Improved Soot Combustion in DPF Catalyzed by Ceria Nanofibers: The Importance of Soot-catalyst Contact 2013-24-0164

Ceria nanofibers were synthesized as soot oxidation catalysts. The morphology of the catalyst was tailored to maximize the contact between the soot particles and the catalyst. Of the synthesized catalysts, the fibrous shape was the most active toward soot oxidation: the peak combustion temperature was reduced from 600°C (non-catalytic combustion) to 375°C during tight contact, 428°C during prolonged loose contact (see detailed definition in the text), and 553°C during loose contact. These results were compared to a very active ceria catalyst generated using the Solution Combustion Synthesis method and characterized by its high porosity and SSA surface. However, although the nanofibers have one fifth of the BET that the nanopowders obtained with SCS have, they display almost the same activity under tight conditions and considerably better activity during prolonged loose contact: their peak temperature was 31°C lower than the peak temperature for SCS-obtained nanopowders during the latter. This encourages us to investigate the interaction between the morphology and real contact conditions between the catalyst and soot in Diesel Particulate Filters (DPF) and to tailor the DPF catalytic support toward enhancing this contact while maintaining the low pressure drop associated with the catalytic layer.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 43% off list price.
Login to see discount.
Special Offer: With TechSelect, you decide what SAE Technical Papers you need, when you need them, and how much you want to pay.
X