SAE 8620 and other steels are typically used in the carburized condition for powertrain applications in the automotive industry, i.e., differential ring gears, camshafts, and transmission gears. Although current recommended carburizing practice involves normalizing the steel prior to carburizing, elimination of this normalizing treatment could lead to significant cost reductions. This research examines whether the normalizing process prior to carburizing could be eliminated without negatively affecting part performance. This study focused on the effects of the initial microstructure on the residual stress, retained austenite, and effective case depths of carburized SAE 8620 and PS-18 steels.

The focus of this study was to determine the residual stress and retained austenite profiles for carbonitrided and nitrocarburized SAE 1010 plain carbon steel and to relate these profiles to one another and to the distortion resulting from heat treatment. Navy C-ring specimens were used for the purpose of this study and X-ray diffraction techniques were used to measure both residual stress and retained austenite. The findings from this research are then applied to a manufacturing application involving the surface hardening of a thin shelled, plain carbon steel automotive component.

Springback compensation studies on a few selected auto panels from the hot selling Chrysler 300C are presented with details. LS-DYNA® is used to predict the springback behavior and to perform the iterative compensation optimization. Details of simulation parameters using LS-DYNA® to improve the prediction accuracy are discussed. An iterative compensation algorithm is also discussed with details. Four compensation examples with simulation predictions and actual panel measurement results are included to demonstrate the effectiveness of LS-DYNA® predictions. An aluminum hood inner and a high strength steel roof bow are compensated, constructed and machined based on simulation predictions. The measurements on actual tryout panels are then compared with simulation predictions and good correlations were achieved. Iterative compensation studies are also done on the aluminum hood inner and the aluminum deck lid inner to demonstrate the effectiveness of LS-DYNA® compensation algorithm.

Nitrocarburizing is an economical surface hardening process and is proposed as an alternative heat treatment method to carbonitriding. The focus of this study is to compare the size and shape distortion and residual stresses resulting from the ferritic nitrocarburizing and gas carbonitriding processes for SAE 1010 plain carbon steel. Gas, ion and vacuum nitrocarburizing processes utilizing different heat treatment temperatures and times were performed to compare the different ferritic nitrocarburizing processes. Navy C-Ring specimens and prototype stamped parts were used to evaluate size and shape distortion. X-ray diffraction techniques were used to determine the residual stresses in the specimens. Overall, the test results indicate that the nitrocarburizing process gives rise to smaller dimensional changes than carbonitriding, and that the size and shape distortion can be considerably reduced by applying appropriate ferritic nitrocarburizing procedures.