Fracture split forged steel connecting rods are utilized in many new high performance automotive engines to increase durability. Higher strength levels are needed as the power density increases. Fracture splitting without plastic deformation is necessary for manufacturability. Metallurgical design is a key for achieving the required performance levels. Several medium carbon steels containing 0.07 wt pct P, 0.06 wt pct S and various amounts of Mn, Si, V, and N were produced by vacuum induction melting laboratory heats and hot working the cast ingots into plates. The plates were cooled at varying rates to simulate typical cooling methods after forging. Microstructures were generally ferrite and pearlite as evaluated by light optical and scanning electron microscopy. Mechanical properties were determined by standard tensile tests, high strain rate notched tensile tests, and Charpy V-notch impact tests to assess “splittability”.

The bending fatigue performance of high temperature (1050 °C) vacuum carburized Nb modified 8620 steel, with niobium additions of 0.02, 0.06 and 0.1 wt pct, was evaluated utilizing a modified Brugger specimen geometry. Samples were heated at two different rates (20 and 114 °C min-1) to the carburizing temperature resulting in different prior austenite grain structures that depended on the specific Nb addition and heating rate employed. At the lower heating rate, uniform fine grained prior austenite grain structures developed in the 0.06 and 0.1 Nb steels while a duplex grain structure with the presence of large (>200 μm grains) developed in the 0.02 Nb steel. At the higher heating rate the propensity for abnormal grain growth was highest in the 0.02 Nb steel and complete suppression of abnormal grain growth was achieved only with the 0.1 Nb steel.

Fine water mist has become a commercial technology for fire suppression in multiple applications. With funding from NASA, ADA Technologies, Inc. (ADA) is developing a handheld fine water mist fire extinguisher for use on manned spacecraft and in future planetary habitats. This design employs only water and nitrogen as suppression agents to allow local refill and reuse. The prototype design incorporates features to generate a uniform fine water mist regardless of the direction of the gravitational vector or lack of gravity altogether. The system has been proven to extinguish open fires and hidden fire scenarios in tests conducted at the Colorado School of Mines (CSM). This design can be deployed as a portable extinguisher or as an automated system for local fire protection in instrument racks or storage spaces. Continued development will result in prototype hardware suitable for use on future manned spacecraft.

ADA Technologies, Inc. has designed and built a microgravity-tolerant portable fire extinguisher prototype for use in manned spacecraft and planetary habitats. This device employs Fine Water Mist (FWM) as the fire extinguishing agent, and is refillable from standard stores on long-duration missions. The design uses a single storage tank for minimal mass and volume. The prototype employs a dual-fluid atomizer concept where the pressurant gas (nitrogen) also enhances the water atomization process to generate a droplet size distribution in the optimum diameter range of 10 to 50 micrometers. The expanding discharge gas plume carries the mist to the immediate vicinity of the fire where its extensive surface area promotes high heat transfer rates. A series of 80 fire suppression tests was recently completed to evaluate design options for the hardware and validate performance on three representative fire scenarios.

Propelled by the renewed international interest in returning to the Moon, an international consortium organized the first European Lunar Base Design Workshop in the summer of 2002. The objective of this Workshop was to propose new design concepts for human and robotic exploration of the Moon and move beyond the outdated ‘man-in-a-can’ genre of space architecture. The Workshop introduced a new genre in lunar base architecture, deriving from bold, innovative and unconventional thinking. It generated experimental concepts for sustainable, advanced, user-oriented architectures for future lunar bases. The Workshop participants chose diverse moon mission scenarios including ice mining, solar cell production, lunar telescopes, He3 mining, research and commercial operations. This paper will present the most important explorations and concepts from this Workshop. It will discuss the rationale behind adopting a multidisciplinary and multicultural design studio approach.

The bending fatigue performance of four heats of carburized, commercially-produced SAE 4320 steel was evaluated. Simulated gear tooth in bending (SGTB) cantilever beam specimens from each heat were identically carburized and fatigue tested in the direct quenched condition after carburizing. The microstructure and fracture surfaces of all specimens were characterized with light and electron microscopy. The four direct quenched sets of specimens performed similarly in low cycle fatigue. Endurance limits among the direct quenched specimens ranged between 1100 and 1170 MPa (160 and 170 ksi) and intergranular cracking dominated fatigue crack initiation. An additional set of specimens from one of the heats was reheated after carburizing. The fatigue performance of the reheated specimens was superior to that of the direct quenched specimens in both the low and high cycle regions. The effects of inclusion content, microstructure, and residual stresses on fatigue performance are discussed.

The effects of austenite grain size on the bending fatigue crack initiation and fatigue performance of gas carburized, modified 4320 steels were studied. The steels were identical in composition except for phosphorus concentration which ranged between 0.005 and 0.031 wt%. Following the carburizing cycle, specimens were subjected to single and triple reheat treatments of 820°C for 30 minutes to refine the austenite grain structure, and oil quenched and tempered at 150°C. Specimens subjected to bending fatigue were characterized by light metallography to determine microstructure and grain size, X-ray analysis for retained austenite and residual stress measurements, and scanning electron microscopy for examination of fatigue crack initiation and propagation. The surface austenite grain size ranged from 15 μm in the as-carburized condition to 6 and 4 μm diameter grain size for the single and triple reheat conditions, respectively.

The bending fatigue performance of gears, cantilever beam specimens, and notched-axial specimens were evaluated and compared. Specimens were machined from a modified SAE-4118 steel, gas-carburized, direct-quenched and tempered. Bending fatigue specimens were characterized by light metallography to determine microstructure and prior austenite grain size, x-ray analysis for residual stress and retained austenite measurements, and scanning electron microscopy to evaluate fatigue crack initiation, propagation and overload. The case and core microstructures, prior austenite grain sizes and case hardness profiles from the various types of specimens were similar. Endurance limits were determined to be about 950 MPa for both the cantilever beam and notched-axial fatigue specimens, and 1310 MPa for the single gear tooth specimens.

The effects of subzero treatments on the bending fatigue performance of carburized gear steels were investigated by cantilever bending fatigue testing. Specimens were machined from SAE-4320 and SAE-9310 bar stock steel, gas-carburized, quenched, tempered at 175°C, subzero cooled to -73°C and -196°C, and tempered at 175°C. Bending fatigue specimens were characterized by light metallography to determine microstructure and prior austenite grain size, x-ray diffraction for residual stress and retained austenite contents, microhardness testing, and scanning electron microscopy to evaluate fatigue crack initiation, propagation and overload. Refrigeration treatments caused additional transformation of retained austenite and increased surface hardness and compressive residual stresses. Bending fatigue endurance limits for the SAE-4320 specimens were determined to be 1310 MPa for the as-carburized condition, 1170 MPa for the -73°C condition, and 1280 MPa for the -196°C condition.

This study evaluated the bending fatigue performance of a modified SAE 4320 steel as a function of carburizing technique. S-N curves and endurance limits were established by fatigue testing modified Brugger-type specimens that are designed to simulate a single gear tooth. Fractured specimens were examined by light and electron microscopy to determine crack initiation sites, establish the extent of stable crack propagation, and analyze surface oxide types and distributions. Test results show that plasma-carburizing boosted the endurance limit of an oxidation-susceptible gear steel from 1100 MPa to 1375 MPa. Fatigue endurance limits in excess of 1400 MPa had previously been achieved in gas-carburized SAE 4320 steels by reheat treatments and reductions in high-oxidation potential elements. The level of improvement observed in this study suggests that any of these advanced processing techniques can allow significant size reductions and weight savings in automotive transmission gears.

The strain-induced diffusionless shear transformation of retained austenite to martensite during straining of transformation induced plasticity (TRIP) assisted steels increases strain hardening and delays necking and fracture leading to exceptional ductility and strength, which are attractive for automotive applications. A novel technique that provides the retained austenite volume fraction variation with strain with improved precision is presented. Digital images of the gauge section of tensile specimens were first recorded up to selected plastic strains with a stereo digital image correlation (DIC) system. The austenite volume fraction was measured by synchrotron X-ray diffraction from small squares cut from the gage section. Strain fields in the squares were then computed by localizing the strain measurement to the corresponding region of a given square during DIC post-processing of the images recorded during tensile testing.