Valve Spring with High Fatigue Resistance for Automotive Engine 880417

Recently, SiCr clean steel wire for springs on automotive engine valves has been developed. This report describes the characteristics of valve springs subjected to a new manufacturing process using SiCr clean steel wire. The process developed by the authors is as follows: First, form a helical spring with SiCr clean steel wire. Next, quench using the distortion preventing technic --Marquenching--. Temper at a temperature lower than the conventional temperature. Shot peen to the surface layer of the spring. And lastly, polish electrolytically to remove micro surface defects formed through shot peening. Using this new manufacturing process, a valve spring with high fatigue resistance can be produced. At the test stress of 588MPa(τm)±490MPa (τa), the number of cycles to fracture was above 100 million, while the number of cycles to fracture was 4 million using the conventional process with the SiCr clean steel which has the best fatigue resistance for commercial use.

SAE MOBILUS

Subscribers can view annotate, and download all of SAE's content. Learn More »

Access SAE MOBILUS »

Members save up to 43% off list price.
Login to see discount.
Special Offer: With TechSelect, you decide what SAE Technical Papers you need, when you need them, and how much you want to pay.
X