Search Results

Vehicle windshields typically include a black decorative pattern around their periphery and other regions. Examination of field failed parts has shown that windshields often break from impacts in these decoration zones; often with the fracture initiating from the decoration material itself. In this work, the effect of different glazing decoration materials on glass strength and laminate impact resistance was evaluated. The decoration materials investigated included traditional inorganic enamel frit, an organic ink, and a new enamel frit that is compatible with glass chemical strengthening. Ring-on-Ring strength tests were conducted and showed that inorganic enamel frit reduces strength of glass by over 50% compared to undecorated glass, while organic inks do not adversely affect strength. Tests of a newly developed decoration frit material, compatible for chemical strengthening processes, showed strength levels that were on par with undecorated, unstrengthened glass.

Examination of field-fractured windshields was conducted for purposes of determining the principle fracture mechanisms experienced in-use. Samples for the study were gathered both in the United States (New York) and in Europe (France) to explore whether the primary causes of failure were similar for the different geographic regions. In total, over two hundred individual field-fractures were obtained and examined for the study. Detailed fracture analysis of the parts was performed, and multiple fracture mechanisms were identified and quantified. It was found that the two most frequently observed failure modes were common for both regions with the most frequent cause (~70%) of fractures being due to sharp contact of the exterior ply, while Hertzian cone cracking of the outer ply was the second leading cause (~20%). Several other modes were also identified. Given that sharp impact fracture was the dominant observed failure mode, a high-speed, sharp impact test method was developed.

The use of lightweight materials to produce automotive glazing is being pursued by vehicle manufacturers in an effort to improve fuel economy. As glazing’s become thinner, reduced rigidity means that the critical flaw size needed to create fracture becomes much smaller due to increased strain under load or impact. This paper documents experiments focused on the impact performance of several alternative thin laminate constructions under consideration for windshield applications (including conventional annealed soda-lime glass as well as laminates utilizing chemically strengthened glass), for the purpose of identifying new and unique failure modes that result from thickness reduction. Regulatory impact tests and experiments that focused on functional performance of laminates were conducted. Given the increased sensitivity to flaw size for thin laminates, controlled surface damage was introduced to parts prior to conducting the functional performance tests.

The objective of this research was to evaluate the effects that higher fluid injection pressures and nozzle geometry have on compound fuel injector nozzle performance. Higher pressures are shown to significantly reduce droplet size, increase the discharge coefficient and reduce the overall size of a nozzle spray. It is also shown that the geometry has a significant effect on nozzle performance, and it can be manipulated to give a desired spray shape.

A computational design of experiments was constructed to analyze two basic nozzle designs. Several geometric features of the nozzles such as cavity height, exit orifice area, turbulence generator area and exit orifice position in addition to the pressure differential across the injector were used in a 2k factorial design study. Performance characteristic which were analyzed in an analysis of variance study included the discharge coefficient. atomization efficiency and predicted spray pattern. The computational design of experiments revealed which of the studied parameters had the greatest influence on a given nozzle performance characteristic. These results were compared to a similar investigation which was later performed experimentally from which similar conclusions were drawn.

The goal of this research was to determine an empirical method of relating the droplet sizes and the spray patterns to the parameters and the geometries of the compound nozzles. Two different types of compound nozzles were studied, the compound silicon micro machined nozzle and the compound metal disk nozzle. Several different orifice geometries of each nozzle type were examined. The injector components upstream of the compound nozzle of two different types of injectors were also studied. A nondimensional characterization of the droplet sizes and the mass flow rates was proposed. The results of this study show that there exists optimum geometric features that will produce sprays with the minimum steady state and dynamic Sauter mean diameter. The spray of a compound nozzle can be characterized by the atomization efficiency and the discharge coefficient. Nozzle testing results show that many flow characteristics are developed in the compound nozzle.

The two stroke direct injected gasoline engine is in part characterized by low temperature exhaust flow, particularly at light loads, due to the fresh air scavenging of the combustion chamber during the exhaust process. This study investigated the possibility of separating the exhaust flow into two regimes: 1) high temperature flow of the combustion products, and 2) low temperature flow from the fresh air scavenging process. Separation of the exhaust flow was accomplished by a mechanical device placed in the exhaust stream. In this way, emissions from the exhaust could be handled by two different catalysts and/or processes, each optimized for different temperature ranges and flow compositions. The first portion of this study involved validation of a computer model, using experimental data from a single cylinder engine with a stationary exhaust port and splitter.

A simple geometry pneumatic atomizer which could be used on internal combustion engine was tested with water as the working fluid. The pneumatic atomizer consists of a cylindrical chamber with an orifice plate at the outlet end. Liquid flows down the chamber walls and onto the nozzle orifice plate as a film. Air flows down the center of the chamber. The interaction of the air and water, which occurs at the orifice, atomizes the water. Large droplets form near the nozzle orifice and break up as they go down stream. Variations in the droplet size occurred in the spray. When geometry and flow rates were varied, changes which decreased the water film thickness or increased the air velocity at the nozzle orifice yielded smaller droplets in the spray. Droplet size data was measured by Malvern Laser Particle Sizer.