Search Results

Forming Limit Diagrams (FLD) have been widely and successfully used in sheet metal stamping as a failure criterion to detect localized necking, which is the most common failure mechanism for conventional steels during forming. However, recent experience from stamping Dual-Phase steels found that, under certain circumstances such as stretching-bend over a small die radius, the sheet metal fails earlier than that predicted by the FLD based on the initiation of a localized neck. It appears that a different failure mechanism and mode are in effect, commonly referred to as “shear fracture” in the sheet metal stamping community. In this paper, experimental and numerical analysis is used to investigate the shear fracture mechanism. Numerical models are established for a stretch-bend test on DP780 steel with a wide range of bend radii for various failure modes. The occurrences of shear fracture are identified by correlating numerical simulation results with test data.

Edge fracture of advanced high strength steels (AHSS) can occur in both the stamping process and the crash event. Fracture due to poor sheared edge conditions in the stamping process was reduced with a recently developed optimal shearing process for AHSS. Currently, the improvement in the energy absorption due to the improved edge condition during crashes performed under different loading conditions had not been closely verified. The purpose of this study is to design and build a miniature component of AHSS and a three-point bending test for investigating the influence of various conditions of the sheared edge on the energy absorption in crashes. AHSS including DP600, TRIP780, DP980 and DP1180 were selected in the study. A small channel component was developed and fabricated using DP980 to simulate key features of the B-pillar. The exposed non-constrained, as-sheared edge was subject to stretch bending forces in three-dimensional space during the three-point bending test.

Practical evaluation and reduction of edge cracking are two challenging issues in stamping AHSS for automotive body structures. In this paper, the effects of the shear clearance and shear rake angle on edge cracking were investigated with three different grades of AHSS; TRIP780, DP 980, and DP 1180. Five different shear clearances, between 5% and 25% of material thickness, were applied to the flexible shearing machine to generate samples for the half specimen dome test (HSDT). The shear loads and the shear edge quality were thoroughly characterized and compared. The HSDT created the edge forming limits as compared to the base material forming limit diagram. The load-displacement curve was acquired by the load-cell and the strain distribution was measured using a digital image correlation (DIC) system during the dome test.

In the first part of this paper, a previously published acceleration compensation methodology for dynamic dent testing [1] was successfully applied to calculate dent loads and applied energy in dynamic dent testing. This procedure was validated utilizing a hydraulic controlled dynamic dent tester on a number of low carbon and bake hardenable steels. In the second part of this study, the impact of strain rate on material bending and hardening in high-speed dynamic dent resistance testing was studied. Previous work [2] investigated these factors in static dent resistance. The procedure utilized in that research was further developed and adapted for high speed testing and used as a basis for a new, single loading incremental dynamic dent test. This new test was used to investigate the effects of material bending and hardening in high-speed dynamic dent resistance. Testing incorporated laboratory produced stretch dome panels with 2% biaxial strains as test specimens.

Different die surface polish conditions result in a noticeable effect on material flow in stamping, which can lead to splitting, wrinkling, or other surface stretching issues associated with different friction conditions. These occurrences are not only limited to the non-coated dies, but also nitrided and chrome plated dies. To ensure quality control of the stamped parts, the die conditions corresponding to different polishing procedures need to be developed based on measurable parameters such as surface roughness (Ra). The intent of this study is to investigate the effects of nitrided and chrome plated die surface roughness on friction. The Bending-Under-Tension (BUT) test was conducted to simulate the stamping process due to the test’s versatility and flexibility in changing test parameters. The test involves moving sheet metal across a 3/8-inch diameter pin, which substitutes for a die surface. The pin can be modified by material, heat treatment, coating, and surface roughness.

The hole piercing process is a simple but important task in manufacturing processes. The quality requirement of the pierced hole varies between different applications. It can be either the size or the edge quality of the hole. Furthermore, the pierced hole is often subject to a secondary forming process, in which the edge stretchability is of a main concern. The recently developed advanced high strength steels (AHSS) and ultra high strength steels (UHSS) have been widely used for vehicle weight reduction and safety performance improvements. Due to the higher strength nature of these specially developed sheet steels, the hole piercing conditions are more extreme and challenging, and the quality of the pierced hole can be critical due to their relatively lower edge stretching limits than those for the conventional low and medium strength steels. The stretchability of the as-sheared edge inside the hole can be influenced by the material property, die condition and processing parameters.

Fracturing in a tight radius during bending is one of the major manufacturing issues in forming Advanced High Strength Steels (AHSS). The study investigated the bendability of AHSS under two forming conditions: bending with and without stretched over the die radius. The bendability was evaluated by conducting modified Bending Under Tension (BUT) test for stretch bending and 90o v bend test for bending without stretch. The study also examined the effect of material properties on the limiting bend ratio. Various strength high strength steels, range from 420 MPa to 1700 MPa tensile strength, were selected in the study. Results indicated that critical radius-to-thickness ratios between the two tests are different but correlated in a relationship which was depicted in the bendability diagram.

Zinc-based electrogalvanized (EG) and hot-dip galvanized (HDGI) coatings have been widely used in automotive body-in-white components for corrosion protection. The formability of zinc coated sheet steels depends on the properties of the sheet and the interactions at the interface between the sheet and the tooling. The frictional behavior of zinc coated sheet steels is influenced by the interfacial conditions present during the forming operation. Friction behavior has also been found to deviate from test method to test method. In this study, various lubrication conditions were applied to both bending under tension (BUT) test and a draw bead simulator (DBS) test for friction evaluations. Two different zinc coated steels; electrogalvanized (EG) and hot-dip galvanized (HDGI) were included in the study. In addition to the coated steels, a non-coated cold roll steel was also included for comparison purpose.

The thermal deflection associated with the conventional die heat treating procedure usually requires extra die grinding process to fine-tune the die surface. Due to the size of the production die, the grinding is time consuming and is not cost effective. The goal of the study is to develop a new die heat treating process utilizing the flexible laser heat treatment, which could serve the same purpose as the conventional die heat treating and avoid the thermal deflection. The unique look of the developed zebra pattern laser heat treating process is defined as the Zebra Line. The heat-treating parameters and processes were developed and calibrated to produce the laser heat treating on laboratory size dies, which were subjected to the die wear test in the laboratory condition. The USS HDGI 980 XG3TM steel was selected to be carried out on the developmental dies in the cyclic bend die wear test due to its high strength and coating characteristic.