Fatigue Behavior of Dissimilar Spot Friction Welds between Aluminum and Coated Steel Sheets in Lap-Shear and Cross-Tension Specimens 2009-01-0036

Fatigue behavior of dissimilar Al/Fe spot friction welds between aluminum 6000 series alloy and coated steel sheets in lap-shear and cross-tension specimens is investigated based on experiments and three-dimensional finite element analyses. Micrographs of the welds after failure under quasi-static and cyclic loading conditions show that the Al/Fe welds in lap-shear and cross-tension specimens failed along the interfacial surface. Three-dimensional finite element analyses based on the micrographs of the welds before testing were conducted to obtain the J-integral solutions at the critical locations of the welds under lap-shear and cross-tension loading conditions. The numerical results suggest that the J-integral solutions at the critical locations of the welds can be used as a fracture mechanics parameter to correlate the experimental fatigue data of the Al/Fe spot friction welds in lap-shear and cross-tension specimens.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 43% off list price.
Login to see discount.
Special Offer: With TechSelect, you decide what SAE Technical Papers you need, when you need them, and how much you want to pay.
X