The effect of GTL diesel fuel on organic materials used in fuel delivery systems of vehicles was investigated. Specimens made from 16 kinds of organic materials were immersed in GTL diesel fuels synthesized at Refinery-A and Refinery-B (referred to as GTL-A and GTL-B, respectively) and then subjected to tensile testing. The tensile test results revealed that elongation of the nylon sample immersed in GTL-A was extremely small, about 4% of that of untreated nylon. In the light of this finding, the GTL diesel fuels and nylons before and after immersion test were analyzed in detail using about 20 analysis methods to determine the cause for poor elongation. The following points were found. (1) GTL-A consisted of low molecular-weight paraffins. (2) GTL-A had low molecular-weight i-paraffins. (3) The nylon immersed in GTL-A contained low molecular-weight paraffins. (4) The paraffins in the nylon immersed in GTL-A were richer in i-paraffins than the original GTL-A.

In a previous paper (Part 1 of this series), nylon-66 specimens were immersed in two GTL diesel fuels (GTL-A and GTL-B) and then subjected to tensile testing. The tensile test results revealed that the elongation of the specimen immersed in GTL-A was dramatically reduced. The GTL diesel fuels and nylon specimens before and after immersion were analyzed to determine the cause of the decline in elongation. It was found that the poor elongation was caused by penetration and oxidation of low molecular-weight paraffins and that the ease of penetration and oxidation of paraffin depended on the structure of paraffin. In this paper, the low molecular-weight paraffins detected in GTL-A were mixed to produce model fuels. Then, pieces of nylon cut from the tensile test specimen, were immersed in the model fuels. In addition, partial oxidation products of the paraffin (alcohol, aldehyde or ketone and acid) were used in immersion tests of the nylon pieces.

In emerging markets, Port Fuel Injection (PFI) technology retains a higher market share than Gasoline Direct Injection (GDI) technology. In these markets fuel quality remains a concern even despite an overall improvement in quality. Typical PFI engines are sensitive to fuel quality regardless of brand, engine architecture, or cylinder configuration. One of the well-known impacts of fuel quality on PFI engines is the formation of Intake Valve Deposits (IVD). These deposits steadily accumulate over time and can lead to a deterioration of engine performance. IVD formation mechanisms have been characterized in previous studies. However, no test is available on a state-of-the-art engine to study the impact of fuel components on IVD formation. Therefore, a proprietary engine test was developed to test several chemistries. Sixteen fuel blends were tested. The deposit formation mechanism has been studied and analysed.