Low-pressure molding compound (LPMC) is a new kind of composite material which can be used for automotive body panels. LPMC has similar mechanical properties compared to conventional sheet molding compound (SMC) but excellent moldability due to the different thickening system. In this paper, we prepared LPMC hood prototype for a passenger car using a low-cost tooling. Inner panel and outer panel were made of general-density- and low-density-grade LPMC, respectively, in order to maximize weight reduction maintaining surface quality. Physical properties containing tensile strength, flexural modulus, notched Izod impact strength of those samples were investigated. In addition, CAE simulation was also done for strength analysis of the hood assembly.

The objective of this study is to investigate mechanical properties and fatigue crack propagation behavior in hybrid metal matrix composites by squeeze infiltration method (15% Al2O3 + SiCw/6061Al). The mechanical properties of Al2O3+SiCw/Al composites including tensile strength, yield strength, Young's modulus, were improved compared with those of unreinforced alloy and Al203/Al composites. The hybrid composites were more ductile than Al2O3/Al composites. Fatigue crack propagation rates of both Al2O3/Al and Al2O3+SiCw/Al composites showed a similar behavior in region II. Their propagation rates were higher in entire ▵K region compared with that of 6061 Al alloy. From the crack path morphology, fatigue cracks propagated linearly and smoothly in 6061 Al alloy. However, in the metal matrix composites cracks tend to avoid the reinforcements promoting crack deflection. It was observed that crack deflection enhanced crack closure due to wedging phenomenon.

The effects of tempering on carburized Cr-Mo gear steel were investigated through mechanical and fatigue tests. Specimens were carburized at 900°C for 180 minutes, and then oil quenched at 150°C for 10 minutes of holding time and cooled to room temperature. The subsequent tempering process was performed to 160°C for 90 minutes. Surface hardness and residual compressive stress were decreased by tempering treatment, whereas tensile strength, yield strength and impact energy were increased. Bending fatigue endurance limits for both tempered and untempered specimens were same as 779MPa. The strength of roller contact fatigue is also not greatly influenced by tempering treatment. Thermal distortion for carburized transfer driven gear before and after tempering exhibited a similar distribution. Microstructural changes during tempering were also discussed.