Fatigue Crack Growth for Typical CV Siderail Hole-making Processes Applied to Heat-treated Steel (MET1123) and Ultra High Strength Low Alloy Steel (120XF) 2009-01-2863

In order to provide the best siderail chassis value to the global commercial vehicle (CV) market two key aspects were investigated in this study:
  1. 1.
    A mechanical characterization for the industry standard heat-treated steel (MET1123) and a comparable ultra-high strength steel (120XF).
  2. 2.
    The impact common hole making processes have on commercial vehicle siderails -specifically crack growth.
For acceptance in the global CV industry it was key to collaborate with recognized research and testing facilities for the respective areas of evaluation.
This study was divided into 2 phases: Material evaluation and fatigue crack growth.
The material evaluation phase determined monotonic properties such as strength, impact and % elongation. As part of the material evaluation the low cycle fatigue (LCF) properties were also evaluated. The heat-treated steel (MET1123) has an industry strength requirement for yield and ultimate of 120ksi (838mpa) and 130ksi (910mpa) respectively and this was met. The ultra high strength steel (120XF) is a new grade, currently in the development phase and these respective properties were slightly less than the MET1123, although very close to the industry standard. The LCF results of the MET1123 and 120XF were comparable.
The next phase of the study was the fatigue crack growth. The holes were cut with: a hydraulic Punch press, CO2 laser, numerically-controlled (NC) drill and O2 Plasma torch. The coupons used were extracted from actual siderails and the holes were processed in the same fashion as the holes cut into a typical production siderail. The specimens were configured into SAE keyhole coupons. The threshold stress intensity, Kth, and crack growth rates were most favorable for the punch press. The HT (MET1123) steel outperformed the HSLA (120XF) for threshold, crack growth rates and fracture toughness for all processes.


Subscribers can view annotate, and download all of SAE's content. Learn More »


Members save up to 18% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:

Galfan Coated Steel for Automotive Applications


View Details


Effect of Balanced Biaxial Stretching on the Low Cycle Fatigue Behavior of SAE 1008 Hot Rolled Low Carbon Steel


View Details


High Strength Ductile Cast Iron in Suspension Components - Structural Durability and Impact Energy Absorption


View Details