Standard

Wrought Nickel and Nickel-Related Alloys

2018-02-15
CURRENT
J470_201802
This Report presents general information on over 50 alloys in which nickel either predominates or is a significant alloying element. It covers primarily wrought materials, and is not necessarily all inclusive. Values given are in most cases average or nominal, and if more precise values are required the producer(s) should be contacted. This report does not cover the so-called "superalloys," or the iron base stainless steels. Refer to SAE J467, Special Purpose Alloys, and SAE J405, Chemical Compositions of SAE Wrought Stainless Steels, respectively, for data on these alloys.
Standard

Automotive Compacted Graphite Iron Castings

2018-02-15
CURRENT
J1887_201802
This SAE Standard covers the mechanical and physical requirements for Compacted Graphite Iron (CGI) castings used in automotive and allied industries. Requirements in this document include: a Tensile Strength b Yield Strength c Elongation d Graphite Morphology
Standard

Wrought Copper and Copper Alloys

2018-01-10
CURRENT
J463_201801
This standard1 describes the chemical, mechanical, and dimensional requirements for a wide range of wrought copper and copper alloys used in the automotive and related industries.
Standard

Engine Poppet Valve Information Report

2018-01-10
CURRENT
J775_201801
This specification supplies engineers and designers with: a Poppet valve nomenclature b Poppet valve alloy designations c Chemical compositions of poppet valve alloys d A guide to valve alloy metallurgy and heat treatments e General information on properties of valve alloys f A guide to the application of valve alloys g A description of valve design and construction, and their relation to valve alloy selection h Valve gear design considerations that affect valves
Standard

Methods of Measuring Decarburization

2018-01-10
CURRENT
J419_201801
This report covers the recommended practice for the evaluation and measurement of decarburization in ferrous material. Included are definitions of types with charts and micrographs and methods most commonly used for the measurement of decarburization.
Standard

Automotive Steel Castings

2018-01-10
CURRENT
J435_201801
This SAE Standard defines the specifications for steel castings used in the automotive and allied industries.
Standard

Leakage Testing

2018-01-10
CURRENT
J1267_201801
This information report provides basic information on leakage testing, as applied to nondestructive testing, and affords the user sufficient information so that he may decide whether leakage testing methods apply to his particular need. Detailed references are listed in Section 2.
Standard

Welding, Brazing, and Soldering - Materials and Practices

2018-01-09
CURRENT
J1147_201801
The Joint AWS/SAE Committee on Automotive Welding was organized on January 16, 1974, for the primary purpose of facilitating the development and publication of various documents related to the selection, specification, testing, and use of welding materials and practices, particularly for the automotive and related industries. A secondary purpose is the dissemination of technical information.
Standard

Automotive Austempered Ductile (Nodular) Iron Castings (ADI)

2018-01-09
CURRENT
J2477_201801
This SAE Standard covers the mechanical and physical property requirements for Austempered Ductile Iron (ADI) castings used in automotive and allied industries. Specifically covered are: a Hardness b Tensile Strength c Yield Strength d Elongation e Modulus of Elasticity f Impact Energy g Microstructure In this document SI units are primary and in-lb units are derived. Appendix A provides general information and related resources on the microstructural, chemical and heat treatment requirements to meet the mechanical properties needed for ADI in particular service conditions and applications.
Standard

Automotive Gray Iron Castings

2018-01-09
CURRENT
J431_201801
This SAE Standard covers the hardness, tensile strength, and microstructure and special requirements of gray iron sand molded castings used in the automotive and allied industries. Specific requirements are provided for hardness of castings. Test bar tensile strength/Brinell hardness (t/h) ratio requirements are provided to establish a consistent tensile strength-hardness relationship for each grade to facilitate prediction and control of tensile strength in castings. Provision is made for specification of special additional requirements of gray iron automotive castings where needed for particular applications and service conditions. NOTE—This document was revised in 1993 to provide grade specific t/h control. In 1999 the document was revised to make SI metric units primary.
Standard

Chemical Compositions of SAE Wrought Stainless Steels

2018-01-09
CURRENT
J405_201801
The chemical composition of standard types of wrought stainless steels are listed in ASTM Specification A240. The UNS 20000 series designates nickel-chromium manganese, corrosion resistant types that are nonhardenable by thermal treatment. The UNS 30000 series are nickel-chromium, corrosion resistant steels, nonhardenable by thermal treatment. The UNS 40000 however, includes both a hardenable, martensitic chromium steel and nonhardenable, ferritic, chromium steel. Reference to SAE J412 is suggested for general information and usage of these types of materials. See Table 1.
Standard

Liquid Penetrant Test Methods

2018-01-09
CURRENT
J426_201801
The scope of this SAE Information Report is to supply the user with sufficient information so that he may decide whether liquid penetrant test methods apply to his particular inspection problem. Detailed technical information can be obtained by referring to Section 2.
Standard

Tool and Die Steels

2018-01-09
CURRENT
J438_201801
This standard covers the identification, classification, and chemical composition of tool and die steels for use by engineers, metallurgists, tool designers, tool room supervisors, heat treaters, and tool makers.
Standard

Zinc Die Casting Alloys

2017-12-20
CURRENT
J469_201712
Because of the drastic chilling involved in die casting and the fact that the solid solubilities of both aluminum and copper in zinc change with temperature, these alloys are subject to some aging changes, one of which is a dimensional change. Both of the alloys undergo a slight shrinkage after casting, which at room temperature is about two-thirds complete in five weeks. It is possible to accelerate this shrinkage by a stabilizing anneal, after which no further changes occur. The recommended stabilizing anneal is 3 to 6 h at 100 °C (212 °F), or 5 to 10 h at 85 °C (185 °F), or 10 to 20 h at 70 °C (158 °F). The time in each case is measured from the time at which the castings reach the annealing temperature. The parts may be air cooled after annealing. Such a treatment will cause a shrinkage (0.0004 in per in) of about two-thirds of the total, and the remaining shrinkage will occur at room temperature during the subsequent few weeks.
Standard

Automotive Compacted Graphite Iron Castings

2007-12-17
HISTORICAL
J1887_200712
This SAE Standard covers the mechanical and physical requirements for Compacted Graphite Iron (CGI) castings used in automotive and allied industries. Requirements in this document include: a Tensile Strength b Yield Strength c Elongation d Graphite Morphology
Standard

Automotive Steel Castings

2007-12-17
HISTORICAL
J435_200712
This SAE Standard defines the specifications for steel castings used in the automotive and allied industries.
Standard

Engine Poppet Valve Information Report

2004-11-02
HISTORICAL
J775_200411
This specification supplies engineers and designers with: a Poppet valve nomenclature b Poppet valve alloy designations c Chemical compositions of poppet valve alloys d A guide to valve alloy metallurgy and heat treatments e General information on properties of valve alloys f A guide to the application of valve alloys g A description of valve design and construction, and their relation to valve alloy selection h Valve gear design considerations that affect valves