The Effect of Surface Finish on Aluminum Sheet Friction Behavior 2011-01-0534

Aluminum sheet is commercially available in three surface finishes, mill finish (MF), electric discharge texture (EDT), and dull finish (DF). This surface finish impacts the friction behavior during sheet metal forming. A study was done to compare ten commercially available sheet samples from several suppliers. The friction behavior was characterized in the longitudinal and transverse directions using a Draw Bead Simulator (DBS) test, resulting in a coefficient of friction (COF) value for each material. Characterization of the friction behavior in each direction provides useful data for formability analysis. To quantitatively characterize the surface finish, three-dimensional MicroTexture measurements were done with a WYKO NT8000 instrument. In general, the MF samples have the smoothest surface, with Sa values of 0.20-0.30 μm and the lowest COF values. The EDT samples have the roughest surface, with Sa values of 0.60-1.00 μm, and the highest COF values. The DF sample falls between the MF and EDT with Sa = 0.60 μm. Also, the EDT and DF samples have a more isotropic surface, as indicated by Stylus X Ra/Stylus Y Ra = 0.97-1.01, and the COF values are approximately the same in the transverse and longitudinal directions for these samples. The MF samples are less isotropic, with Stylus X Ra/Stylus Y Ra = 1.79-4.87, and the COF values are lower in the transverse direction than in the longitudinal direction for the MF samples.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
We also recommend:
TECHNICAL PAPER

Experimental Study of Stretchability of Sheared Edge of Aluminum Sheet 6111-T4

2015-01-0516

View Details

TECHNICAL PAPER

A Fresh Look at Resistance Spot Welding of Aluminum Automotive Components

940160

View Details

JOURNAL ARTICLE

Effects on Surface Roughness and Friction on Aluminum Sheet under Plain Strain Cyclic Bending and Tension

2011-01-0535

View Details

X