Search Results

A fatigue crack growth model is adopted in this paper to investigate the fatigue lives of resistance spot welds in square-cup and lap-shear specimens of dual phase, low carbon and high strength steels under cyclic loading conditions. The fatigue crack growth model is based on the global stress intensity factor solutions for main cracks, the local stress intensity factor solutions for kinked cracks as functions of the kink length, the experimentally determined kink angles, and the Paris law for kinked crack propagation. The predicted fatigue lives based on the fatigue crack growth model are then compared with the experimental data. The results indicate that the fatigue life predictions based on the fatigue crack growth model are in agreement with or lower than the experimental results.

Failure loads of spot welds are investigated under static and impact loading conditions. A test fixture was designed and used to obtain maximum loads of spot welds under a range of combined opening and shear loads with different loading rates. Optical micrographs of the cross sections of spot welds before and after failure were obtained to understand the failure processes under various loading rates and different combinations of loads. The experimental results indicate that under nearly pure opening loads, the failure occurs along the nugget circumferential boundary. Under combined opening and shear loading conditions, the failure starts from the tensile side of the base metal near the nugget in a necking/shear failure mode. The effects of sheet thickness and combined load on the load carrying behavior of spot welds are investigated under static and impact loading conditions based on the experimental results.

Effects of impact velocity on the crush behavior of aluminum 5052-H38 honeycomb specimens are investigated by experiments. An impact test machine using pressurized nitrogen was designed to perform dynamic crush tests. A test fixture was designed such that inclined loads can be applied to honeycomb specimens in dynamic crush tests. The results of dynamic crush tests indicate that the effects of impact velocity on the normal and inclined crush strengths are significant. The trends of the inclined crush strengths for specimens with different in-plane orientation angles as functions of impact velocity are very similar to that of the normal crush strength. Experimental results show similar progressive folding mechanisms for honeycomb specimens under pure compressive and inclined loads. Under inclined loads, the inclined stacking patterns were observed. The inclined stacking patterns are due to the asymmetric locations of the horizontal plastic hinge lines.

In this paper, the formability of AA5754 aluminum laser-welded blanks produced by Nd:YAG laser welding is investigated under biaxial straining conditions. The mechanical behavior of the laser-welded blanks is first examined by uniaxial tensile tests conducted with the weld line perpendicular to the tensile axis. Shear failure in the weld metal is observed in the experiments. Finite element simulations under generalized plane strain conditions are then conducted in order to further understand the effects of weld geometry and strength on the shear failure and formability of these welded blanks. The strain histories of the material elements in the weld metal obtained from finite element computations are finally used in a theoretical failure analysis based on the material imperfection approach to predict the failure strains for the laser-welded blanks under biaxial straining conditions.

Resonant frequencies of a resonant bending system with notched crankshaft sections are obtained experimentally and numerically in order to investigate the effect of notch depth on the drop of the resonant frequency of the system. Notches with the depths ranging from 1 to 5 mm, machined by an EDM (Electrical-Discharging Machining) system, were introduced in crankshaft sections at the fillet between the main crank pin and crank cheek. The resonant frequencies of the resonant bending system with the crankshaft sections with various notch depths were first obtained from the experiments. Three-dimensional finite element models of the resonant bending system with the crankshafts sections with various notch depths are then generated. The resonant frequencies based on the finite element computations are in good agreement with those based on the experimental results.

In this paper, the fatigue failure of the primary roller used in a crankshaft fillet rolling process is investigated by a failure analysis and a two-dimensional finite element analysis. The fillet rolling process is first discussed to introduce the important parameters that influence the fatigue life of the primary roller. The cross sections of failed primary rollers are then examined by an optical microscope and a Scanning Electron Microscope (SEM) to understand the microscopic characteristics of the fatigue failure process. A two-dimensional plane strain finite element analysis is employed to qualitatively investigate the influences of the contact geometry on the contact pressure distribution and the Mises stress distribution near the contact area. Fatigue parameters of the primary rollers are then estimated based on the Findley fatigue theory.

Failure behavior of spot welds is investigated under impact loading conditions. Three different impact speeds were selected to test both HSLA steel and mild steel specimens under combined opening and shear loading conditions. A test fixture was designed and used to obtain the failure loads of spot weld specimens of different thicknesses under a range of combined opening and shear loads with different impact speeds. Accelerometers were installed on the fixtures and the specimens for investigation of the inertia effects. Optical micrographs of the cross sections of failed spot welds were obtained to understand the failure processes in both HSLA steel and mild steel specimens under different combined impact loads. The experimental results indicate that the failure mechanisms of spot welds are very similar for both HSLA steel and mild steel specimens with the same sheet thickness. These micrographs show that the sheet thickness can affect the failure mechanisms.

Experiments to obtain the failure loads of spot welds are first reviewed under combined opening and shear loading conditions. A failure criterion is then presented for spot welds under combined opening and shear loading conditions based on the results from the experiments and a lower bound limit load analysis. In order to account for spot welds under more complex loading conditions, another lower bound limit load solution is presented to characterize the failure loads of spot welds under combinations of three forces and three moments. Based on the limit load solution, an engineering failure criterion is proposed with correction factors determined by different spot weld tests. The engineering failure criterion can be used to characterize the failure loads of spot welds with consideration of the effects of sheet thickness, nugget radius and combinations of loads.

Sandwich specimens with DP590 steel face sheets and structural epoxy foam cores are investigated under three-point bending conditions. Experimental results indicate that the maximum loads correspond to extensive cracking in the foam cores. Finite element simulations of the bending tests are also performed to understand the failure mechanisms of the epoxy foams. In these simulations, the plastic behavior of the steel face sheets is modeled by the Mises yield criterion with consideration of plastic strain hardening. A pressure sensitive yield criterion is used to model the plastic behavior of the epoxy foam cores. The epoxy foams are idealized to follow an elastic perfectly plastic behavior. The simulation results indicate that the load-displacement responses of some sandwich specimens agree with the experimental results.

We conduct static experiments to investigate the influence of shear stress on the crush behavior of honeycomb materials. The aluminum honeycomb materials selected in this investigation are orthotropic due to their manufacturing processes. A test fixture and honeycomb specimens are designed such that combined compressive and shear loads along the strongest material symmetry axis can be controlled and applied accurately. The experimental results indicate that both the peak and crush strengths under combined compressive and shear loads are lower than those under pure compressive loads. A yield function is suggested for honeycomb materials under the combined loads based on a phenomenological plasticity theory. The microscopic crush mechanism under the combined loads is also investigated. A microscopic crush model based on the experimental observations is developed. The crush model includes the rupture of aluminum cell walls so that the kinematic requirement can be satisfied.

An effective fatigue driving stress is proposed to predict the failure of spot welds under cyclic combined loading conditions. The effective fatigue driving stress is obtained based on the Mises yield criterion in terms of the resultant forces and moments in a plastic collapse analysis of spot welds under complex combined loading conditions as discussed in Lin et al. [1]. The effective fatigue driving stress can be used to correlate the fatigue data of spot welds with consideration of the effects of the sheet thickness, nugget diameter and loading conditions. Experimental results for coach-peel and lap-shear specimens under cyclic loading conditions are used to evaluate the applicability of the effective fatigue driving stress. The experimental results for spot welds in both coach-peel and lap-shear specimens are correlated very well based on the effective fatigue driving stress.

Fatigue failures of spot friction welds in lap-shear specimens of aluminum 6111-T4 sheets under cyclic loading conditions are investigated in this paper. The paths of fatigue cracks near the spot friction welds are first discussed. A fatigue crack growth model based on the Paris law for crack propagation and the global and local stress intensity factors for kinked cracks is then adopted to predict the fatigue lives of these spot friction welds. The global stress intensity factors and the local stress intensity factors based on the recent published works for resistance spot welds in lap-shear specimens are used to estimate the local stress intensity factors for kinked cracks with experimentally determined kink angles. The results indicate that the fatigue life predictions based on the Paris law and the local stress intensity factors as functions of the kink length agree well with the experimental results.

The crush strength of aluminum 5052-H38 honeycomb materials under combined compressive and shear loads are investigated here. The experimental results indicate that both the peak and crush strengths under combined compressive and shear loads are lower than those under pure compressive loads. A yield function is suggested for honeycomb materials under the combined loads based on a phenomenological plasticity theory. The microscopic crush mechanism under the combined loads is also investigated. A microscopic crush model based on the experimental observations is developed. The crush model includes the assumptions of the asymmetric location of horizontal plastic hinge line and the ruptures of aluminum cell walls so that the kinematic requirement can be satisfied. In the calculation of the crush strength, two correction factors due to non-associated plastic flow and different rupture modes are considered.

The quasi-static crush behavior of aluminum 5052-H38 honeycomb specimens under non-proportional compression dominant combined loads is investigated by experiments. Compression dominant combined loads and pure compressive loads were applied in different sequences to induce non-proportional combined loads. The experimental results show that the normal crush and shear strengths in combined loading regions and the normal crush strengths in pure compressive loading regions of the non-proportional combined loads are quite consistent with the existing phenomenological yield criterion based on the experimental normal crush and shear strengths under proportional combined loads. The experimental results indicate that the sequence of loading paths for the non-proportional combined loads does not affect the crush strengths of honeycomb specimens.

A general failure criterion for spot welds is proposed with consideration of the plastic anisotropy and the separation speed for crash applications. A lower bound limit load analysis is conducted to account for the failure loads of spot welds under combinations of three forces and three moments. Based on the limit load solution and the experimental results, an engineering failure criterion is proposed with correction factors determined by different spot weld tests. The engineering failure criterion can be used to characterize the failure loads of spot welds with consideration of the effects of the plastic anisotropy, separation speed, sheet thickness, nugget radius and combinations of loads. Spot weld failure loads under uniaxial and biaxial opening loads and those under combined shear and twisting loads from experiments are shown to be characterized well by the engineering failure criterion.