Technical Paper

Improvement of Heat Resistance for Lean NOx Catalyst

2004-03-08
2004-01-1495
When the alkali metal-supported catalyst was treated at 830°C, the NOx conversion decreased because the alkali metals in the catalyst layer gradually moved to the cordierite honeycomb layer and reacted with the cordierite elements. This phenomena decreased to be added the basic metal oxide (α) in the catalyst layer. The improved catalyst with α 2 showed higher performance than the conventional catalyst in the model gas test. Moreover, the emission values of NOx, HC, and CO were 50% or less than Japanese domestic regulation values even after 830°C×60h heat treatment in a vehicle test.
Journal Article

Development of a New Metal Substrate for Lean NOx Trap

2008-04-14
2008-01-0806
This paper presents a new substrate for Lean NOx Traps (LNT) which enables high NOx conversion efficiency, even after long-term aging, when using alkali metals as the NOx adsorber. When a conventional metal honeycomb is used as the LNT substrate, the chromium in the metal substrate migrates into the washcoat and reacts with the alkali metals after thermal aging. In order to help prevent this migration, we have developed a new substrate where a fine -alumina barrier is precipitated to the surface of the metal substrate. The new substrate is highly capable of preventing migration of chromium into the washcoat and greatly enhances the NOx conversion. The durability of the new substrate and emission test using a test vehicle are also examined.
Technical Paper

Improvement of Thermal Resistance for Lean NOx Catalyst

2003-03-03
2003-01-1166
A new type of lean NOx catalyst has been developed with improved thermal resistance. This lean NOx catalyst contains precious metals and NO2 adsorbents. The precious metals are used mainly for the oxidation reaction of NO, and the NO2 adsorbents are for the adsorption removal of generated NO2. The thermal resistance of the catalyst was raised by paying attention to the following points. 1) Improvement of thermal resistance for the NO oxidation activity by addition of a different precious metal element. 2) Prevention of thermal degradation of the NO2 adsorbent by addition of a new metal oxide. For item 1, Pd was added to the catalyst which had already included Pt. By having Pd coexist with Pt, the precious metal dispersion was kept high even after heat treatment, so the NO oxidizing ability was improved. For item 2, thermal degradation of NO2 adsorbent was prevented by addition of the new metal oxide (B) to the adsorbent.