive fashion.

Protocols for sampling and analysis of particulate and gaseous-phase diesel emissions were developed to characterize the chemical and biological effects of using ceramic traps as particulate control devices. A stainless-steel sampler was designed, constructed, and tested with XAD-2 sorbent for the collection of volatile organic compounds (VOC). Raw exhaust levels of TPM and SOF and mutagenicity of the SOF and VOC were all reduced when the traps were used. Hydrocarbon mass balances indicated that some hydrocarbons were not collected by the sampling system and that the proportions of collected SOF and VOC were altered by the use of the traps. SOF hydrocarbons appeared to be derived mainly from engine lubricating oil; VOC hydrocarbons were apparently fuel-derived. There was no apparent effect on SOF mutagenicity due to either sampling time or reexposure of particulate to exhaust gases.

The increase in power-to-weight ratio that results from the use of higher-horsepower diesel engines in highway service prompted this study of engine cooling. This paper covers the results obtained in testing different power-to-weight ratios on grades from sea level to over 11,000 ft and compares these results with those obtained from chassis and towing dynamometer cooling trials.

A series of comparative evaluation tests to determine the effect of various full-flow and combination full-flow and bypass filter systems on diesel engine piston ring and crankshaft bearings was made using radioactive tracer wear measurement and component weight loss techniques. The results of these tests indicate that bypass lube oil filtration combined with good full-flow lube oil filtration result in lowest engine wear rate and lowest total cost for the engine user.

Cavitation corrosion is a very complex phenomenon that is governed by a formidable amount of factors and parameters. The phenomenon is a multi-disciplinary one which involves several aspects of physical sciences and engineering. This process is a slow progressive phenomenon with its detrimental effects being felt after severe damage has already occurred. A real time detection method for the severity of fluid cavitation and bubble collapse is described. The results are correlated to dynamic instantaneous pressure fluctuation measurements. The method is fast, reliable, and less restrictive of the sensing location. It has been tested and verified through a specially designed cavitation test rig and instrumentation setup. The method can be used for cavitation studies on ultrasonic bench rig tests and for cavitation measurements on running engines. The method was used to shed some light on characteristic cavitation differences between water and glycol which is used in engine coolants.

RAPID CORROSIVE WEAR OF COPPER ALLOYS caused by a friction reducing additive was encountered in field tests of experimental lubricants. This oil soluble molybdenum, sulphur, and phosphorous containing additive subsequently was used in several commercial heavy duty diesel lubricants although the additive manufacturer did not recommend it for such applications. Numerous engine failures occurred due to the aggressiveness of this additive toward copper. Standard laboratory engine test methods or standard bench test methods did not predict the severe field problem. A new laboratory engine test method has been shown to duplicate the field failures. Bench test methods to duplicate the field failures are discussed. The mode of failure is shown and described.

Testing procedures to evaluate new coolant pump seal face materials and new coolant pump seal designs were evaluated. Rig testing of materials and seals followed by engine dynamometer testing enabled changes in the seal materials or design to be validated prior to field testing and limited production. These procedures were used to test and implement a coolant pump seal face material change to silicon carbide versus carbon. The change resulted in higher reliability for the coolant pump seal and reduced warranty cost for the engine.

A Minimum Cooled Engine (MCE) has been successfully run for 250 hours at rated condition of 298 kW and 1900 rpm. This engine was all metallic without any coolant in the block and lower part of the heads. Ring/liner/lubricant system and thermal loading on the liner at top ring reversal (TRR) as well as on the piston are presented and discussed. Ring/liner wear is given as well as oil consumption and blow-by data during the endurance run. Another engine build with a different top ring coating and several lubricants suggested that a 1500 hours endurance run of MCE is achievable. Rig test data for screening ring materials and synthetic lubricants necessary for a successful operation of a so-called Adiabatic Engine with the ring/ceramic liner (SiN) interface temperature up to 650°C are presented and discussed.

The effect of eight installation and component parameters on cooling system heat rejection and air flow were examined in detail in a wind tunnel facility. A quarter-replicate, two level factorial test plan was followed. Within the ranges of each parameter tested, the fan characteristics and the projection of fan into the shroud are highly significant parameters. The fan to radiator distance, the radiator characteristics, and the fan tip to shroud clearance are significant parameters. The fan to engine block distance and the type of shroud are not significant parameters.