The paper describes the fabrication and testing of thin sheet metal uniaxial fatigue specimens that have been laminated to prevent buckling. When hot or cold rolled metal thicknesses are below 5 mm, the usual fatigue specimens, having a uniform gauge length of 7.5 mm or more, buckle in the short life region (∼10000 cycles) of strain-life testing. For thinner materials, non-standard specimen designs or anti-buckling guides have been used, but each of these solutions requires additional instrumentation. The results presented in this paper show that laminating multiple sheets of material together to increase the specimen's effective thickness raises the strain level for the onset of buckling of the standard uniaxial specimen. Constant and variable amplitude fatigue tests extending into the high-strain short-life region were performed. Fatigue life data for multiple layer specimens were in good agreement with those obtained for single layer specimens.

This paper presents a model for fatigue life prediction for metals subjected to variable amplitude service loading. The model, which is based on crack growth and crack closure mechanisms for short fatigue cracks, incorporates a strain-based damage parameter, EΔε*, determined from the effective or open part of a strain cycle along with a fatigue resistance curve that takes the form: EΔε* = A(Nf)b, where E is the elastic modulus, Nf is the number of cycles to failure, and A and b are experimentally determined material constants. The fatigue resistance curve is generated for a SAE 1045 steel and the model is used successfully to predict the fatigue lives of smooth axial specimens subjected to two variable amplitude strain histories. The model is also used to predict the magnitude of non-damaging cycles that can be omitted from the strain histories to accelerate fatigue testing.