SLAM, A Fast High Volume Additive Manufacturing Concept by Impact Welding; Application to Ti6Al4V Alloy 2006-01-3156

Against the manufacturing requirement for both lower lead time and reduced machining time for titanium components, a new concept was conceived assembling sheet material and other stock into semi finished parts by (explosive) impact welding. It is believed that this concept (which we named SLAM) could be especially beneficial for titanium alloy and nickel alloy.
The present investigation centered on the feasibility of this technology for the widely used Ti6Al4V alloy.
Impact process parameters were established and mechanical properties were investigated. In general, static properties were good. Fatigue strength reduced however, although much less so for notched specimens compared to un-notched material.
Fatigue crack initiation could be linked to complex features within the (wavy) weld interface associated with the ‘first generation’ impact welding parameters. Next steps are foreseen to improve the fatigue performance.
Two manufacturing demonstrators were manufactured showing the application to a T-bar manufactured from plate and sheet, as well as a tool-cladding application.


Subscribers can view annotate, and download all of SAE's content. Learn More »


Members save up to 16% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:

Nickel Alloy, Brazing Filler Metal 94Ni - 3.5Si - 1.8B 1800 °F (982 °C) Solidus, 1950 °F (1066 °C) Liquidus


View Details


Nickel Alloy, Brazing Filler Metal 71Ni - 10Si - 19Cr 1975 °F (1080 °C) Solidus, 2075 °F (1135 °C) Liquidus


View Details


Steel, Corrosion Resistant, Seamless or Welded Hydraulic Tubing 19Cr - 10Ni (304) Solution Heat Treated


View Details