This paper proposes a rolling machine that forms fine corrugated section patterns for thin sheets. A prototype of the machine was made and the performance of the machine was tested. As compared with press forming, rolling has the advantages of the high forming limit, the low forming reaction force, the easy control of the thin sheet's curve and high productivity. We confirmed these four advantages by using finite element analyses and the prototype rolling machine. Stainless steel sheets and titanium sheets, which were one of the materials with a low forming limit, were used. Firstly, the rolling showed a 1.3-times higher forming limit than the press forming in the case that a fine corrugated section pattern was formed in a stainless steel sheet of 22-mm square sizes. Secondly, the forming reaction force of the rolling was about one-twentieth of the press forming without coining, and the experimental results agreed with the finite element simulation.

Vibration damping steel sheets (VDSS), which have sandwich structures with intermediate layers of resin, have been studied. The most important characteristics of VDSS for inner panels of automotive vehicles are the vibration damping properties, press formability and spot weldability. Vibration damping properties, which are quantified by loss factor,η, were influenced by both tanδ, which indicates damping capacity of resins, and elastic modulus of core resin. From a view point of vibration damping properties, resins with larger tanδ and relatively lower elastic modulus were favorable. Because these mechanical characteristics vary considerably with temperature, it is important to select the most suitable resin for the service temperature range. The relationship between noise reduction effect and loss factor of VDSS were also studied. It was experimentally confirmed that noise reduction effect of VDSS is proportional to the logarithm of their loss factor.

The application of tailored blanks to autobody parts has progressed because of its numerous advantages. The forming of tailored blanks has, however, a lot of technical problems. Among the problems, weld-line movement and formability deterioration are the most significant ones in case of deep drawing. The weld-line movement and formability change were examined experimentally as a function of weld-line location in square cup deep drawing. The weld-line movement of tailored blank consists of two sources. One is the geometrical reason, and the other is due to the hardening of weld bead. The formability of tailored blank is inferior to that of an original blank by the existence of hardened weld region. The mode of fracture changes from wall breakage to a fracture adjacent to punch radius when the weld-line was close to the punch corner.

This paper describes the lap welding of Zinc-coated steel sheet using a high power continuous wave YAG laser. The well-known problem of welding the Zinc-coated sheet is related to the low boiling point of zinc compared with the melting point of steel. During lap welding, zinc coating at the interface vaporize rapidly and causes defects1)2). In this study, therefore, lap welding was performed by YAG laser. The effects of type of coating layer, welding conditions, tensile strength and corrosion resistance after electro-deposition was examined. It was found that the weldability of coated steel is different by type of coating. Zn-Ni coated steel showed good weldability, but galvanealed steel inevitably pore pits with no gap set up. These defects not only lower the strength of joint, but also produce irregular bead where easily corroded after electro-deposition.

A method of fatigue life prediction of spot welded joint under multi-axial loads has been developed by fatigue life estimation working groups in the committee on fatigue strength and structural reliability of JSAE. This method is based on the concept of nominal structural stress ( σ ns) proposed by Radaj and Rupp, and improved so that D value is not involved in stress calculation. The result of fatigue life estimation of actual vehicle with nominal structural stress which was calculated through newly developed method had very good correlation with the result of multi-axial loads fatigue test carried out with test piece including high strength steel.

Galvannealed steel sheet (GA) is very extensively used for vehicle panels. However ζ-phase (FeZn13) in GA coat causes poor stamping formability. Previously, there were no easy methods to evaluate the influence of ζ-phase on the frictional characteristics other than the X-ray diffraction method. This study will discuss the development of a new testing method: Dr. STAMP Method that is both efficient and convenient with pin-on-disc tester.

Tensile testing technique for the small sample was newly developed. Small tensile specimens with gage length of 1mm were taken from spot welds of high tensile strength steel sheets, and stress-strain relationships and ductility of base metal, heat affected zone including corona bond and nugget were individually measured. Finite element analyses of spot-welded joints under the conditions of static and dynamic tensile-shear loading were carried out with these local mechanical properties to predict the fracture mode and strength of the joints. It was clarified that the effects of both nugget diameter and class of steels were evaluated with good accuracy.

In this paper the fatigue life of welded steel sheet structures is predicted by using FE-Fatigue, which is one of fatigue analysis software tools on the market, and these predicted results are evaluated by reference to corresponding experimental results. Also, we try to predict these structures by using two fatigue life prediction theories established by the JSAE fatigue and reliability committee to compare prediction results. It was confirmed that spot welds fatigue life predictions agree qualitatively with corresponding experimental results and arc welds fatigue life predictions are in good agreement with corresponding experimental results in cases where the SN curve database is modified appropriately.

The main operations for the manufacturing of auto parts are the cutting of the flange and the stamping. In order to perform accurate fatigue calculation it is necessary to have the material properties for each point of the structure. Usually, only the fatigue curve obtained on the flat sheet with polished edges is used because it represents the basic metal behaviour. The real edge quality decreases the fatigue limit while the hardening induced by the stamping increases it. To take these effects into account allows a better fatigue calculation of the structural part.

The newly developed sheet steel lightly coated with an organic composite is as follows. Zn-Ni alloy plated sheet steel with a coating weight of 30 g/m2 and average Ni concentration of 11.5 ∼12.0 % is chromated through electrolysis. The coating weight of chromate film is 50 ∼90 mg/m2 in Cr. Furthermore, emulsified olefin-acrylic acid copolymer resin mixed with colloidal silica of particle size 7 ∼8 nm applied to a thickness of 1.0 ∼1.8 μm. Olefin-acrylic acid copolymer resin and colloidal silica are mixed at the rate of 100 and 30 (parts by weight). It maintains excellent corrosion resistance even after forming, C-ED paint corrosion resistance and paint adhesion. Furthermore, it has excellent perforation resistance. The product has excellent weldability and is well suited to continuous forming, too.

As a demand for vehicles of higher functionality grows, automakers and material suppliers are devoting increasing efforts to develop technologies for greater safety, lighter weight, higher corrosion resistance, and enhanced quietness. The resin-sandwiched vibration damping steel sheet (VDSS), developed as a highly functional material for reducing vehicle vibration and noise, has been used for oil pans1) and compartment partitions2). First applied for a structural dash panel of the new Mazda 929, a Zn-Ni electroplated VDSS which allows direct electric welding has contributed to greater weight reduction as well as improved quietness.

This paper describes the deformation analysis of hemispherical punch stretching and square shell drawing, using 3-D finite element program “ROBUST”. The effects of material properties and process factors on cup height to punch force relation, and strain distributions on formed parts were investigated. The calculated values give considerably good agreement with experimental measurements from LDH, FLD and square shell tests. The results can be expected to contribute to predictive evaluation of forming limits using computer simulation.

Recently, many kinds of coated steel sheets are developed and used for automobile panels. Some of them show higher coefficient of friction and poorer formability than a cold rolled steel sheet. New polymer lubricating films are developed and proved to improve frictional characteristics of coated steel sheets in this study. The developed polymer lubricating films are applied to Electro Galvanized steel sheet and Hot Dip Galvannealed steel sheet, and coefficient of friction and formability of them are measured by using model dies. Different coefficients of friction are obtained by a change in a combination of components in a polymer lubricating film. As a result, the most suitable coefficient of friction is able to chose in forming conditions by the developed polymer lubricating films.

Extremely formable cold sheet steel with an ultra-high Lankford value of more than 2.5 and an n value of more than 0.27 has been developed. This steel is obtained due to the following factors; using extremely pure IF (Interstitial free) steel, immediate rapid cooling upon completion of rolling in the hot rolling process, a high reduction in the cold rolling process, and a high soaking temperature in the continuous annealing process. This steel sheet shows excellent deep drawability and stretch formability compared with conventional steel sheet (former IF steel and low carbon aluminum-killed steel) as a result of evaluating the limiting drawing ratio and limiting dome height, respectively. This excellent formability is also shown by the model forming tests for simulating the actual stamping of an oilpan and a side-panel. Furthermore, this steel shows the same spot-weldability as that of former IF steel, and zinc phosphatability similar to that of low carbon aluminum-killed steel.

Aluminum alloy sheets are used for automotive body-panels, but their small Young's modulus results in inferior shape-fixability than conventionally-applied steel sheets with similar strengths. Smaller radius of curvature, indicating better shape-fixability, is found at the center of a panel press-formed with higher blank holder force (BHF). Higher force can be applied for press-forming of alloy sheets with larger strain-hardening exponent (n value) induced by an increased addition of Mg. Recently-developed 5000 series alloy sheets containing 5.5 pct Mg and 0.3 pct Cu have an elongation over 33 pct at an ultimate tensile strength of 270 MPa and can be press-formed with better shape-fixability.

Improvement of material characteristic values, adjustment of forming conditions as well as introduction of new forming technics are necessary to promote wide application of aluminum alloy sheets into automotive parts. 5000 series and 6000 series aluminum alloy sheets are concerned about the relationship between material characteristic values and fundamental forming ability required to apply them to automobile body parts as well as the effect of lubricant on their formability. The hardening parameters, n values, of them are larger than those of cold-rolled steel sheets. However, the r values and the local elongations are extremely small. The improvement of stretch formability owing to increase of n value is smaller than that of the steel sheets. Inferior deep drawability of the aluminum alloy sheets is due to low fracture resistance force caused by low r value.

Gas shielded metal arc welding is generally applied to automobile chassis parts. However, the weld parts with the E-coat show poor corrosion resistance. Therefore, the corrosion mechanism of the weld parts was investigated. The results found two reasons why the weld parts corroded faster than the non weld parts:(1)inadequate phosphating (2)defects in the E-coat. After detailed investigation, it was clarified that the major cause of poor corrosion resistance was the defects in the E-coat caused by slags formed on the surface of the weld bead. Therefore the amount of slag has to be decreased to improve the corrosion resistance. The effect of shielding gas composition on the amount of slag was then investigated. In the case of Ar and oxidizing gas mixture, the corrosion resistance improved as the oxidizing gas content decreased. This was due to the reduction of slags.

In continuous annealing, accelerated cooling methods have recently found practical application in addition to conventional gas jet cooling or water jet quenching method. Moderate cooling rate of gas jet cooling or accelerated cooling makes it possible to utilize new high-strength steels with excellent properties. The faster cooling rate deteriorates ductility of steels. These newly developed steels are improved rephosphorized steels with high r̄-value and high bake hardenability, dual phase steels with superior ductility, Ti-stabilized high-strength steels with very high r̄-value, grain boundary hardening steels employing low temperature annealing, and unique ultra high-strength steels. This paper describes properties and process factors of these steels, and their applications to automotive.

In order to attain the gauge reduction of outer body panels without spoiling the dent-resistance and formability, a bake-hardenable Al-killed steel sheet, named RBH-35, and has been developed in the conventional box-annealing process. RBH-35 is an 0.01% carbon, low manganese and rephosphorized Al-killed steel sheet retaining solute carbon of about 10 ppm. The steel exhibits high r-value, bake-hardenability of 40 MPa, ultimate tensile strength of above 350 MPa and substantially non-aging property. Results of stamping test of door outer panel showed that RBH-35 is the most suitable steel sheet for the thinning of outer body panels by about 10%. This paper reports the metallurgical features, mechanical properties and applications of the steel.

Carburizing heat treatment is one of the automobile component manufacturing steps, which consumes a large amount of energy. Raising the carburizing temperature can shorten the carburizing time and save the energy, but involves the risks of grain coarsening and attendant property deterioration. The authors have clarified the precipitation behavior of aluminum nitride (A1N) in the automobile gear manufacturing process and the optimum precipitation of A1N in as-rolled steel bars to prevent the grain coarsening. Through the application of the controlled rolling technique to ensure the optimum precipitation of A1N in continuously cast steel of uniform chemical composition, the authors have substantially saved energy while maintaining high quality, and developed a high-temperature carburizing steel expected to minimize and stabilize quenching strains.