The influence of engine oil viscosity on the wear of piston rings and cam faces has been investigated by fired engine tests using a radioisotope (RI) tracer technique. High-temperature and high-shear-rate (HTHS; 150°C, 1O6 s-1) viscosities of the experimental oils prepared are 2.2, 2.4, 2.6 and 3.1 mPa•s. At an oil temperature of 90°C the wear of piston rings and cam faces did not increase, even if the HTHS viscosity was lowered down to 2.2 mPa•s. However, both piston rings and cam faces exhibited an increase in wear below 2.4 mPa•s at 130°C. It was also recognized that valve train wear did not significantly increase with reducing viscosity in the motored engine tests at a temperature of 50°C. From these test results, it was suggested that the oil with the HTHS viscosity of 2.6 mPa•s sufficiently demonstrates the antiwear performance equivalent to that with around 3.0 mPa•s for application to piston rings and cam faces.

The purposes of this paper are to develop a new laboratory oxidation stability testing method and to clarify factors relative to the viscosity increase of engine oil. Polymerized products, obtained from the oil after a JASO M333-93 engine test, were found to consist mainly of carboxyl, nitrate and nitro compounds and to increase the oil viscosity. A good similarity between the JASO M333-93 test and the laboratory simulation test was found for the polymerized products. The products were obtained not by heating oil only in air but by heating oil while supplying a synthetic blowby gas consisting of fuel pyrolysis products, NO, SO2 and air. The laboratory test has also revealed that the viscosity increase depends on oil quality, organic Fe content and hydrocarbon composition in the fuel. Moreover, it has been found that blowby gas and organic Fe accelerate ZnDTP consumption and that aromatics concentration in the fuel correlates with the viscosity increase of oil.