Search Results

Deformation Resistance Welding (DRW) is a process that employs resistance heating to raise the temperature of the materials being welded to the appropriate forging range, followed by shear deformation which increases the contacting surface area of the materials being welded. Because DRW is a new process, it became desirable to establish variable selection strategies which can be integrated into a production procedure. A factorial design of experiment was used to examine the influence of force, number of pulses, and weld cycles (heating/cooling time ratio) on the DRW process. Welded samples were tensile tested to determine their strength. Once tensile testing was complete, the resulting strengths were observed and compared to corresponding percent heat and percent reduction in thickness. Tensile strengths ranged from 107 kN to 22.2 kN. A relationship between the maximum current and the weld variables was established.

Conductive heat resistance seam welding (CHRSEW) is a new process developed at Edison Welding Institute for creating butt joints on aluminum sheet. The process uses conventional resistance seam welding equipment, and takes advantage of steel cover sheets on either side of the intended joint. Resulting joints are fusion in character, and can be manufactured at very high welding speeds (∼ 3 to 4 m/min). In this study, the conductive heat resistance seam welding process was extended to some new applications. These included joining a 7075-T6 alloy, and a dissimilar thickness 1- to 2-mm 5754 configuration. The former is generally considered unweldable by fusion methods, and is of considerable interest for aerospace applications. The latter is representative of a tailor welded blank for automotive applications. Resulting welds were evaluated using metallurgical examinations and mechanical testing.

Laser welding has long been evaluated as a joining technique for galvanized steels in a lap-joint configuration in the automotive industry. However, a problem associated with the low boiling point of zinc limits the application of the laser process in a lap-joint configuration. Zinc-coatings at the interface of the two coated sheets vaporize during welding and the volume of the zinc vapor expands rapidly. The venting of the zinc vapor from the weld pool causes expulsion of the molten metal during welding and a portion of zinc vapor remains in the weld as porosity after welding. To improve the weld quality of galvanized steel, many efforts have been attempted worldwide, but limited success has been reported. Edison Welding Institute (EWI) investigated the laser weldability of galvanized steel in a lap-joint configuration with no gap using a dual beam laser welding technique.

Weldability study has been performed on Polypropylene (PP) and PC/ABS samples to investigate how the paint layer along the weld joint affects the vibration weldability. The plastic used for this study were PP representing semicrystalline thermoplastics and PC/ABS representing amorphous thermoplastics. Both resins were molded to generate sample plaques for the study. Design of Experiment (DOE) studies were initially conducted with unpainted plaques and then repeated with the painted plaques for comparison. Optimal welding parameters were determined through DOE and the maximum weld strength under optimized welding conditions were determined and compared. Following each DOE, a regression analysis, using the weld strength as a response, was performed.

Friction stir welding (FSW) is a new welding process developed at The Welding Institute in Cambridge, U.K. This process uses a non-consumable rotating third body to generate frictional heat and create forging to facilitate continuous solid-state joints. In this paper, the current state of the art of FSW is discussed. A preliminary description of the process is provided, followed by the results of some relatively simple thermal modeling. The modeling results are used to provide a description of temperature distributions in FSW, as well as illustrate the effects of variations in process conditions. Representative microstructures of FSW on an Al 6061 alloy are then presented. Properties of these friction stir welds are then discussed and compared to those of both the base metal and to comparable GTAW welds. Some discussion is then given to the effects of section thickness on FSW. Examples are given of friction stir welds on aluminum alloys ranging from 2 to 30 mm in thickness.

The fatigue performance of fillet-welded transverse attachments was compared for several procedure variants for both FCAW and SAW on ½ in. steel plates. Measurements of weld toe shape on adjacent pieces of weld indicated that smoother weld toes, as evidenced by larger weld toe radius, were correlated to improved fatigue performance for both processes. Fatigue tests conducted on 59 and 109 ksi yield strength plates did not show an effect of plate strength. Weld procedures designed to provide smooth toes, such as reduced parameter FCAW beads at horizontal weld toes and flat position FCAW at higher heat inputs, were shown to provide fatigue performances near post-weld improved fillets.

Welding residual stress is one of the primary factors responsible for cracking at the access hole interface between the flange and web plate of welded heavy W-shapes. During multi-pass welding, cracks can be found in either the flange plate or the web plate, depending upon welding sequence, joint details and access hole size. In this study, an integrated numerical and experimental investigation was conducted to evaluate the effects of welding parameters and joint geometry on the magnitude and distribution of residual stresses in thick-section butt joints. The results provide guidelines for improved design for welding of heavy W-shapes.

Resistance welding control systems utilizing secondary current feedback receive widespread utilization both in Europe and Japan. However, these types of control systems are only beginning to be used in any extended basis in this country. Currently, two variants of these systems are available; so called “self-teaching” systems, and “learning curve” systems. Either system has been shown to be capable of providing a stable secondary resistance welding current within two cycles. Recent work has indicated, however, that the self-teaching type control systems may be adversely affected by non-optimum set-up conditions, particularly poor fit-up and the introduction of organics (sealers or adhesives) at the faying surface. This work examines the performance of learning curve type constant current control systems under these adverse set-up conditions. Six conditions were selected for study; three degrees of progressively poorer fit-up, with and without an organic sealer.

Many automotive production plants are using various prepulse schedules for resistance spot welding thin gauge galvanized steel. The claimed reasons are that wider current range and longer electrode life are obtainable in comparison to the conventional schedule. However, data to support this are not available. The objective of this program was to determine the effect of prepulsation on spot weldability of galvanized steel. In this work, several prepulse resistance spot welding schedules were evaluated in two full factorial experiments. The effect of the number of prepulse cycles, the prepulse heat level and the effect of cool time were studied in detail. Weldability was evaluated using an electrode life test procedure in which the current range was periodically examined over the life of the electrodes. Generally, the results indicate that prepulsation has a negative effect on the resistance spot weldability of thin gauge galvanized steel.

This study examined the effect of primers containing a conductive pigment on the resistance spot weldability of hot-dip galvanized steel. The pigment used was ferrophos, essentially Di-iron phosphide. Basically, two types of tests were used in this work. Current range tests were used to establish the effect these primers have on the effective ranges of weldability. Limited electrode life tests were used to infer the long term performance of the hot-dip galvanized steels with and without this paint. It was found that the addition of the Ferrophos bearing paints had pronounced effects on weldability. Typically, required current levels were reduced by several thousand amps, and effective current ranges were increased by 50 to 100 percent. During electrode life testing significant reductions were also noted both in the rates of electrode face diameter increase, and the degree of electrode pitting.