Weight reduction of automobiles is one of the most highlighted subjects in automobile industry from the energy saving and clean environment points of view. A typical approach for the purpose is to use high strength steel sheets as well as optimizing designs and using low density materials. It is not, however, easy to apply high strength steel sheets to automotive panels because of their strict requirement for the shape-fixability although a high dent resistance is also required. Besides the use of bake hardening steels, two different high strength steel sheets, which are a continuously annealed extra-low carbon titanium-added IF steel and a low carbon TRIP steel which contains about six volume% of austenite, were assessed for the application to automotive panels in combination with a tension-controled press-forming technique and showed as good shape-fixability as a conventional box-annealed aluminum-killed DDQ steel sheet when high blank-holding-forces were applied.

Extremely formable cold sheet steel with an ultra-high Lankford value of more than 2.5 and an n value of more than 0.27 has been developed. This steel is obtained due to the following factors; using extremely pure IF (Interstitial free) steel, immediate rapid cooling upon completion of rolling in the hot rolling process, a high reduction in the cold rolling process, and a high soaking temperature in the continuous annealing process. This steel sheet shows excellent deep drawability and stretch formability compared with conventional steel sheet (former IF steel and low carbon aluminum-killed steel) as a result of evaluating the limiting drawing ratio and limiting dome height, respectively. This excellent formability is also shown by the model forming tests for simulating the actual stamping of an oilpan and a side-panel. Furthermore, this steel shows the same spot-weldability as that of former IF steel, and zinc phosphatability similar to that of low carbon aluminum-killed steel.

Improvement of material characteristic values, adjustment of forming conditions as well as introduction of new forming technics are necessary to promote wide application of aluminum alloy sheets into automotive parts. 5000 series and 6000 series aluminum alloy sheets are concerned about the relationship between material characteristic values and fundamental forming ability required to apply them to automobile body parts as well as the effect of lubricant on their formability. The hardening parameters, n values, of them are larger than those of cold-rolled steel sheets. However, the r values and the local elongations are extremely small. The improvement of stretch formability owing to increase of n value is smaller than that of the steel sheets. Inferior deep drawability of the aluminum alloy sheets is due to low fracture resistance force caused by low r value.