Search Results

We characterize the cyclic behavior of an AM30 extruded magnesium alloy. The micromechanisms of cyclic damage were studied by means of strain controlled experiments in both the extruded and transverse directions. A scanning electron microscope (SEM) analysis of the microstructure revealed that second phase particles were present in the Mg alloy that nucleated the cracks. However, crack initiation sites were observed to occur due to profuse twinning. Low cycle fatigue parameters were determined, and a microstructure-sensitive MultiStage Fatigue (MSF) model, which is able to capture mechanical and microstructure properties, was implemented to predict fatigue behavior and failure.

EcoCAR 2: Plugging In to the Future (EcoCAR) is North America's premier collegiate automotive engineering competition, challenging students with systems-level advanced powertrain design and integration. The three-year Advanced Vehicle Technology Competition (AVTC) series is organized by Argonne National Laboratory, headline sponsored by the U. S. Department of Energy (DOE) and General Motors (GM), and sponsored by more than 28 industry and government leaders. Fifteen university teams from across North America are challenged to reduce the environmental impact of a 2013 Chevrolet Malibu by redesigning the vehicle powertrain without compromising performance, safety, or consumer acceptability. During the three-year program, EcoCAR teams follow a real-world Vehicle Development Process (VDP) modeled after GM's own VDP. The VDP serves as a roadmap for the engineering process of designing, building and refining advanced technology vehicles.

A common interaction between a penetrator and a target has been the use of copper and nickel materials. However, a multiscale analysis has not been performed on such a system. Compared to steels, aluminum alloys, titanium alloys and other metallic materials, a description of the mechanical behavior of pure ductile metals such as Cu struck by a penetrator comprises nickel under the high strain rate at different multiscale still remains unknown. In this research, Modified Embedded Atom Method (MEAM) Potential is utilized to study this system and the molecular dynamics simulation is employed in order to provide structure property evolution information for plasticity and shearing mechanisms.

The vibration response from undamaged and damaged polymer matrix composite beams at elevated temperatures is analyzed using the Hilbert-Huang Transform (HHT) technique. The HHT shows potential in identifying the nonlinear damaged response of the beams. Using empirical mode decomposition to separate superposed modes of signals, several intrinsic mode functions can be determined which can reveal more information about complex nonlinear signals than traditional data analysis techniques such as the Fourier Transform. The composite beams are fabricated from an out-of-autoclave uniaxial carbon/epoxy prepreg (CYCOM™-5320-1/T650). Delamination damage in the composite layups is introduced by insertion of mold release wax films during fabrication. A shaker-table fixture was used for the vibration testing of all beams in a vertical cantilever configuration. High temperature piezoelectric accelerometers were used to obtain the vibration data for a frequency range of 1-61 Hz.

The moisture/water absorption and microvoids/cracks progression are two well-understood mechanisms that have significant degradation effects on the mechanical properties/behaviors of the polymer-based composites. To theoretically investigate the effects of above two mechanisms, we develop a simple fiber reinforced polymer composites model by employing the internal state variable (ISV) theory. The water content and the anisotropically distributed damage of the composites are considered as two ISVs (the water content is described by a scalar variable and the damage is defined as a second order tensor) whose histories are governed by two specific physically-based evolution equations. The proposed model can be easily cast into a general theoretical framework to capture more polymer composites behaviors such as viscoelasticity, viscoplasticity and the thermal effect.

Polymer matrix composites are increasingly adopted in aerospace and automotive industries due to their many attributes, such as their high strength to weight ratio, tailorability, and high fatigue and durability performance. However, these materials also have complex damage and failure mechanisms, such as delaminations, which can severely degrade their strength and fatigue performance. To effectively and safely use composite materials in primary structures, it is essential to assess composite damage response for development of accurate predictive models. Therefore, this study focuses on determining the response of damaged and undamaged carbon epoxy beams subjected to vibration loadings at elevated temperatures. The Hilbert-Huang Transform (HHT) technique is used to analyze the beams’ modal response. The HHT shows potential in identifying the nonlinear damaged response of the beams.