An experimental investigation of the effects of ceramic coatings on diesel engine performance and exhaust emissions was conducted. Tests were carried out over a range of engine speeds at full load for a standard metal piston and two pistons insulated with 0.5 mm and 1.0 mm thick ceramic coatings. The thinner (0.5 mm) ceramic coating resulted in improved performance over the baseline engine, with the gains being especially pronounced with decreasing engine speed. At 1000 rpm, the 0.5 mm ceramic coated piston produced 10% higher thermal efficiency than the metal piston. In contrast, the relatively thicker coating (1 mm), resulted in as much as 6% lower thermal efficiency compared to baseline. On the other hand, the insulated engines consistently presented an attractive picture in terms of their emissions characteristics. Due to the more complete combustion in the insulated configurations, exhaust CO levels were between 30% and 60% lower than baseline levels.

An advanced low heat rejection engine concept has been selected based on a trade-off between thermal insulating performance and available technology. The engine concept heat rejection performance is limited by available ring-liner tribology and requires cylinder liner cooling to control the piston top ring reversal temperature. This engine concept is composed of a titanium piston, headface plate and cylinder liner insert with thermal barrier coatings. Monolithic zirconia valve seat inserts, and thermal barrier coated valves and intake-exhaust ports complete the insulation package. The tribological system is composed of chrome oxide coated cylinder, M2 steel top piston ring, M2 steel valve guides, and an advanced polyol ester class lubricant.

The cylinder of the aluminum engine block without iron sleeve was coated directly with thin thermal barrier coatings of zirconia and chrome oxide. The cylinder head and valve face and the piston crown were also coated. These three engine components were tested individually and together. The fuel consumption performance of this 84 x 70 mm direct injection diesel engine improved 10% with only coated cylinder bore. When the fuel injection timing of the coated cylinder bore engine was retarded by about 2°CA, emissions characteristics were approximately the same level as for the baseline engine with 8% improvement in brake specific fuel consumption compared with the baseline engine. At constant fuel flow rate to the engine, the exhaust and cylinder head temperatures were higher for the insulated bore case. One can summarize the combustion temperature must have been higher and heat release rates were faster in the insulated case.

The trend toward lighter vehicles for improved performance has recently introduced the use of aluminum and plastic materials for vehicle bodies and drive trains. In particular, the aluminum alloy block for engine application is certain to reappear. The soft aluminum cylinder liner will require additional treatment before acceptance. Three possible approaches appear to solve the aluminum cylinder liner dilemma. These approaches are: 1. Use of high silicon aluminum such as the 390 aluminum. 2. Insert or cast steel liners into the aluminum engine block. 3. Ceramic coat the low cost standard aluminum engine block. Each has known advantages and disadvantages. It is the purpose of this paper to present the merits of Option 3, the ceramic coated aluminum cylinder bore from the standpoint of low weight, cost, and tribological effectiveness. The advantages of approaches (1) and (2) are obvious. High temperature after treatment of the ceramic engine components is not required.

The experimental emissions testing of a turbocharged six cylinder Caterpillar 3116 diesel engine converted to the Miller cycle operation was conducted. Delayed intake valve closing times were also investigated. Effects of intake valve closing time, injection time, and insulation of piston, head, and liner on the emission characteristics of the Miller cycle engine were experimentally verified. Superior performance and emission characteristic was achieved with a LHR insulated engine. Therefore, all emission and performance comparisons are made with LHR insulated standard engine with LHR insulated Miller cycle engine. Particularly, NOx, CO2, HC, smoke and BSFC data are obtained for comparison. Effect of increasing the intake boost pressure on emission was also studied. Poor emission characteristics of the Miller cycle engine are shown to improve with increased boost pressure. Performance of the insulated Miller cycle engine shows improvement in BSFC when compared to the base engine.

Thermal barrier coatings (TBC) are perceived as enabling technology to increase low heat rejection (LHR) diesel engine performance and improve its longevity. The state of the art of thermal barrier coating is the plasma spray zirconia. In addition, other material systems have been investigated for the next generation of thermal barrier coatings. The purpose of this TBC program is to focus on developing binder systems with low thermal conductivity materials to improve the coating durability under high load and temperature cyclical conditions encountered in the real engine. Research and development (R&D) and analysis were conducted on aluminum alloy piston for high output turbocharged diesel engine coated with TBC.

A zero-dimensional heat release model has been formulated for small bore, automotive-type, direct injection diesel engines and compared with high-speed data acquired from a prototype single-cylinder engine. This comparison included a significant portion of the full-load torque curve and various light-loads with variable speed, injection timing sweeps, and injection pressures. In general, the agreement between the predicted net heat release rate profiles and the experimentally, indirectly-determined profiles was acceptable from a mean cylinder pressure point-of-view while employing a single constant for the turbulent mixing dissipation rate. The proposed model also revealed that moderate swirl rates included in this study had little impact on the gross fuel burning rate profile especially at higher load conditions.

A highly effective thermal insulating piston concept with high projected durability characteristics has been developed by means of computer aided modelling, thermal rig bench screening, and small-bore engine testing. The piston concept is composed of a relatively low thermal conductivity titanium alloy type 6242 structural material and a 1.25 mm thick slurry densified thermal barrier coating. The piston material, structural configuration, and detail design features were selected through computer aided modelling and qualified through small-bore engine testing. Screening of plasma sprayed thermal barrier coatings was performed on a simple thermal test rig and final selection of a system was made through small-bore engine testing.

This paper deals with the analysis of heat release characteristics of an insulated turbocharged, six cylinder, DI contemporary diesel engine. The engine is fully insulated with thin thermal barrier coatings. Effect of insulation on the heat release was experimentally verified. Tests were carried over a range of engine speeds at 100%, 93%, 75% and 50% of rated torque. Fuel injection system was instrumented to obtain injection pressure characteristics. The study shows that rate of heat release, particularly in the major portion of the combustion, is higher for the insulated engine. Improvement in heat release and performance are primarily attributed to reduction in heat transfer loss due to the thin thermal barrier coating. Injection pressure at the rated speed and torque was found to be 138 MPa and there was no degradation of combustion process in the insulated engine. Improvements in BSFC at 93% load are 3.25% and 6% at 1600 and 2600 RPM, respectively.

A high output experimental single cylinder diesel engine that was fully coated and insulated with a ceramic slurry coated combustion chamber was tested at full load and full speed. The cylinder liner and cylinder head mere constructed of 410 Series stainless steel and the top half of the articulated piston and the cylinder head top deck plate were made of titanium. The cylinder liner, head plate and the piston crown were coated with ceramic slurry coating. An adiabaticity of 35 percent was predicted for the insulated engine. The top ring reversal area on the cylinder liner was oil cooled. In spite of the high boost pressure ratio of 4:1, the pressure charged air was not aftercooled. No deterioration in engine volumetric efficiency was noted. At full load (260 psi BMEP) and 2600 rpm, the coolant heat rejection rate of 12 btu/hp.min. was achieved. The original engine build had coolant heat rejection of 18.3 btu/hp-min and exhaust energy heat rejection of 42.3 btu/hp-min at full load.

An advanced low heat rejection engine concept has successfully completed a 100 hour endurance test. The combustion chamber components were insulated with thermal barrier coatings. The engine components included a titanium piston, titanium headface plate, titanium cylinder liner insert, M2 steel valve guides and monolithic zirconia valve seat inserts. The tribological system was composed of a ceramic chrome oxide coated cylinder liner, chrome carbide coated piston rings and an advanced polyolester class lubricant. The top piston compression ring Included a novel design feature to provide self-cleaning of ring groove lubricant deposits to prevent ring face scuffing. The prototype test engine demonstrated 52 percent reduction in radiator heat rejection with reduced intake air aftercooling and strategic forced oil cooling.

This paper investigates theoretically the effects of heat transfer characteristics, such as crank-angle phasing and wall temperature swings, on the thermodynamic efficiency of an IC engine. The objective is to illustrate the fundamental physical basis of applying thin thermal barrier coatings to improve the performance of military and commercial IC engines. A simple model illustrates how the thermal impedance and thickness of coatings can be manipulated to control heat transfer and limit the high temperatures in engine components. A friction model is also included to estimate the overall improvement in engine efficiency by the proper selection of coating thickness and material.

The successful design of engine components for high temperature applications is very dependent on the use of advanced finite element methods. Without the use of thermal and structural modeling techniques it is virtually impossible to establish the reliable design specifications to meet the application requirements. Advanced modeling and design of two key engine components, the cylinder head thermal insulating headface plate and the capped air gap insulated piston, are presented. Prior engine test experience contributes to further understanding of the important factors in recognizing successful design solutions. It has been found that the modeling results are only as good as the modeling assumptions and that all modeling boundary conditions and constraints must be reviewed carefully.

This paper investigates theoretically the benefits of the Miller cycle diesel engine with and without low heat rejection on thermodynamic efficiency, brake power, and fuel consumption. It further illustrates the effectiveness of thin thermal barrier coatings to improve the performance of military and commercial IC engines. A simple model which includes a friction model is used to estimate the overall improvement in engine performance. Miller cycle is accomplished by closing the intake valve late and the engine components are coated with PSZ for low heat rejection. A significant improvement in brake power and thermal efficiency are observed.

Thermal barrier coatings are becoming increasingly important in providing thermal insulation for heat engine components. Thermal insulation reduces in-cylinder heat transfer from the engine combustion chamber as well as reducing component structural temperatures. Containment of heat also contributes to increased in-cylinder work and offers higher exhaust temperatures for energy recovery. Lower component structural temperatures will result in greater durability. Advanced ceramic composite coatings also offer the unique properties that can provide reductions in friction and wear. Test results and analysis to evaluate the performance benefits of thin thermal barrier coated components in a single cylinder diesel engine are presented.

Past experience has shown that the power density of an engine itself is not a sufficient guide to determine whether it will meet the power density needs of the intended combat vehicle application. The real need is for the complete propulsion system to be power dense. Here the definition of the propulsion system includes the engine, transmission, cooling system, air filtration system, intake and exhaust ducting, controls, accessories, batteries, fuel system and final drives. The power pack is a subset of the propulsion system and consists of that part of the propulsion system that would be lifted out of the vehicle for service or replacement and would typically consist of at least the engine, and transmission, cooling system, and power pack controls and ideally would also include the air filtration system and accessory drives. Engine operating characteristics will directly impact power density for some propulsion system items.

This paper describes the progress on the Cummins-TARADCOM adiabatic turbocompound diesel engine development program. An adiabatic diesel engine system adaptable to the use of high performance ceramics which hopefully will enable higher operating temperatures, reduced heat loss, and turbo-charged exhaust energy recovery is presented. The engine operating environments as well as the thermal and mechanical loadings of the critical engine components are covered. Design criteria are presented and techniques leading to its fulfillment are shown. The present shortcomings of the high performance ceramic design in terms of meeting reliability and insulation targets are discussed, and the needs for composite designs are shown. A ceramic design methodology for an insulated engine component is described and some of the test results are shown. Other possible future improvements such as the minimum friction-unlubricated engine through the use of ceramics are also described.

A Minimum Cooled Engine (MCE) has been successfully run for 250 hours at rated condition of 298 kW and 1900 rpm. This engine was all metallic without any coolant in the block and lower part of the heads. Ring/liner/lubricant system and thermal loading on the liner at top ring reversal (TRR) as well as on the piston are presented and discussed. Ring/liner wear is given as well as oil consumption and blow-by data during the endurance run. Another engine build with a different top ring coating and several lubricants suggested that a 1500 hours endurance run of MCE is achievable. Rig test data for screening ring materials and synthetic lubricants necessary for a successful operation of a so-called Adiabatic Engine with the ring/ceramic liner (SiN) interface temperature up to 650°C are presented and discussed.

This paper discusses the goals, progress, and future plans of the TACOM/Cummins Adiabatic Engine Program. The Adiabatic Engine concept insulates the diesel combustion chamber with high temperature materials to allow hot operation near an adiabatic operation condition. Additional power and improved efficiency derived from this concept occur because thermal energy, normally lost to the cooling and exhaust systems, is converted to useful power through the use of turbomachinery and high-temperature materials. Engine testing has repeatedly demonstrated the Adiabatic Engine to be the most fuel efficient engine in the world with multi-cylinder engine performance levels of 0.285 LB/BHP-HR (48% thermal efficiency) at 450 HP representative. Installation of an early version of the Adiabatic Engine within a military 5 ton truck has been completed, with initial vehicle evaluation successfully accomplished.

A new concept is described for a combined cycle Diesel-Stirling engine that promises to achieve an extraordinarily high thermal efficiency. The two basic cycles are coupled together in series, the high temperature exhaust gases from an adiabatic Diesel engine are fed into a high efficiency Stirling engine in such a way that both engines produce mechanical power. The whole combined cycle is highly turbocharged in order to get the desired power density, favorable heat transfer conditions and energy saving regeneration of exhaust gas heat. The problems posed by such a combined cycle are examined and calculation results are presented and discussed using a mathematical model developed as a preliminary effort of optimization and evaluation.