Search Results

This SAE Information Report provides: a Types of valve guides and their nomenclature b Valve guide alloy designations and their chemistries c Valve guide alloy metallurgy d Typical mechanical and physical properties of guide alloys e Typical dimensional tolerances of valve guides and their counterbores f Recommended interference fits g Installation procedures h Application considerations

This SAE Recommended Practice defines the set-up and procedure for conducting the SAE Single Tooth Bending Fatigue Test. The details of the test fixture to be used (referred henceforth as “the test fixture” in this document) and gear test sample and the procedures for testing and analyzing the data are presented in this document.

This SAE Recommended Practice defines the set-up and procedure for conducting the SAE Single Tooth Bending Fatigue Test. The details of the test fixture to be used (referred henceforth as “the test fixture” in this document) and gear test sample and the procedures for testing and analyzing the data are presented in this document.

Compositions apply to the finished bearing or bearing lining, not necessarily to the alloy at an intermediate processing stage. All values not given as ranges are maxima. (See Tables 1 through 5.)

This recommended practice defines, illustrates, and specifies allowable limits for the various types of surface discontinuities that may occur during the manufacture and processing of metric-series nuts, in sizes 6.3 to 25 mm and inch-series nuts in sizes ¼ to 1 in., inclusive, which are primarily intended for use in automotive assemblies.

Powder metal (P/M) parts are manufactured by pressing metal powders to the required shape in a precision die and sintering to produce metallurgical bonds between the particles, thus generating the appropriate mechanical properties. The shape and mechanical properties of the part may be subsequently modified by repressing or by conventional methods such. as machining and/or heat treating. While powder metallurgy embraces a number of fields wherein metal powders may be used as raw materials, this standard is concerned primarily with information relating to mechanical components and bearings produced from iron-base materials.

Powder metal (P/M) parts are manufactured by pressing metal powders to the required shape in a precision die and sintering to produce metallurgical bonds between the particles, thus generating the appropriate mechanical properties. The shape and mechanical properties of the part may be subsequently modified by repressing or by conventional methods such. as machining and/or heat treating. While powder metallurgy embraces a number of fields wherein metal powders may be used as raw materials, this standard is concerned primarily with information relating to mechanical components and bearings produced from iron-base materials.

Powder metal (P/M) parts are manufactured by pressing metal powders to the required shape in a precision die and sintering to produce metallurgical bonds between the particles, thus generating the appropriate mechanical properties. The shape and mechanical properties of the part may be subsequently modified by repressing or by conventional methods such. as machining and/or heat treating. While powder metallurgy embraces a number of fields wherein metal powders may be used as raw materials, this standard is concerned primarily with information relating to mechanical components and bearings produced from iron-base materials.

This recommended microscopic practice for evaluating the inclusion content in steel has been developed as a practical method of quantitatively determining the degree of cleanliness of steel. This method has been established as a reasonable control for steel mill operations and acceptance for production manufacturing. It has been widely accepted for carbon and alloy steel bars, billets, and slabs. Exceptions are resulfurized grades which are outside the limits of these photomicrographs and the high carbon bearing quality steels which are generally classified using ASTM E 45-60T, Method A, Jernkontoret Charts.