Part II of the paper focuses on fatigue tests of four specific gear steels: SAE 4320, SAE 8822, PS18, and 20MnCr5. Fatigue life, S-N curves are experimentally generated for all steels at low cycle fatigue and high cycle fatigue. The failure stresses at cycle one and slope of the linear portion of S-N curves are determined based on the experimental data. Endurance limits were tested. Uncertainty in the fatigue data is analyzed in details and values of sigma are calculated. Design curves were estimated based on the fatigue test results.

This particular study focuses on four specific gear steels: SAE 4320, SAE 8822, PS18, and 20MnCr5. Notched specimens are manufactured from the four materials. Three point bending experiments were conducted which include ultimate tests and fatigue tests. Part I is on ultimate test only. Part II will concentrate on fatigue testing. In order to see how the carburization affected the fatigue performance of these steels, a residual stress test was performed on one sample of each steel by mean of the incremental hole drilling method. The compressive stresses were found in all four steels with minimum and maximum stress approximately equal. This suggests that the residual stresses are biaxial in the carburized steel case. The difference between the maximum and minimum stresses is within 37% for all steels. The residual stress after the carburization process were found to be highest in the 4320 steel and SAE 8822, followed by PS 18 and then MnCr.