Vibration Welding Scale Up - A Comparison of Laboratory and Industrial Components 2002-01-0718

The objective of this study was to compare mechanical properties of lab-scale vibration welded test specimens with those of a complex automotive component using several different materials. Different laboratory specimens (butt, Tee, cup-plate with/without flash trap) were made under different vibration welding conditions (weld pressure, meltdown) and then tested in tension. The tensile properties of the specimens were then compared with the burst pressure results from a prototype air intake manifold. 30% glass reinforced nylon 66 and polypropylene compounds were used. The lab scale specimens and manifolds showed similar trends: (i) all parts failed at the weld; (ii) increased weld pressure generally caused decreased weld strength (iii) meltdown was observed to have little effect on part strength (iv) the ratio of lab specimen strength to burst strength was comparable but not equal for the materials tested. Flash traps significantly affect weld strength when over filled. At low weld pressures, over filled flash traps decrease weld strength. At high pressures, over filled flash traps increase weld strength.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

Vibration Welding of Glass Filled Nylon 66 - Effect of Part Geometry

2001-01-0440

View Details

TECHNICAL PAPER

Shear Strength of Vibration Welded Lap Joints

2004-01-0734

View Details

TECHNICAL PAPER

Use of Stainless Precision Strip for Multi-Layer Cylinder-Head Gaskets

2004-01-0889

View Details

X