A new nitriding technology and material technology have been developed to increase the strength of microalloyed gears. The developed nitriding technology makes it possible to freely select the phase composition of the nitride compound layer by controlling the treatment atmosphere. The treatment environment is controlled to exclude sources of supply of [C], and H2 is applied as the carrier gas. This has made it possible to control the forward reaction that decomposes NH3, helping to enable the stable precipitation of γ′-phase, which offers excellent peeling resistance. A material optimized for the new nitriding technology was also developed. The new material is a low-carbon alloy steel that makes it possible to minimize the difference in hardness between the compound layer and the substrate directly below it, and is resistant to decline in internal hardness due to aging precipitation in the temperature range used in the nitriding treatment.

In this research, a new wire material made using surface-reforming heat treatment was developed in order to enhance the corrosion fatigue resistance of suspension springs. The aim of surface reforming is to improve hydrogen embrittlement characteristics through grain refinement and to improve crack propagation resistance by partial softening of hardness. The grain refinement method used an α'→γ reversed transformation by rapid short-term heating in repeated induction heating and quenching (R-IHQ) to refine the crystal grain size of SAE 9254 steel spring wire to 4 μm or less. In order to simultaneously improve the fatigue crack propagation characteristics, the possibility of reducing the hardness immediately below the spring surface layer was also examined. By applying contour hardening in the second IHQ cycle, a heat affected zone (HAZ) is obtained immediately below the surface.

A new motor has been developed that combines the goals of greater compactness, increased power and a quiet drive. This motor is an interior permanent magnet synchronous motor (IPM motor) that combines an interior permanent magnet rotor and a stator with concentrated windings. In addition, development of the motor focused on the slot combination, the shape of the magnetic circuits and the control method all designed to reduce motor noise and vibration. An 8-pole rotor, 12-slot stator combination was employed, and a gradually enlarged air gap configuration was used in the magnetic circuits. The gradually enlarged air gap brings the centers of the rotor and the stator out of alignment, changing the curvature, and continually changing the amount of air gap as the rotor rotates. The use of the gradually enlarged air gap brings torque degradation to a minimum, and significantly reduces torque fluctuation and iron loss of rotor and stator.

A sports car exhibits many challenges from an aerodynamic point of view: drag that limits top speed, lift - or down force - and balance that affects handling, brake cooling and insuring that the heat exchangers have enough air flowing through them under several vehicle speeds and ambient conditions. All of which must be balanced with a sports car styling and esthetic. Since this sports car applies two electric motors to drive front axle and a high-rev V6 turbo charged engine in series with a 9-speed double-clutch transmission and one electric motor to drive rear axle, additional cooling was required, yielding a total of ten air cooled-heat exchangers. It is also a challenge to introduce cooling air into the rear engine room to protect the car under severe thermal conditions. This paper focuses on the cooling and heat resistance concept.

When a vehicle is cruising, unpleasant noise in the 4 to 5 KHz high-frequency band can be heard at the center of all seats in the vehicle cabin. In order to specify the source of this noise, the correlation between the noise and airborne noise from the outer surface of the transmission was determined, and transfer path analysis was conducted for the interior of the transmission. The results indicated that the source of the noise was the 0th-order breathing mode specific to the drive motor. To make it possible to predict this at the desk, a vibrational analysis method was proposed for drive motors made up of laminated electrical steel sheets and segment-type coils. Material properties data for the electrical steel sheets and coils was employed in the drive motor vibrational analysis model without change. The shapes of the laminated electrical steel sheets and coils were also accurately modeled.

Conventionally, the Ni-based superalloys NCF3015 (30Ni-15Cr) and the high nickel content NCF440 (70Ni-19Cr) (with its outstanding wear resistance and corrosion resistance), have been used as engine exhaust valve materials. In recent years, automobile exhaust gases have become hotter because of exhaust gas regulations and enhanced fuel consumption efficiency. Resource conservation and cost reductions also factor into global environmental challenges. To meet these requirements, NCF5015 (50Ni-15Cr), a new resource-conserving, low-cost Ni-based heat-resistant alloy with similar high-temperature strength and wear resistance as NCF440, has been developed. NCF5015's ability to simultaneously provide wear resistance, corrosion resistance and strength when NCF5015 is used with diesel engines was verified and the material was then used in exhaust valves.

Just as CO2 reduction is required of four wheeled vehicles for environmental protection, similar environmental concerns drive the development of motorcycle oil technology. Zinc dialkyldithiophosphate (Zn-DTP) type additives are widely used for engine oil formulations. However, phosphorus compounds are environmental load materials. The reduction of the quantity of phosphorus compounds in engine oils is required to reduce poisoning of three-way catalysts used to purify exhaust gases from internal combustion engines. Mr. Ito and his co-authors1) reported that they developed a sulfur-based additive as a substitute for Zn-DTP. Their non-phosphorus engine oil formulation for four-wheeled vehicles with a sulfur-based additive was examined to evaluate its anti-wear performance using the following test methods:JASO M328 for gasoline engines (KA24E) and JASO M354 for Diesel engine (4D34T4).

Power generation systems employed in small gas engine cogeneration were examined to compare losses in the converter, which converts three-phase alternator power to direct current (DC) voltage, and losses in the inverter, which converts power to high-quality alternating current (AC) voltage that can be connected into electric utility power lines. It is a characteristic of alternators that their efficiency and output voltage decline in the heavy load range. It was found, therefore, that step-down methods using thyristors operate in a low-efficiency range in order to provide a satisfactory supply of the targeted DC output voltage. Use of switching regulator methods, on the other hand, can generate the target voltage by regulating a switching device after first storing the alternator output in a choke coil. It was found, therefore, that these use the high-efficiency range of the alternator. The converter was found to have a resulting loss decrease of 19.4 W.

SUS301-EH is widely used as a material for exhaust system gaskets, however, at temperatures in excess of 400°C, it can not be used as gas-seal ability of the material declines due to its reduced hardness. The following methods were found to be effective in controlling the softening of stainless steel at high temperatures: (1) The addition of a nitrogen component; (2) Stabilization of the austenite structure; (3) The addition of a molybdenum component. The addition of 0.5% nitrogen to austenitic stainless steel containing molybdenum has enabled the speed of softening at high temperatures to be significantly reduced, due to strain aging by solid nitrogen below 600°C and the combined effects of precipitation hardening and control of growth of recrystallized grains through the precipitation of fine Cr2N on the dislocations and the grain boundary above 600°C.

When the alkali metal-supported catalyst was treated at 830°C, the NOx conversion decreased because the alkali metals in the catalyst layer gradually moved to the cordierite honeycomb layer and reacted with the cordierite elements. This phenomena decreased to be added the basic metal oxide (α) in the catalyst layer. The improved catalyst with α 2 showed higher performance than the conventional catalyst in the model gas test. Moreover, the emission values of NOx, HC, and CO were 50% or less than Japanese domestic regulation values even after 830°C×60h heat treatment in a vehicle test.

1 Many different bolts are employed in automobiles for different purposes and uses, and their strength generally ranges from 700 N/mm2 to 1200 N/mm2. Automobiles face the issue of making improvements in fuel economy as an environmental measure, and there is consequently a requirement to lighten component parts. The creationof higher-strength bolts is an important factor in achieving lighter weight. Increasing the strength, however, can also bring about an increased incidence of delayed fracture, and the conventional solution used to require the application of special steels such as expensive maraging steel. The present development addressed this issue by focusing on high carbon steel rod, which had been considered less susceptible to delayed fracture, although heading was also considered to be difficult. Heading techniques were therefore devised that made it possible not only to form bolts from this material, but also to provide satisfactory strength.

In the consideration of safety to health, many countries have recently been enforsing regulations on the use of asbestos. To keep abreast of this trend, it has become necessary to replace the gasket materials currently used in the cases and the covers of motorcycle engines with non-asbestos materials. The gaskets used in motorcycles are subjected to extremely severe sealing loads and temperature in the small and high performance engines. They are required to have excellent sealability and creep relaxation characteristics at high temperature. Under such conditions, it is extremely difficult to substitute non-asbestos materials for asbestos which has superb material characteristics such as higher heat resistance and greater aspect ratio (length of fiber/dia.).

An attempt was made to apply the index U* in detail analysis of load paths in structural joints under static load, using as examples coupling structures of two joined frames with hat-shaped sections, and T-beam joint structures each including spot welds, both of which are widely used in automotive body structures. U* is a load path analysis index that expresses the strength of connection between load points and arbitrary points on a structure. It was possible to identify areas making up load paths by means of the magnitude of U* values, and to clarify the areas that should be coupled in order to achieve effective load transfer to contiguous members. In addition, because it is possible to determine whether or not each section of a structure possesses the potential for load transfer using U* analysis, the research also demonstrated that U* could be used as an indicator of joint structures providing efficient load transfer.

Honda’s purpose is to realize the joy and freedom of mobility and a sustainable society in which people can enjoy life. As such, three series of environmental vehicles-FCVs, BEVs, and PHEVs-have been developed so that users in communities around the world can select the ones best suited to their local energy circumstances and individual lifestyles. This paper discusses a structure that enhances both the motive power performance and quietness of a newly developed FCV/BEV traction motor. To enhance motive power performance, the research focused on the stator lamination technique. As for methods of affixing the stator’s layers, the practice with previous models has been adhesion lamination, using electric steel sheets that come pre-made with adhesive layers. Having adhesive layers, however, lowers the ratio (space factor) of steel sheet layers. The new motor uses electric steel sheets without an adhesive layer in order to enhance motive power performance.

There are several all-aluminum cylinder blocks. A typical example is a mono-block cylinder of alusil alloy produced by low pressure die casting. This material's resistance to abrasion and seizure, however, is not satisfactory for motorcycle; in addition, long processing time is another disadvantage. To cope with these problems, the authors developed a light and highly productive all-aluminum cylinder block with a cast-in liner through die casting. The liner is made from powder metallurgy composite (PMC) with 3 to 5 % alumina and 0.5 to 3 % of graphite additives. The PMC reconciles abrasion resistance and machinability. The hardness deterioration of the composite due to the heat at die casting is avoided by using heat-resistant rapidly-solidified powders, made from an aluminum-silecon-iron alloy, for the matrix.

There are strong demands for reduced production costs of ordinary bolts, of which a large number are used throughout automobiles. In addition, there are continued demands for higher performance and lower weight in automobiles. For this reason, there is an increasing trend to develop steel for high strength bolts or to adopt the plastic region tightening method. At present, the principal materials used in high strength bolts of class 10.9 are medium carbon alloy steel. When a low carbon boron steel bolt is used as a class 10.9 bolt under high stress, delayed fracture may occur, so that these cannot always be used for the body and chassis applications. The authors have developed a new low carbon boron steel with increased delayed fracture strength on the same order as that of JIS-SCM435 (equivalent to SAE4135) medium carbon alloy steel. Attention was focused principally on decreasing the amounts of phosphorus and sulfur in the steel.

The use of low-density materials in body panels is increasing as a measure to reduce the weight of the vehicle body. Honda has developed an aluminum/steel sheet hybrid door that is more effective in reducing weight than an all-aluminum door. Because aluminum was used in the door skin, bimetallic corrosion at the connection between the aluminum and the steel sheets represented an issue. It was possible that the difference in the electrical potential of the two metals might promote corrosion at the connection between the aluminum door skin and the steel sheet door panel, in particular at the lower edge of the door, where rainwater and other moisture tend to accumulate, with the result that the appeal of the exterior of the door might decline.

Development is proceeding on catalysts which separate the NOx in lean exhaust gas by adsorption and then reduce the adsorbed NOx in combustion exhaust gas with the stoichiometric or a slightly richer air fuel ratio, as well as exhaust conversion technology that uses these catalysts. Amidst this research it has been found that catalysts containing mixed metal oxides exhibit superior NOx adsorption performance, so the authors prepared a mixed metal oxide catalyst by adding precious metals and promoters, etc. The resulting catalyst has high heat resistance and also offers excellent SOx durability. These properties were presumed to be due to an adsorbent including the mixed metal oxide, and the relation between the physical properties and NOx conversion properties of the catalyst was investigated.

The purpose of our research is to omit normalizing after hot forging in nitrocarburized crankshafts. Based on fundamental studies about the influence of chemical composition on as-forged and nitrocarburized properties, the authors have developed a new nitrocarburizing steel composed of 0.3% carbon, 0.8% manganese, and 0.02% nitrogen. The newly designed crankshafts for compact cars using the steel can be in use without the normalizing and have equivalent properties to conventional crankshafts, though the treatment is an indispensable process for conventional ones.

Initiation and propagation of ductile fractures in crashed automotive components made from high strength steels are investigated in order to understand the mechanism of fracture propagation. Fracture of these components is often prone to occur at the sheet edge in a strain concentration zone under crash deformation. The fracture then extends intricately to the inside of the structure under the influence of the local stress and strain field. In this study, a simple tensile test and a 3-point bending test of high strength steels with tensile strengths of 590 MPa and 1180 MPa are carried out. In the tensile test, a coupon having a hole and a notch is deformed in a uniaxial condition. The effect of the notch type on the strain concentration and fracture behavior are investigated by using a digital imaging strain measurement system.