The application of tailored blanks to autobody parts has progressed because of its numerous advantages. The forming of tailored blanks has, however, a lot of technical problems. Among the problems, weld-line movement and formability deterioration are the most significant ones in case of deep drawing. The weld-line movement and formability change were examined experimentally as a function of weld-line location in square cup deep drawing. The weld-line movement of tailored blank consists of two sources. One is the geometrical reason, and the other is due to the hardening of weld bead. The formability of tailored blank is inferior to that of an original blank by the existence of hardened weld region. The mode of fracture changes from wall breakage to a fracture adjacent to punch radius when the weld-line was close to the punch corner.

Improvement of material characteristic values, adjustment of forming conditions as well as introduction of new forming technics are necessary to promote wide application of aluminum alloy sheets into automotive parts. 5000 series and 6000 series aluminum alloy sheets are concerned about the relationship between material characteristic values and fundamental forming ability required to apply them to automobile body parts as well as the effect of lubricant on their formability. The hardening parameters, n values, of them are larger than those of cold-rolled steel sheets. However, the r values and the local elongations are extremely small. The improvement of stretch formability owing to increase of n value is smaller than that of the steel sheets. Inferior deep drawability of the aluminum alloy sheets is due to low fracture resistance force caused by low r value.

This paper describes the deformation analysis of hemispherical punch stretching and square shell drawing, using 3-D finite element program “ROBUST”. The effects of material properties and process factors on cup height to punch force relation, and strain distributions on formed parts were investigated. The calculated values give considerably good agreement with experimental measurements from LDH, FLD and square shell tests. The results can be expected to contribute to predictive evaluation of forming limits using computer simulation.

Aluminum alloy sheets are used for automotive body-panels, but their small Young's modulus results in inferior shape-fixability than conventionally-applied steel sheets with similar strengths. Smaller radius of curvature, indicating better shape-fixability, is found at the center of a panel press-formed with higher blank holder force (BHF). Higher force can be applied for press-forming of alloy sheets with larger strain-hardening exponent (n value) induced by an increased addition of Mg. Recently-developed 5000 series alloy sheets containing 5.5 pct Mg and 0.3 pct Cu have an elongation over 33 pct at an ultimate tensile strength of 270 MPa and can be press-formed with better shape-fixability.