Transition materials consisting of steel clad aluminum have been used to join aluminum and steel. This technique allows joining by resistance spot welding since the clad transition material allows the actual transition from one metal to the other to occur at the clad bond interface. Welding studies show that in the recommended range of weld parameters, high strength joints are produced. A wide range of corrosion tests have been used to determine the durability of these joints in automotive environments. Results show that the use of transition material in joining aluminum to steel or EG steel eliminates galvanic corrosion.

Transition materials which are used to join dissimilar metals such as steel and aluminum on automobiles are described in this paper. The problems associated with conventional methods of joining these two metals include galvanic corrosion, brittle welds, reduced mechanical properties and reduced design flexibility. These problems are solved through the use of clad transition materials at the joints. Transition materials are fabricated by roll bonding dissimilar metals to form the clad materials and subsequently forming the materials to the desired configurations. The clad material allows the actual transition from one metal to the other to occur at the clad bond interface and thus only similar metal joints exist in the assembly. Welding studies describe the high strength and ductility of steel to aluminum joints through the use of steel clad aluminum transition materials.

Galvanic corrosion and mechanical properties are major design considerations for bimetallic assemblies. Galvanic corrosion can lead to rapid degradation while welding of dissimilar metals such as steel and aluminum can lead to reduced structural stability. This paper describes a new concept in joining dissimilar metals involving the use of transition materials. The clad transition materials is composed of the dissimilar metals to be joined and effectively reduces the corrosion and mechanical problems associated with the system. Results of galvanic corrosion field tests and welding studies for transition materials are presented and several examples of automotive applications are cited.

1006 steel clad aluminum has been used as a transition material to directly spot weld steel to aluminum. Advantages of the clad metal transition include the ability to spot weld with existing equipment and reduction of dissimilar metal crevice corrosion at the steel-aluminum interface. Sheet steel between 0.8mm and 2.0mm has been spot welded to aluminum between 0.8mm and 3.0mm in a variety of combinations with the transition material. This paper contains specific spot welding parameters for a variety of joints containing steel and aluminum at thicknesses normally encountered in body applications. The mechanism of weld nugget formation for aluminum-transition-steel joints is evaluated. Weld lobes established according to SAE and Aluminum Association guidelines are presented. The effect of electrode design on joint strength and heat balance are discussed.