Search Results

The newly developed sheet steel lightly coated with an organic composite is as follows. Zn-Ni alloy plated sheet steel with a coating weight of 30 g/m2 and average Ni concentration of 11.5 ∼12.0 % is chromated through electrolysis. The coating weight of chromate film is 50 ∼90 mg/m2 in Cr. Furthermore, emulsified olefin-acrylic acid copolymer resin mixed with colloidal silica of particle size 7 ∼8 nm applied to a thickness of 1.0 ∼1.8 μm. Olefin-acrylic acid copolymer resin and colloidal silica are mixed at the rate of 100 and 30 (parts by weight). It maintains excellent corrosion resistance even after forming, C-ED paint corrosion resistance and paint adhesion. Furthermore, it has excellent perforation resistance. The product has excellent weldability and is well suited to continuous forming, too.

As a demand for vehicles of higher functionality grows, automakers and material suppliers are devoting increasing efforts to develop technologies for greater safety, lighter weight, higher corrosion resistance, and enhanced quietness. The resin-sandwiched vibration damping steel sheet (VDSS), developed as a highly functional material for reducing vehicle vibration and noise, has been used for oil pans1) and compartment partitions2). First applied for a structural dash panel of the new Mazda 929, a Zn-Ni electroplated VDSS which allows direct electric welding has contributed to greater weight reduction as well as improved quietness.

In order to clarify the effect of design and materials of the hem as well as the climatic factors on perforation corrosion of the automobile doors, field car and laboratory investigation has been carried out Field car investigation revealed that corrosion of the hem can be minimized by using two side galvanized steel plus adhesives. The ratio of wet/dry environment was evaluated in laboratory on hemmed sample, and it was found that the design of the hem in conjunction with the various wet/dry ratio affected the corrosion rate differently.

A metal support for use in an automotive catalyst is exposed to the severe heat cycle brought about by the intermittent flow of a high temperature exhaust gas. Accordingly, the metal support must have high beat resistance(ex. oxidation resistance) and a rigid structure. Therefore, 20% chromium-5% aluminum ferritic stainless steel(containing small quantities of rare earth metals and titanium) is used as a highly beat resistant honeycomb foil in addition to a highly mechanical durable brazing honeycomb structure. This study examined the durability of a metal honeycomb installed in a gasoline engine. Both an engine bench durability test of a manifold converter type metal support which is connected directly to the exhaust manifold of the gasoline engine and a vehicle durability test of an under the floor type metal support were carried out to evaluate oxidation damage of the metal honeycomb as well as its mechanical durability.

To give the wear-resistance to titanium intake valves by simple oxidation treatment, oxidation condition and microstructure of Ti-6Al-4V bars were studied. The wear test using a valve simulator shows that the wear of the face oxidized at 820°C for 1 and 4h in air is superior to that of ferrous valves. The best micro-structure of Ti-6Al-4V bar is an acicular structure with the prior β grain size of 30 to 60 μ m in average, which prevents distortion during the oxidation treatment and has excellent mechanical properties.

We have taken notice of Zn-Fe alloy electroplating with an eye to developing new corrosion-resistant steel sheets for automotive use with both cosmetic corrosion resistance and perforating corrosion resistance, and as a result of investigations into its paintability and corrosion resistance over the whole range of its compositions, we have come to a conclusion that steel sheets with two-layer Zn-Fe alloy electroplating that consists of a thin upper layer with a 75 to 85% Fe content and a lower layer with a 10 to 20% Fe content is the best choice.

The Strategic Alliance for Steel Fuel Tanks (SASFT), an international group of steel producers and manufacturing companies, recently completed a major corrosion study of various steel ‘systems’ for automobile fuel tanks. The ten steel systems included low carbon steels (either pre-painted or post-painted with protective coatings) and stainless steels. The 2-year corrosion test program included testing in salt solutions to simulate road environments for the exterior of a fuel tank. Special test specimens were designed to represent a manufactured tank. The external tests used were the Neutral Salt Spray test (ASTM B117) with exposures up to 2000 hours and the Cyclic Corrosion test (SAE J2334) with exposures up to 120 and 160 cycles to represent vehicle lives of 15 years and 20 years, respectively. Additionally, the resistance to an aggressive ethanol-containing fuel (internal tank corrosion) was assessed by using uniquely designed drawn cups of the various steel systems.