Friction Stir Welding of Aluminum for Automotive Closure Panel Applications 2008-01-0145

Friction stir welding (FSW) shows advantages for joining lightweight alloys for automotive applications. In this research, the feasibility of friction stir welding aluminum for an automotive component application was studied. The objective of this research was to improve the Friction Stir Spot Welding (FSSW) technique used to weld an aluminum closure panel (CP). The spot welds were made using the newly designed swing-FSSW technique. In a previous study (unpublished), the panel was welded from the thin to thick side using both an 8 mm and a 10 mm diameter tool. The 10 mm tool passed various fatigue tests; however, the target was to improve performance of the 8 mm tool, especially to increase the number of cycle before the first crack appearance during fatigue testing. In this study fatigue tests and static strength was recorded for weld specimens that were welded from thick-to-thin with an 8 mm diameter tool. Coach peel coupons were welded to help optimize weld parameters and determine weld failure type (failure mode). Panels were welded using a multi-articulate robot and were fatigue tested, using a previously developed technique to 100,000 cycles. Fatigue tests showed improved fatigue life than had been previously achieved with 8 mm tool for thin-to-thick panel welding. Energy consumption for swing-FSSW panels was less than 700 J/weld, thus swing-FSSW can help reduce energy consumption and help contribute to Green Manufacturing.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

Spot Friction Welding of Mg-Mg, Al-Al and Mg-Al Alloys

2008-01-0144

View Details

TECHNICAL PAPER

Sand and Ceramic Casting Technology for Prototyping and “Bridge” Production of Complex Aluminum Die Cast Parts

2001-01-1048

View Details

TECHNICAL PAPER

Reinforcement Challenges and Solutions in Optimized Design of Injection Molded Plastic Parts

2003-01-1123

View Details

X