Examination of field-fractured windshields was conducted for purposes of determining the principle fracture mechanisms experienced in-use. Samples for the study were gathered both in the United States (New York) and in Europe (France) to explore whether the primary causes of failure were similar for the different geographic regions. In total, over two hundred individual field-fractures were obtained and examined for the study. Detailed fracture analysis of the parts was performed, and multiple fracture mechanisms were identified and quantified. It was found that the two most frequently observed failure modes were common for both regions with the most frequent cause (~70%) of fractures being due to sharp contact of the exterior ply, while Hertzian cone cracking of the outer ply was the second leading cause (~20%). Several other modes were also identified. Given that sharp impact fracture was the dominant observed failure mode, a high-speed, sharp impact test method was developed.

The use of lightweight materials to produce automotive glazing is being pursued by vehicle manufacturers in an effort to improve fuel economy. As glazing’s become thinner, reduced rigidity means that the critical flaw size needed to create fracture becomes much smaller due to increased strain under load or impact. This paper documents experiments focused on the impact performance of several alternative thin laminate constructions under consideration for windshield applications (including conventional annealed soda-lime glass as well as laminates utilizing chemically strengthened glass), for the purpose of identifying new and unique failure modes that result from thickness reduction. Regulatory impact tests and experiments that focused on functional performance of laminates were conducted. Given the increased sensitivity to flaw size for thin laminates, controlled surface damage was introduced to parts prior to conducting the functional performance tests.