The Effect of Ceria Content on the Performance of a NOx Trap 2003-01-1160

A study was performed on a lean NOx trap in which the loading of a ceria-containing mixed oxide in the washcoat was varied. After a mild stabilization of the traps, the time required to purge the NOx trap generally increased with increasing amount of mixed oxide. The purge NOx release also increased with increasing mixed oxide level but was greatly diminished after thermal aging. The sulfur tolerance of the NOx trap improved as the mixed oxide content was increased from 0% to 37%. The sample with 0% mixed oxide was more difficult to desulfate than the other samples due to poor water-gas-shift capability.
After thermal aging, the NOx reduction efficiency on a 60 second lean/5 second rich cycle was highest for the samples with 0% to 37% mixed oxide at evaluation temperatures of 400°C to 500°C. For the samples with higher amounts of mixed oxide, the higher oxygen storage capacities at these temperatures removed more of the reductants during the purges and led to incomplete purging of these samples. Conversely, the performance at 300°C was highest for the samples with 50 to 100% mixed oxide because the ceria provided NOx storage capability at low temperatures.
For both stabilized and thermally aged samples of the NOx traps, the sample with 0% mixed oxide had poor NOx conversion at stoichiometry relative to the other samples, but the HC conversion at 0.98 lambda generally decreased with increasing content of mixed oxide. After thermal aging, the stoichiometric lightoff temperature for 50% conversion generally increased with increasing content of mixed oxide. Considering all of these factors, the performance of the NOx trap in this study was maximized with 37% mixed oxide.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

A New Test for Catalyst Oxygen Storage Which Correlates with Catalyst Performance on the Vehicle

942071

View Details

TECHNICAL PAPER

High Temperature Stability of Ceria-Zirconia Supported Pd Model Catalysts

980668

View Details

TECHNICAL PAPER

Study of Large OSC Materials (Ln2O2SO4) on the Basis of Sulfur Redox Reaction

2009-01-1071

View Details

X