Search Results

The conventional forming limit curve (FLC) has been widely and successfully used as a failure criterion to detect localized necking in stamping. However, in stamping advanced high strength steels (AHSS), under certain circumstances such as stretching-bending over a small die radius, the sheet metal fails much earlier than predicted by the FLC. This type of failure on the die radius is commonly called “shear fracture.” In this paper, the laboratory Stretch-Forming Simulator (SFS) and the Bending under Tension (BUT) tester are used to study shear fracture occurring during both early and later stages of stamping. Results demonstrate that the occurrence of shear fracture depends on the combination of the radius-to-thickness (R/T) ratio and the tension/stretch level applied to the sheet during stretching or drawing. Based on numerous experimental results, an empirical shear fracture limit curve or criterion is obtained.

Forming Limit Diagrams (FLD) have been widely and successfully used in sheet metal stamping as a failure criterion to detect localized necking, which is the most common failure mechanism for conventional steels during forming. However, recent experience from stamping Dual-Phase steels found that, under certain circumstances such as stretching-bend over a small die radius, the sheet metal fails earlier than that predicted by the FLD based on the initiation of a localized neck. It appears that a different failure mechanism and mode are in effect, commonly referred to as “shear fracture” in the sheet metal stamping community. In this paper, experimental and numerical analysis is used to investigate the shear fracture mechanism. Numerical models are established for a stretch-bend test on DP780 steel with a wide range of bend radii for various failure modes. The occurrences of shear fracture are identified by correlating numerical simulation results with test data.

Advanced High Strength Steels (AHSS) such as DP590 HDGI are helping automakers meet increasingly higher structural performance requirements while maintaining or reducing weight of the vehicle body structure [7]. One of the issues facing design engineers implementing new materials such as AHSS is the lack of understanding the expected material variability within a steel supplier and also from one steel supplier to another; and how the variability affects product attribute performances. In this paper, we present an analysis of the aggregated mechanical property variability data obtained from several steel suppliers for a popular AHSS grade and also present studies related to the effect of material variability on structural responses.

Advanced high strength steels (AHSS) are particularly attractive to automotive industry. Stamping AHSS parts, however, results in accelerated die wear problems which could emerge after few thousands of stampings. The existing wear testing methods are either not suitable for charactering die wear in stamping or requires significant capital investment. The first generation of strip-on-cylinder wear test apparatus which can efficiently and economically characterize die wear is introduced in this paper. Different measurement methods were compared and white light interferometer with nanoscale accuracy was chosen to determine the wear volume due to its overall advantages. Based on the strip-on-cylinder wear test apparatus, a design of experiments study analyzing the effects of contact pressure, sliding speed and hardness of the die material on die wear was conducted and the results were discussed.

Die wear is a significant issue in sheet metal forming particularly for stamping Advanced High-Strength Steels (AHSS) because of their higher strength and microstructure composition. Reliable predictions of the magnitude and distribution of die wear are essential if cost-effective wear-protection strategies are desired in the early stages of tooling development. A die Wear Severity Index (WSI) is introduced in this paper to quantify the magnitude of die wear, which in essence characterizes the frictional energy dissipation per unit area on the die surface throughout the entire forming cycle. It can be readily obtained as part of any finite element simulation of stamping process utilizing incremental solution techniques.

Prediction of springback has become a major focus in sheet metal forming. Validation of finite element codes that are being developed to predict springback require accurate property data and a more complete understanding of the residual stresses that are involved. To provide experimental data for these calculations, neutron and synchrotron X-ray diffraction measurements were carried out to determine the through-thickness distribution of axial and hoop (or tangential) residual stresses in deep-drawn steel and aluminum cups. The techniques are able to provide true spatial resolutions as low as 0.05 mm for a strain measurement on cups with ≤ 1 mm wall thickness. It was found that the stresses exhibit non-linear gradients through the thickness that also depend on the axial position.

Dent resistance is an important attribute in the automotive panel design, and the ability to accurately predict a panel's dentability requires careful considerations of sheet metal properties, including property changes from stamping process. The material is often work-hardened significantly during forming, and its thickness is reduced somewhat. With increased demand for weight reduction, vehicle designers are seriously pushing to use thinner-gauged advanced high-strength steels (AHSS) as outer body panels such as fenders, hoods and decklids, with the expectation that its higher strength will offset reduced thickness in its dentability. A comparative study is conducted in this paper for a BH210 steel fender as baseline design and thinner DP500 steel as the new design.

Experimental procedures and results of a benchmark test for springback are reported and a complete suite of obtained data is provided for the validation of forming and springback simulation software. The test is usually referred as the Slit-Ring test where a cylindrical cup is first formed by deep drawing and then a ring is cut from the mid-section of the cup. The opening of the ring upon slitting releases the residual stresses in the formed cup and provides a valuable set of easy-to-measure, easy-to-characterize springback data. The test represents a realistic deep draw stamping operation with stretching and bending deformation, and is highly repeatable in a laboratory environment. In this study, six different automotive materials are evaluated.