High-Cycle and Impact Fatigue Behavior of Carburized Steels 780771

The influence of residual stress and retained austenite on the fracture behavior of bend test specimens of carburized steels was evaluated. The test results are part of an ongoing research effort intended to compare the relative fracture properties of alternate grades of steel and their respective standard grades having similar hardenability. In general, steels of equal hardenability and core carbon content exhibited similar fracture behavior. Compressive residual stress in the carburized case was found to significantly influence the impact fracture stress which, in turn, was correlated with impact fatigue properties. High levels of retained austenite at the surface caused the peak compressive residual stress to occur further into the case. The occurrence of residual stress peaks further into the case was not necessarily detrimental to impact fracture stress or impact fatigue properties. High-cycle fatigue limits were more dependent on processing variables than on differences in alloy content.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 18% off list price.
Login to see discount.
Special Offer: Download multiple Technical Papers each year? TechSelect is a cost-effective subscription option to select and download 12-100 full-text Technical Papers per year. Find more information here.
We also recommend:
TECHNICAL PAPER

Fatigue Strength as a Design Criterion

700556

View Details

TECHNICAL PAPER

Further Developments Towards a Standard Accelerated Corrosion Test for Automotive Materials

912277

View Details

TECHNICAL PAPER

The Effect of Galvanizing on the Fatigue Characteristics of an HSLA Steel

780042

View Details

X