The bending fatigue performance of gears, cantilever beam specimens, and notched-axial specimens were evaluated and compared. Specimens were machined from a modified SAE-4118 steel, gas-carburized, direct-quenched and tempered. Bending fatigue specimens were characterized by light metallography to determine microstructure and prior austenite grain size, x-ray analysis for residual stress and retained austenite measurements, and scanning electron microscopy to evaluate fatigue crack initiation, propagation and overload. The case and core microstructures, prior austenite grain sizes and case hardness profiles from the various types of specimens were similar. Endurance limits were determined to be about 950 MPa for both the cantilever beam and notched-axial fatigue specimens, and 1310 MPa for the single gear tooth specimens.

The effects of subzero treatments on the bending fatigue performance of carburized gear steels were investigated by cantilever bending fatigue testing. Specimens were machined from SAE-4320 and SAE-9310 bar stock steel, gas-carburized, quenched, tempered at 175°C, subzero cooled to -73°C and -196°C, and tempered at 175°C. Bending fatigue specimens were characterized by light metallography to determine microstructure and prior austenite grain size, x-ray diffraction for residual stress and retained austenite contents, microhardness testing, and scanning electron microscopy to evaluate fatigue crack initiation, propagation and overload. Refrigeration treatments caused additional transformation of retained austenite and increased surface hardness and compressive residual stresses. Bending fatigue endurance limits for the SAE-4320 specimens were determined to be 1310 MPa for the as-carburized condition, 1170 MPa for the -73°C condition, and 1280 MPa for the -196°C condition.