Search Results

An experimental investigation of the effects of ceramic coatings on diesel engine performance and exhaust emissions was conducted. Tests were carried out over a range of engine speeds at full load for a standard metal piston and two pistons insulated with 0.5 mm and 1.0 mm thick ceramic coatings. The thinner (0.5 mm) ceramic coating resulted in improved performance over the baseline engine, with the gains being especially pronounced with decreasing engine speed. At 1000 rpm, the 0.5 mm ceramic coated piston produced 10% higher thermal efficiency than the metal piston. In contrast, the relatively thicker coating (1 mm), resulted in as much as 6% lower thermal efficiency compared to baseline. On the other hand, the insulated engines consistently presented an attractive picture in terms of their emissions characteristics. Due to the more complete combustion in the insulated configurations, exhaust CO levels were between 30% and 60% lower than baseline levels.

An experimental study of the effects of thin ceramic thermal barrier coatings on the performance of a spark-ignited gasoline engine was conducted. A modified 2.5 liter GM engine with ceramic-coated pistons, liners, head, valves and ports was used. Experimental results obtained from the ceramic engine were compared with baseline metal engine data. It was shown that at low-speed part-load conditions encountered in typical driving cycles the ceramic engine could achieve up to 18% higher brake power and up to 10% lower specific fuel consumption. At wide open throttle conditions, the two engines exhibited similar characteristics, except at high speeds where the metal engine showed better performance at the expense of inferior fuel economy. The ceramic coating did not produce any observable knock in the engine and showed no significant wear at the conclusion of the testing phase.

Finite element models of various fast-response thermocouple designs have been developed. Due to the small differences in thermal properties between thermoelements and metal engine components, standard co-axial thermocouples can measure transient temperatures of metal components within an accuracy of 98%. However, these relatively small errors in total temperature measurement translate into as high as 30% errors in indicated peak-to-peak-temperature swings for iron surfaces. The transient swing errors result in up to 30% errors in peak heat flux rates to iron surfaces. These peak heat flux errors can be substantially larger if coaxial thermocouples are used for heat flux measurements in aluminum or ceramic surfaces. Increasing the thin film thickness is a compromise solution to reduce the discrepancy in peak heat flux measured with coaxial designs in metal engines. An alternative overlapping thin film thermocouple design has also been evaluated.

Transient tests in a 2.0 liter in-line 4 cylinder downsizing gasoline direct injection engine were conducted under various transient conditions in order to investigate effects of lower rotational inertia of titanium aluminide alloy (TiAl) turbine wheel on engine and turbocharger performances. As a representative result, fast boost pressure build up was achieved in case of TiAl turbocharger compared to Inconel turbocharger. This result was mainly due to lower rotational inertia of TiAl turbine wheel. Engine torque build up response was also improved with TiAl turbocharger even though engine torque response gap between both turbochargers was slightly reduced due to retarded combustion phase. In addition, with advanced ignition timing, fuel consumption became less than that of Inconel turbocharger with similar engine torque response.