Intergranular Corrosion Susceptibility of Al-Mn-Cu Alloys, Heat-Treated after Simulated Brazing 2005-01-2026

The development of air-conditioners using CO2 refrigerants in place of freon-based refrigerants is underway. In these air-conditioners, the temperature of the heat-exchange cycle increases to 453 K [1]. The intergranular corrosion susceptibility of the Al-Mn-Cu alloy was investigated using the anode galvanic dissolution test after performing brazing and heat treatment at 453 K.
The intergranular corrosion susceptibility was dependent on the amounts of Mn and Cu, and heat treatment at 453 K resulted in an increase in the intergranular corrosion susceptibility. In the case where brazing was not followed by heat treatment at 453 K, TEM observation revealed Al-Cu intermetallic compounds with Al-Mn precipitates on the grain boundary. On the other hand, when heat treatment was carried out at 453 K, the growth of both Al-Cu intermetallic compounds and their precipitates was observed on the grain boundary with no Al-Mn precipitates. It is believed that the Cu-depleted zone along the grain boundaries increases with the precipitation of Cu on the grain boundary. This is believed to be the reason for an increase in the intergranular corrosion susceptibility with an increase in both the duration of heating at 453 K and the amounts of Mn and Cu.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

Effect of Brazing Temperature on Electrochemical Performance and Zinc Diffusion of AA7072 Clad in Tri-layer Aluminum Brazing Sheet AA7072/3003/4343

2005-01-2025

View Details

TECHNICAL PAPER

Tube-Fin Interaction - A Closer Look at the Corrosion Mechanism

2005-01-2027

View Details

TECHNICAL PAPER

Electrochemical and Corrosion Performance of Zinc-containing Tri-layer Aluminum Brazing Sheet AA7072/3003/4343 in OY Synthetic Water

2005-01-2035

View Details

X