Search Results

The compatibility of plastic materials used in gasoline storage and dispensing applications was determined for test fuels representing neat gasoline (Fuel C), and blends containing 25% ethanol (CE25a), 16% isobutanol (CiBu16a), and 24% isobutanol (CiBu24a). A solubility analysis was also performed and compared to the volume swell results obtained from the test fuel exposures. The plastic specimens were exposed to each test fuel for16 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured for volume and hardness. Dynamic mechanical analysis (DMA), which measures the storage modulus as a function of temperature, was also performed on the dried specimens to determine the temperature associated with the onset of the glass-to-rubber transition (Tg). For many of the plastic materials, the solubility analysis was able to predict the relative volume swell for each test fuel.

The compatibility of elastomer materials used in fuel storage and dispensing applications was determined for an off-highway diesel fuel and a blend containing 20% bio-oil (Bio20) derived from a fast pyrolysis process. (This fuel blend is not to be confused with B20, which is a blend of diesel fuel with 20% biodiesel.) The elastomer types evaluated in this study included fluorocarbon, fluorosilicone, acrylonitrile rubber (NBR), styrene butadiene rubber (SBR), polyurethane, neoprene, and silicone. All of these elastomer types are used in sealing applications, but some, like the nitrile rubbers are also common hose materials. The elastomer specimens were exposed to the two fuel types for 4 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured. A solubility analysis was performed to better understand the performance of plastic materials in fuel blends composed of bio-oil and diesel.

The compatibility of plastic materials used in fuel storage and dispensing applications was determined for an off-highway diesel fuel and a blend containing 20% bio-oil (Bio20) derived from a fast pyrolysis process. Bio20 is not to be confused with B20, which is a diesel blend containing 20% biodiesel. The feedstock, processing, and chemistry of biodiesel are markedly different from bio-oil. Plastic materials included those identified for use as seals, coatings, piping and fiberglass resins, but many are also used in vehicle fueling systems. The plastic specimens were exposed to the two fuel types for 16 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 65 hours at 60°C and then remeasured to determine extent of property change. A solubility analysis was performed to better understand the performance of plastic materials in fuel blends composed of bio-oil and diesel.

The compatibility of elastomeric materials used in fuel storage and dispensing applications was determined for test fuels representing neat gasoline and gasoline blends containing 10 and 17 vol.% ethanol, and 16 and 24 vol.% isobutanol. The actual test fuel chemistries were based on the aggressive formulations described in SAE J1681 for oxygenated gasoline. Elastomer specimens of fluorocarbon, fluorosilicone, acrylonitrile rubber (NBR), polyurethane, neoprene, styrene butadiene rubber (SBR) and silicone were exposed to the test fuels for 4 weeks at 60°C. After measuring the wetted volume and hardness, the specimens were dried for 20 hours at 60°C and then remeasured for volume and hardness. Dynamic mechanical analysis (DMA) was also performed to determine the glass transition temperature (Tg). Comparison to the original values showed that all elastomer materials experienced volume expansion and softening when wetted by the test fuels.

The compatibility of key fuel system infrastructure elastomers with promising bio-blendstock fuel candidates was examined using Hansen solubility analysis. Thirty-four candidate fuels were evaluated in this study including multiple alcohols, esters, ethers, ketones, alkenes and one alkane. These compounds were evaluated as neat molecules and as blends with the gasoline surrogate, dodecane and a mix of dodecane and 10% ethanol (E10D). The elastomer materials were fluorocarbon, acrylonitrile butadiene rubber (NBR), styrene butadiene (SBR), neoprene, polyurethane and silicone. These materials have been rigorously studied with other fuel types, and their measured volume change results were found to correspond well with their predicted solubility levels. The alcohols showed probable compatibility with fluorocarbon and polyurethane, but are not likely to be compatible at low blend levels with NBR and SBR.

The compatibility of notable infrastructure elastomers and plastics with DME and its blends with diesel fuel were examined using solubility analysis. The elastomer materials were fluorocarbon, acrylonitrile butadiene rubber (NBR), styrene butadiene (SBR), neoprene, polyurethane and silicone. Plastic materials included polyphenylene sulfide (PPS), polyethylene terephthalate (PET), polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), polyoxymethylene (POM), polybutylene terephthalate (PBT), polypropylene (PP), high density polyethylene (HDPE), along with several nylon grades and thermosetting resins. These materials have been rigorously studied with other fuel types, and their volume change results were found to correspond well with their predicted solubility levels. A Hansen solubility analysis was performed for each material with DME, diesel, and blends of both fuel components.