Through a polymer design and precise morphology control, The Super Olefin Polymer, TSOP-1 and TSOP-5 were developed for the material consolidation of interior and exterior parts, respectively. Due to a good balance of TSOP performance, several conventional materials were consolidated into one material for each application. Accordingly, considerable amounts of weight reduction and cost savings have been obtained. In addition to the excellent recyclability of TSOP, the coated bumpers collected from the market were re-utilized through paint decomposition technology. The first dashboard construction, molded partially with foam-padded skin, was also realized. The current amount of TSOP used in a vehicle is about 30% of the total amount of plastic materials. Through the usage of TSOP, 70% of the material consolidation has been achieved.

ϵ-caprolactam was polymerized in the interlayer space of montmorillonite, the clay mineral yielding a nylon-clay hybrid (NCH). X-ray and TEM measurements revealed that each template of the silicate, which was 1 nm thick, was dispersed in the nylon 6 matrix, and that the interlayer distance of clay increased continuously from 1.2 nm for the unintercalated material to 21.4 nm for the intercalated material. Thus, NCH is a polymer-based molecular composite or a nano-composite. NCH contains 1-15 vol% of monolayer clay. Injection-molded NCH showed excellent mechanical properties compared with nylon 6 in terms of tensile strength, tensile modulus and heat resistance. The tensile modulus of NCH was twice that of Nylon 6, and the heat distortion temperature increased from 65°C for nylon 6 to 145°C for the NCH containing only 1.6 vol% of a clay mineral. It was found that such excellent properties of an NCH system was due to the strong ionic interaction between nylon 6 and the silicate layer.

The EMT (Elastomer Modified Thermoplastics) currently used in passenger car bumper fascia are limited in retaining low CLTE (Coefficient of Linear Thermal Expansion) and impact resistance, although they are highly rigid, which allows a reduction in weight, and also have high flowability during injection molding. We have developed a new bumper material called “Super Olefin Polymer” using a unique theory based upon a reversal of the current concept. The current polymer design concept of the EMT material is to compound and disperse the EPR (Ethylene Propylene Rubber) into the resin matrix such as polypropylene. We reversed the domain and the matrix, and treated the resin phase as the filler and the elastomer phase as the matrix.

A new automotive interior component material, TSOP-5 has been developed by refining the technology utilized to develop TSOP-1, the high modulus and high flow material for bumper covers. This new interior component material has excellent molding capability (MI=30dg/min.) yet still maintains high impact resistance which enables the material to be used in areas such as the dash board as well as trim covers requiring to meet the FMVSS 214, the new side impact regulation or the FMVSS 201, the new soft upper trim regulation.