Failure Mode and Fatigue Behavior of Ultrasonic Spot Welds with Adhesive in Lap-Shear Specimens of Magnesium and Steel Sheets 2013-01-1020

Failure modes and fatigue behaviors of ultrasonic spot welds in lap-shear specimens of magnesium AZ31B-H24 and hot-dipped-galvanized mild steel sheets with and without adhesive are investigated. Ultrasonic spot welded, adhesive-bonded, and weld-bonded lap-shear specimens were made. These lap-shear specimens were tested under quasi-static and cyclic loading conditions. The ultrasonic spot weld appears not to provide extra strength to the weld-bonded lap-shear specimen under quasi-static and cyclic loading conditions. The quasi-static and fatigue strengths of adhesive-bonded and weld-bonded lap-shear specimens appear to be the same. For the ultrasonic spot welded lap-shear specimens, the optical micrographs indicate that failure mode changes from the partial nugget pullout mode under quasi-static and low-cycle loading conditions to the kinked crack growth mode under high-cycle loading conditions. For the adhesive-bonded lap-shear specimens, the optical micrographs indicate that failure mode changes from the cohesive failure mode near the interfaces under quasi-static and low-cycle loading conditions to the kinked crack growth mode under high-cycle loading conditions. For the weld-bonded lap-shear specimens, the optical micrographs indicate that failure mode changes from the cohesive failure mode near the interfaces through the adhesive and interfacial failure mode through the spot weld under quasi-static and low-cycle loading conditions to the kinked crack growth mode under high-cycle loading conditions.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
We also recommend:
JOURNAL ARTICLE

Failure Mode and Fatigue Behavior of Friction Stir Spot Welds in Lap-Shear Specimens of Dissimilar Advanced High Strength Steels

2013-01-1023

View Details

JOURNAL ARTICLE

Fatigue Behavior of Spot Friction Welds in Cross-Tension Specimens of Aluminum 6061-T6 Sheets

2011-01-0470

View Details

JOURNAL ARTICLE

Investigation of Failure Mode and Fatigue Behavior of Flow Drill Screw Joints in Lap-Shear Specimens of Aluminum 6082-T6 Sheets

2016-01-0501

View Details

X