Search Results

While standardized laboratory-scale wear tests are available to predict the lubricity of liquid fuels under ambient conditions, the reality is that many injection systems operate at elevated temperatures where fuel vaporization is too excessive to perform the measure satisfactorily. The present paper describes a High Pressure High Frequency Reciprocating Rig (HPHFRR) purposely designed to evaluate fuel lubricity in a pressurized environment at temperatures of up to 300°C. The remaining test parameters are identical to those of the widely standardized High Frequency Reciprocating Rig (HFRR). Results obtained using the HPHFRR indicate that wear rate with poor lubricity fuels is strongly sensitive to both temperature and oxygen partial pressure and may be orders of magnitude higher than at ambient conditions. Surprisingly however, wear rate was found to decrease dramatically at temperatures above 100°C, possibly due to evaporation of dissolved moisture.

The continuing trend toward “cleaner” distillate fuels has prompted concerns about the lubricity characteristics of current and future distillates. Since many U.S. Navy ships utilize seawater-compensated fuel tanks to maintain the ship's trim, the Navy performed a detailed study in order to better understand the relationship between fuel water content and lubricity characteristics. The lubricity test methods, modified for this study, were ASTM D 6078 (SLBOCLE), D 6079 (HFRR), and D 5001 (BOCLE). The results indicated that, with few exceptions, there was generally no evidence of a correlation between the water content of the fuels and the corresponding lubricity measurements as determined by the laboratory tests.

A cooperative research and development program was organized to determine the critical particle size of abrasive debris that will cause significant wear in rotary injection fuel pumps. Various double-cut test dusts ranging from 0-5 to 10-20 μm were evaluated to determine which caused the pumps to fail. With the exception of the 0-5-μm test dust, all other test dust ranges evaluated caused failure in the rotary injection pumps. After preliminary testing, it was agreed that the 4-8-μm test dust would be used for further testing. Analysis revealed that the critical particle size causing significant wear is 6-7 μm. This is a smaller abrasive particle size than reported in previously published literature. A rotary injection pump evaluation methodology was developed. During actual operation, the fuel injection process creates a shock wave that propagates back up the fuel line to the fuel filter.

The United States and Europe are mandating increasingly severe diesel fuel specifications, particularly with respect to sulfur content, and in some areas, aromatics content. This trend is directed towards reducing vehicle exhaust emissions and is generally beneficial to fuel quality, ignition ratings, and stability. However, laboratory studies, as well as recent field experience in Sweden and the United States, indicate a possible reduction in the ability of fuels to lubricate sliding components within the fuel injection system. These factors, combined with the trend toward increasing injection pressure in modern engine design, are likely to result in reduced durability and failure of the equipment to meet long-term emissions compliance. The U.S. Army Belvoir Fuels and Lubricants Research Facility (BFLRF) located at Southwest Research Institute (SwRI) developed an accelerated wear test that predicts the effects of fuel lubricity on injection system durability.