Mechanism of Corrosion and Delamination of Painted Phosphated Steel During Accelerated Corrosion Testing 860110

A THEORETICAL MODEL for the delamination of organic coatings from zinc-phosphated steel surfaces will be presented. It will be shown that under ambient conditions and in neutral NaCl media delamination occurs as a result of the formation of a surface-tension gradiant during oxygen depolarization and, subsequently, the disruption of adhesion at the coating-phosphate interface. Dissolution of the phosphate coating occurs only after adhesion is lost. An accelerated cathodic delamination test showing good correlation with the long-term GM-scab test will also be introduced.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 43% off list price.
Login to see discount.
Special Offer: Purchase more aerospace standards and aerospace material specifications and save! AeroPaks off a customized subscription plan that lets you pay for just the documents that you need, when you need them.
X