Search Results

A general failure criterion for spot welds is proposed with consideration of the plastic anisotropy and the separation speed for crash applications. A lower bound limit load analysis is conducted to account for the failure loads of spot welds under combinations of three forces and three moments. Based on the limit load solution and the experimental results, an engineering failure criterion is proposed with correction factors determined by different spot weld tests. The engineering failure criterion can be used to characterize the failure loads of spot welds with consideration of the effects of the plastic anisotropy, separation speed, sheet thickness, nugget radius and combinations of loads. Spot weld failure loads under uniaxial and biaxial opening loads and those under combined shear and twisting loads from experiments are shown to be characterized well by the engineering failure criterion.

Quantitative planar laser-induced fluorescence measurements of fuel/air mixing in engines are usually based on the use of fluorescence tracers. The strength of the signals often depends on temperature, pressure and mixture composition. This complicates a quantitative analysis. The use of a small-bore optical engine for fundamental studies of absorption and fluorescence properties of fluorescence tracers is described. The temperature, pressure and composition dependence of the spectra of toluene, acetone, 3-pentanone, and biacetyl are examined under motored conditions to extend the experimental data base for the development of comprehensive models that predict the strength of fluorescence signals for a given condition.

A formulation that accounts for manufacturing variability in the analysis of structural/acoustic systems is presented. The methodology incorporates the concept of fast probability integration with finite element (FEA) and boundary element analysis (BEA) for producing the probabilistic acoustic response of a structural/acoustic system. The advanced mean value method is used for integrating the system probability density function. FEA and BEA are combined for producing the acoustic response that constitutes the performance function. The probabilistic acoustic response is calculated in terms of a cumulative distribution function. The new methodology is used to illustrate the difference between the results from a probabilistic analysis that accounts for manufacturing uncertainty, and an equivalent deterministic simulation through applications. The probabilistic computations are validated by comparison to Monte Carlo simulations.

An effective fatigue driving stress is proposed to predict the failure of spot welds under cyclic combined loading conditions. The effective fatigue driving stress is obtained based on the Mises yield criterion in terms of the resultant forces and moments in a plastic collapse analysis of spot welds under complex combined loading conditions as discussed in Lin et al. [1]. The effective fatigue driving stress can be used to correlate the fatigue data of spot welds with consideration of the effects of the sheet thickness, nugget diameter and loading conditions. Experimental results for coach-peel and lap-shear specimens under cyclic loading conditions are used to evaluate the applicability of the effective fatigue driving stress. The experimental results for spot welds in both coach-peel and lap-shear specimens are correlated very well based on the effective fatigue driving stress.

An automotive absorption air conditioning system would use engine-rejected heat as its energy source. Three possible cycles were studied, based on using water-lithium bromide, ammonia-water, and refrigerant 22-dimethyl ether of tetraethylene glycol as the refrigerant-absorbent pairs. Heat balances were calculated for the cycles and for a comparable vapor compression cycle. Energy input requirements, cooling capacities, coefficients of performance, and pressures and temperatures at various points in the cycle are given. Energy input requirements are compared with test data on the heat rejection from a 390 cu in. displacement production engine.

Closed-form stress intensity factor solutions at the critical locations of spot welds in four types of commonly used specimens are obtained based on elasticity theories and fracture mechanics. The loading conditions for spot welds in the central parts of four types of specimens are first examined. The resultant loads on the weld nugget and the self-balanced resultant loads on the lateral surface of the central parts of the specimens are then decomposed into various types of symmetric and anti-symmetric parts. Closed-form structural stress and stress intensity factor solutions for spot welds under various types of loading conditions are then adopted from a recent work of Lin and Pan to derive new closed-form stress intensity factor solutions at the critical locations of spot welds in the four types of specimens.

This paper analyzes and compares reactor and engine behavior of a diesel oxidation catalyst (DOC) in the presence of conventional diesel exhaust and low temperature premixed compression ignition (PCI) diesel exhaust. Surrogate exhaust mixtures of n-undecane (C11H24), ethene (C2H4), CO, O2, H2O, NO and N2 are defined for conventional and PCI combustion and used in the gas flow reactor tests. Both engine and reactor tests use a DOC containing platinum, palladium and a hydrocarbon storage component (zeolite). On both the engine and reactor, the composition of PCI exhaust increases light-off temperature relative to conventional combustion. However, while nominal conditions are similar, the catalyst behaves differently on the two experimental setups. The engine DOC shows higher initial apparent HC conversion efficiencies because the engine exhaust contains a higher fraction of trappable (i.e., high boiling point) HC.

When performing vibration analysis of complex vehicle structures, it is often important to be able to evaluate the effects of design changes in one or more substructures (e.g., for design optimization). It may also be convenient to allow different components to be modeled independently by different groups or organizations. For both cases, it is inevitable that some substructures will have non-matching finite element meshes at the interface where they are physically connected. Thus, a key challenge is to be able to handle the dynamic assembly of components with non-matching meshes and the subsequent global vibration analysis in a systematic and efficient manner. To tackle this problem, the enhancement of component mode synthesis methods for handling finite element models partitioned into non-matching substructures is considered in this paper. Some existing methods are reviewed, and new methods are developed.

This paper presents a general control module to control the speed of an electric vehicle (EV). This module consists of a microprocessor and several C-programmable micro-controllers. It uses an identification algorithm to estimate the system parameters on-line. With the estimated parameters, control gains are calculated via pole-placement. In order to compensate for the internal errors, a cross-coupling control algorithm is included. To estimate the true velocity and acceleration from measurements, a discrete-time Kalman filter was utilized. The experimental results validate the general control module for EVs.

The transient cone angle of a pressure swirl spray from an injector for gasoline direct injection engines was measured from 2D Mie scattering images. Iso-octane was used as the fluid that was delivered at room temperature for two different static pressures, 5MPa and 8.5MPa. The iso-octane was injected into a chamber at room temperature and ambient pressure. After a rapid initial increase, the cone angle oscillates before stabilizing to a steady-state value very close to the nominal cone angle. The period of the oscillation was found to correlate well with oscillations measured in the fuel line pressure.

In this investigation, dissimilar 5754/7075 and 7075/5754 spot friction welds were first made under different processing conditions. The spot friction welds in lap-shear specimens were tested under quasi-static loading conditions. The optimal processing times to maximize the failure loads of the 5754/7075 and 7075/5754 welds under lap-shear loading conditions are identified. The maximum failure load of the 7075/5754 welds is about 40% larger than that of the 5754/7075 welds. Optical micrographs of both types of spot friction welds made at different processing times before and after failure are examined. The micrographs show different weld geometries and different failure modes of spot friction welds made at different processing times. The failure modes of the 5754/7075 and 7075/5754 spot friction welds appear to be quite complex and strongly depend on the geometry and the strength of the interfacial surface between the two deformed sheet materials.

Characterization of materials used in the automotive industry is often done via component testing. A strict regimen of tests is conducted on a component to determine material parameters for numerical simulations of more complicated loading conditions. Separation of material constants and geometrically- or experimentallyinduced effects is difficult with this method of characterization. Well-controlled experiments that determine the material response in basic deformations allow material properties to be determined. In this paper low strain rate and high strain rate experimental responses of dummy skin material (i.e. plasticized polyvinyl chloride) are presented. Details of the experimental procedures used to acquire the data are also included. In addition, a rate-dependent constitutive model for the plasticized material is developed, and its simulated results are compared with low strain rate results.

The spark process has previously been shown to heavily influence ignition stability, particularly in direct-injected gasoline engines. Despite this influence, few studies have addressed spark behavior in direct-injected engines. This study examines the role of environmental factors on the behavior of the spark. Through measurement of the spark duration, by way of the ignition current trace, several observations are made on the influence of external factors on the behavior of the spark. Changing the level of nitrogen in the cylinder (to simulate EGR), the level of wetting and velocity imparted by the spray, the ignition dwell time and the orientation of the ground strap, observations are made as to which conditions are likely to produce unfavorable (shorter) spark durations. Through collection of a statistically significant number of sample spark lengths under each condition, histograms have been assembled and compared under each case.

Sandwich specimens with DP590 steel face sheets and structural epoxy foam cores are investigated under three-point bending conditions. Experimental results indicate that the maximum loads correspond to extensive cracking in the foam cores. Finite element simulations of the bending tests are also performed to understand the failure mechanisms of the epoxy foams. In these simulations, the plastic behavior of the steel face sheets is modeled by the Mises yield criterion with consideration of plastic strain hardening. A pressure sensitive yield criterion is used to model the plastic behavior of the epoxy foam cores. The epoxy foams are idealized to follow an elastic perfectly plastic behavior. The simulation results indicate that the load-displacement responses of some sandwich specimens agree with the experimental results.

Experiments to obtain the failure loads of spot welds are first reviewed under combined opening and shear loading conditions. A failure criterion is then presented for spot welds under combined opening and shear loading conditions based on the results from the experiments and a lower bound limit load analysis. In order to account for spot welds under more complex loading conditions, another lower bound limit load solution is presented to characterize the failure loads of spot welds under combinations of three forces and three moments. Based on the limit load solution, an engineering failure criterion is proposed with correction factors determined by different spot weld tests. The engineering failure criterion can be used to characterize the failure loads of spot welds with consideration of the effects of sheet thickness, nugget radius and combinations of loads.

In this paper, the formability of AA5754 aluminum laser-welded blanks produced by Nd:YAG laser welding is investigated under biaxial straining conditions. The mechanical behavior of the laser-welded blanks is first examined by uniaxial tensile tests conducted with the weld line perpendicular to the tensile axis. Shear failure in the weld metal is observed in the experiments. Finite element simulations under generalized plane strain conditions are then conducted in order to further understand the effects of weld geometry and strength on the shear failure and formability of these welded blanks. The strain histories of the material elements in the weld metal obtained from finite element computations are finally used in a theoretical failure analysis based on the material imperfection approach to predict the failure strains for the laser-welded blanks under biaxial straining conditions.

Fatigue failures of spot friction welds in lap-shear specimens of aluminum 6111-T4 sheets under cyclic loading conditions are investigated in this paper. The paths of fatigue cracks near the spot friction welds are first discussed. A fatigue crack growth model based on the Paris law for crack propagation and the global and local stress intensity factors for kinked cracks is then adopted to predict the fatigue lives of these spot friction welds. The global stress intensity factors and the local stress intensity factors based on the recent published works for resistance spot welds in lap-shear specimens are used to estimate the local stress intensity factors for kinked cracks with experimentally determined kink angles. The results indicate that the fatigue life predictions based on the Paris law and the local stress intensity factors as functions of the kink length agree well with the experimental results.

For applications of planar laser induced fluorescence (PLIF) to measure the fuel or equivalence ratio distributions in internal combustion (IC) engines it is typically assumed that the addition of a fluorescence tracer to a base fuel does not alter the combustion performance. We have investigated the impact on combustion performance through the addition of various amounts of 3-pentanone or toluene to iso-octane fuel. Correlations between equivalence ratio for a range of fuel/tracer mixtures and engine parameters, like peak pressure, location of peak pressure, indicated mean effective pressure (IMEP), and peak burn rate are discussed for data obtained in a spark-ignition direct-injection (SIDI) gasoline engine operated with near homogeneous charge. For typical tracer concentrations the impact on combustion performance is mostly negligible.

Coordinate measurement gages dominate in the area of dimensional control and variation reduction of automotive body assembly processes. However, coordinate measurement gages do not have the capability to track certain measured features. This incapability introduces inherent measurement error created by part (feature) mislocation in constrained non-measured directions. This inherent measurement error weakens the methods used for process control and variation reduction. In this paper, a principle of measurement uncertainty is developed in order to estimate the measurement error caused by this deficiency. The developed principle describes measurement error, which is independent of any other error related to the mechanical or optical coordinate measurement machines (CMMs, OCMMs). Additionally, an error map determined by the measurement uncertainty principle is created for error compensation.

The LDH (Limiting Dome Height Test) is widely used at Ford Motor Co. stamping plants laboratories to monitor the formability of incoming sheet materials. Although the LDH test is very easy to implement and interpret, variability of the results and poor reproducibility between laboratories limit its acceptance. In this investigation, some of the causes of variability and differences between plant laboratories are discussed. Much of the experimental work was done at plant laboratories and the results are directly applicable to quality control (QC) machines. It was found that the binder force and the binder shape have a big influence on the results, and they should be carefully controlled. The binder cleaning procedure is also relevant to the test variability. Punch temperature has a much greater influence on QC machines than on research machines and a method for controlling the punch temperature in QC machines is presented.